Extreme pressure anti-wear agent composition for gear oil and application of extreme pressure anti-wear agent composition
A technology of extreme pressure antiwear agent and composition, which is applied in the direction of lubricating composition, additives, petroleum industry, etc., can solve problems that need to be further improved, and achieve the effect of excellent extreme pressure and antiwear properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0052] The specific components of gear oil extreme pressure antiwear agent composition are shown in Table 1, and its preparation method is as follows:
[0053] 1) Add base oil in proportion, heat up to 50-60°C for heating and stirring, keep it for 2-3 hours, then lower the temperature to 40-50°C;
[0054] 2) Then add the components of extreme pressure agent and anti-wear agent in order of the amount added, from small to large, and stir for 2 to 3 hours until the mixture is completely dissolved and becomes transparent.
[0055] Table 1 Components of gear oil extreme pressure antiwear agent composition
[0056] Raw material components, wt% Component content Group I 150BS base oil margin Group II 150N base oil Appropriate amount Group II hydrogenated No. 6 base oil Sulfurized isobutylene 45 Phosphorothioate complex ester amine salt A 30 Phosphorothioate complex ester amine salt B tricresyl phosphate Thioaminoester ...
Embodiment 2
[0059] The specific components of the extreme pressure and antiwear agent composition for gear oil are shown in Table 2, and its preparation method is the same as in Example 1.
[0060] Table 2 Components of gear oil extreme pressure antiwear agent composition
[0061] Raw material components, wt% Component content Group I 150BS base oil margin Group II 150N base oil Group II hydrogenated No. 6 base oil Appropriate amount Sulfurized isobutylene 30 Phosphorothioate complex ester amine salt A Phosphorothioate complex ester amine salt B 20 tricresyl phosphate 12 Thioaminoester 10 n-butyl phosphite 8
[0062] Among them, the weight percent ratio of Type I 150BS to Type II hydrogenated No. 6 base oil is 1:3.
Embodiment 3
[0064] The extreme pressure and antiwear properties of the gear oil extreme pressure and antiwear composition are detected by the experimental method specified in the national standard as shown in Table 3. The results are shown in Table 3. From the analysis of the test results, it can be seen that the above two examples The extreme pressure and antiwear agent composition of the present invention can reach a certain enterprise standard, and the extreme pressure and antiwear agent for gear oil provided by the invention has excellent extreme pressure and antiwear properties, and can be used in industrial and vehicle gear lubricating oil additives.
[0065] Table 3 Performance testing of gear oil extreme pressure antiwear agent composition
[0066]
PUM
| Property | Measurement | Unit |
|---|---|---|
| viscosity index | aaaaa | aaaaa |