Polymer integrally-formed shoe outsole and preparation method thereof

A technology of shoe outsole and polymer, applied in shoe sole, footwear, application and other directions, can solve the problems of poor overall performance and single material, and achieve the effect of reducing production cost, excellent performance and good resilience

Inactive Publication Date: 2020-02-28
广东康诚新材料科技股份有限公司
View PDF14 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The general shoe sole includes a shoe outsole and a PU foam sole located on the shoe outsole, and the shoe outsole includes a shoe cover in contact with the ground and a shoe midsole

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A polymer integrally formed shoe outsole, the shoe outsole includes a shoe cover in contact with the ground and a shoe midsole integrally formed with the shoe cover, the shoe cover is made of TPU material, and the shoe midsole is made of PU foam Material and TPU popcorn material, or composed of PU foam material and elastic rubber material, the two materials of the midsole of the shoe are mixed and poured into the shoe cover, and the shoe outsole is formed integrally.

[0030] The density of the TPU material is 1.17g / cm 3 , Shore hardness is 76A.

[0031] The density of the PU foam material is 0.27g / cm 3 , the rebound rate is 45%.

[0032] The density of the elastic rubber material is 0.43g / cm 3 , the rebound rate is 50%.

[0033] The density of the TPU popcorn material is 0.12g / cm 3 , the rebound rate is 55%.

[0034] The weight ratio of the PU foam material to the TPU popcorn material or elastic glue material is 55:45.

[0035] A method for preparing the outsole...

Embodiment 2

[0044] The difference between this embodiment and the above-mentioned embodiment 1 is:

[0045] The density of the TPU material is 1.18g / cm 3 , Shore hardness is 77A.

[0046] The density of the PU foam material is 0.28g / cm3 , the rebound rate is 48%.

[0047] The density of the elastic rubber material is 0.44g / cm 3 , the rebound rate is 52%.

[0048] The density of the TPU popcorn material is 0.14g / cm 3 , the rebound rate is 58%.

[0049] The weight ratio of the PU foam material to the TPU popcorn material or elastic glue material is 58:42.

[0050] A method for preparing the outsole of a polymer integrally formed shoe, comprising the steps of:

[0051] (1) Add the PU foam material to 0.8‰ catalyst first, stir evenly, then add it to the material tank of the PU machine, pour the TPU popcorn material or elastic glue material into the granule tank, and then add water to the water tank Inside;

[0052] (2) Then adjust the machine ratio, the weight ratio of water to PU foa...

Embodiment 3

[0059] The difference between this embodiment and the above-mentioned embodiment 1 is:

[0060] The density of the TPU material is 1.20g / cm 3 , Shore hardness is 79A.

[0061] The density of the PU foam material is 0.30g / cm 3 , the rebound rate is 50%.

[0062] The density of the elastic rubber material is 0.46g / cm 3 , the rebound rate is 55%.

[0063] The density of the TPU popcorn material is 0.15g / cm 3 , the rebound rate is 60%.

[0064] The weight ratio of the PU foam material to the TPU popcorn material or elastic glue material is 60:40.

[0065] A method for preparing the outsole of a polymer integrally formed shoe, comprising the steps of:

[0066] (1) Add the PU foaming material to 1‰ of the catalyst first, stir evenly, then add it to the material tank of the PU machine, pour the TPU popcorn material or elastic glue material into the granule tank, and then add water to the water tank Inside;

[0067] (2) Then adjust the machine ratio, the weight ratio of water...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of shoe soles, and particularly relates to a polymer integrally-formed shoe outsole and a preparation method thereof. The shoe outsole comprises a shoe cover in contact with the ground and a shoe midsole integrated with the shoe cover, wherein the shoe cover is a TPU material; the shoe midsole is composed of two kinds of materials of a PU foaming material and a TPU popcorn material, or two kinds of materials of the PU foaming material and an elastic rubber material; and the two materials in the shoe midsole are mixed and poured into the shoe cover,and the shoe outsole is integrally formed. The integrally-formed shoe outsole provided by the invention has the characteristics of light weight, high resilience, wear-resistant and non-slip characteristics and high wearing comfort, and is integrally formed by adopting a plurality of materials, excellent in performance and low in cost.

Description

technical field [0001] The invention relates to the technical field of shoe soles, in particular to a polymer integrally formed shoe outsole and a preparation method thereof. Background technique [0002] As the fourth-generation sole material after rubber, PVC, and SBS, TPU (thermoplastic polyurethane elastomer) has better elasticity, wear resistance, tear resistance, and bending properties, and is a variety of special shoes with extremely high requirements. It is one of the preferred materials for soles of football shoes, skate shoes, hiking shoes, etc. [0003] The existing TPU used in the production of shoe materials is the TPU foaming process. The so-called "TPU foaming process" is actually like popcorn. The TPU is made into granules, and these granules can be thought of as one by one. old corn. Then throw it into a machine, which is similar to a popcorn machine, and after high temperature and high pressure, the corn becomes popcorn, and then uses a steam molding proc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A43B13/04B29C44/04B29K75/00
CPCA43B13/04B29C44/04B29K2075/00
Inventor 冯建龙田心花
Owner 广东康诚新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap