High-resilience wear-resistant EVA composite foam material, preparation method and composition for preparing material

A technology of composite foaming and composition, applied in the field of rubber-plastic composite materials, can solve the problems of poor cushioning and rebound properties of materials, affecting the wearing experience of shoes, and loss of elasticity of the soles, etc., to achieve good resilience and excellent physical properties. Effect of Mechanical Properties, Guaranteed Mechanical Properties and Resilience

Pending Publication Date: 2020-01-17
ANTA CHINA
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in order to meet certain wear-resistant requirements, the current EVA foam materials for shoe soles generally have higher hardness and higher density, and the materials have poor cushioning and rebound performance.
The wear-resis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-resilience wear-resistant EVA composite foam material, preparation method and composition for preparing material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The technical solutions in the embodiments of the present invention are clearly and completely described below. Obviously, the described embodiments are preferred embodiments of the invention and should not be seen as excluding other embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0023] In embodiment one, in the composition that is used to prepare high elastic wear-resistant EVA composite foaming material, each component is as follows by mass parts:

[0024] Ethylene-vinyl acetate copolymer: 30 parts by mass

[0025] Polyolefin thermoplastic elastomer: 12 parts by mass

[0026] Polyolefin block copolymer: 10 parts by mass

[0027] Thermoplastic polyurethane: 4 parts by mass

[0028] Thermoplastic polyester elastomer: 8 parts by mass

[0029] Anti-wear agent: 5 parts by mass

[0030] Zinc oxide...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-resilience wear-resistant EVA composite foam material, a preparation method and a composition for preparing the material. The composition comprises the ingredients in parts by mass: 30-50 parts of ethylene-vinyl acetate copolymer, 10-20 parts of polyolefin thermoplastic elastomer, 10-20 parts of polyolefin block copolymer, 4-10 parts of thermoplastic polyurethane, 5-10 parts of thermoplastic polyester elastomer, 5-10 parts of anti-wear agent, 0.5-1 part of zinc oxide, 0.5-1.5 parts of zinc stearate, 0.5-1.2 parts of cross-linker, 0.1-0.3 part of crosslinking assistant and 1.5-3.5 parts of foamer. The preparation method comprises the steps of feed weighing, reblending, granulating and foaming. The obtained high-resilience wear-resistant EVA composite foam material is high in resilience and excellent in wear resistance and is applied to production of shoe soles of sports shoes.

Description

technical field [0001] The invention relates to the field of rubber-plastic composite materials, in particular to a high-elastic and wear-resistant EVA composite foam material, a preparation method and a composition for preparing the material. Background technique [0002] As the main component of sports shoes, the sole affects the wearer's experience. The demand for lightweight and high-elastic sports shoes has attracted more and more attention from consumers. At the same time, reducing the links in the manufacturing process and reducing production costs are also the direction of efforts of sports shoe manufacturers. The use of high-elastic and wear-resistant EVA foam material to replace part of the rubber directly as the outsole of sports shoes can effectively solve the above problems. However, in order to meet certain wear-resisting requirements, the current EVA foam materials for shoe soles generally have higher hardness, higher density, and poor performances such as ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08L75/04C08L53/00C08L67/00C08K13/02C08K3/22C08K5/098C08J9/10
CPCC08J9/103C08J9/0061C08J9/0095C08J9/0066C08J9/0023C08J2203/04C08J2323/08C08J2423/08C08J2475/04C08J2453/00C08J2467/00
Inventor 丁世家刘超陈绍猛王有承
Owner ANTA CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products