Preparation method of antibacterial sol for shoemaking and antibacterial finishing method

An antibacterial finishing and sol technology, which is applied in fiber treatment, biochemical fiber treatment, textiles and papermaking, etc., can solve the problems of discoloration of matrix materials, affecting the appearance of shoe materials, and the ineffective effect of fungi on foot diseases, etc., to achieve good antibacterial effect of effect

Inactive Publication Date: 2020-02-21
江西省东鹏鞋业有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, most of the existing antibacterial shoe materials have good antibacterial effects on typical bacteria such as Escherichia coli and Staphylococcus aureus, but have no obvious effect on fungi that actually cause foot diseases
Silver-based antibacterial agents can easily cause discoloration of the base material under light conditions, affecting the appearance of the shoe material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A preparation method of antibacterial sol for shoemaking and an antibacterial finishing method, comprising the following steps:

[0016] (1) According to n(TEOS): n(H 2 O): n(EtOH): n(GPTMS)=(4~8):(150~200):(40~80):(1~5) for proportioning, wherein EtOH is added in two steps, the first step Add 2 / 3 of total EtOH content, use 65% HNO 3 Adjust the pH to 2, stir electrically at 30°C to make a mixed solution; secondly, take 0.1mol of TEOS, add 0.1g of TH, dissolve it evenly with the remaining 1 / 3 of EtOH, add it to the mixed solution prepared in the previous step, 30 ℃ water bath constant temperature electric stirring for 5 hours, placed in the condition of 15 ℃ for a period of time, to obtain a transparent antibacterial sol;

[0017] (2) Antibacterial finishing of shoe lining by padding finishing process, soaking the fabric in transparent antibacterial sol for a certain period of time, wherein the pre-baking temperature is 110°C, the pre-baking time is 3min, and the bakin...

Embodiment 2

[0019] A preparation method of antibacterial sol for shoemaking and an antibacterial finishing method, comprising the following steps:

[0020] (1) According to n(TEOS): n(H 2 O): n(EtOH): n(GPTMS)=(4~8):(150~200):(40~80):(1~5) for proportioning, wherein EtOH is added in two steps, the first step Add 2 / 3 of total EtOH content, use 65% HNO 3 Adjust the pH to 2, stir electrically at 30°C to make a mixed solution; secondly, take 0.1mol of TEOS, add 0.1g of TH, dissolve it evenly with the remaining 1 / 3 of EtOH, add it to the mixed solution prepared in the previous step, 30 ℃ water bath constant temperature electric stirring for 5 hours, placed in the condition of 15 ℃ for a period of time, to obtain a transparent antibacterial sol;

[0021] (2) Antibacterial finishing of shoe lining by padding finishing process, soaking the fabric in transparent antibacterial sol for a certain period of time, wherein the pre-baking temperature is 120°C, the pre-baking time is 3min, and the bakin...

Embodiment 3

[0023] A preparation method of antibacterial sol for shoemaking and an antibacterial finishing method, comprising the following steps:

[0024] (1) According to n(TEOS): n(H 2 O): n(EtOH): n(GPTMS)=(4~8):(150~200):(40~80):(1~5) for proportioning, wherein EtOH is added in two steps, the first step Add 2 / 3 of total EtOH content, use 65% HNO 3 Adjust the pH to 2, stir electrically at 30°C to make a mixed solution; secondly, take 0.1mol of TEOS, add 0.1g of TH, dissolve it evenly with the remaining 1 / 3 of EtOH, add it to the mixed solution prepared in the previous step, 30 ℃ water bath constant temperature electric stirring for 5 hours, placed in the condition of 15 ℃ for a period of time, to obtain a transparent antibacterial sol;

[0025] (2) The padding finishing process is used to carry out antibacterial finishing on the lining of shoes, and after soaking the fabric in the transparent antibacterial sol for a certain period of time, the pre-baking temperature is 130°C, the pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of antibacterial sol for shoemaking and an antibacterial finishing method. The preparation method and the antibacterial finishing method include: using TEOSas the precursor, EtOH as the solvent and HNO3 as the catalyst, adding a certain amount of GPTMS and TH, electrically stirring for 5 hours at hydrolysis temperature of 30 DEG C, and standing at roomtemperature for a certain period of time to obtain the transparent antibacterial sol; using a padding finishing process to perform antibacterial finishing on lining fabric for shoes, soaking the fabric into the transparent antibacterial sol for a certain period of time, using a rolling manner to press the transparent antibacterial sol into the gaps of the fabric, and removing the redundant transparent antibacterial sol at the same time. Compared with the prior art, the antibacterial finishing method has the advantages that the two-dipping two-rolling process with the pick up being 70-80% is used under the conditions that dipping time is 10 seconds, pre-drying temperature is 130 DEG C, pre-drying time is 2.5 minutes, drying temperature is 190 DEG C and drying time is 40 seconds, the processed shoe material is good in antibacterial effect on Candida albicans and Trichophyton rubrum, and the antibacterial rate is larger than 90%.

Description

technical field [0001] The invention relates to the field of shoe-making antibacterial technology, in particular to a method for preparing an antibacterial sol for shoemaking and an antibacterial finishing method. Background technique [0002] Shoes are the necessities of people's daily life. With the development of society and the improvement of people's living standards, people have higher and higher requirements for the comfort and hygiene of shoes and boots. In recent years, the antibacterial agent and antibacterial fabric industry has gradually matured. Some international and domestic scholars have tried to apply it to footwear products, and a number of antibacterial agents and antibacterial shoe materials for shoes have emerged on the market. [0003] Although footwear antibacterial materials have emerged in the market, there are still many deficiencies in the application of antibacterial agents in footwear. For example, most of the existing antibacterial shoe materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/79D06M13/513D06M23/00
CPCD06M11/79D06M13/513D06M16/00D06M23/00
Inventor 彭颜华
Owner 江西省东鹏鞋业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap