Puncture-resistant high-wear-resistant woven curtain and preparation method thereof

A technology with high wear resistance and puncture resistance, applied in the field of curtains, can solve the problems of heavy weight, thick thickness, lack of flexibility and comfort, etc., and achieve the effect of good restoration of original shape, strong puncture resistance and good resilience

Pending Publication Date: 2021-02-05
海宁优韵家居有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current puncture-resistant fiber fabrics have general puncture resistance, and are heavy in weight, too thick, and the softness and comfort of the materi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Puncture-resistant high-wear-resistant woven curtain and preparation method thereof
  • Puncture-resistant high-wear-resistant woven curtain and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0040]Example 1:

[0041]S1. Preparation of outer protective layer 1: Open, mix and comb the TPU sheath-core monofilament yarns with high abrasion resistance in sequence, and add ultra-high-strength polyethylene fiber to the TPU sheath-core monofilament yarns. Laying and pre-needling processing, thermal bonding and strengthening processing at 180 ℃, the hot pressing speed is 0.5m / min;

[0042]S2. Preparation of puncture-resistant layer 3: Firstly, polyester fiber and PBO fiber are opened, mixed, combed, and knitted into threads in sequence, and then woven and connected into a puncture-resistant woven fabric through the "joint bonding method";

[0043]S3. Preparation of connecting layer 2 threads: spun into stainless steel spun yarn by spinning technology, and stainless steel spun yarn is wrapped with aluminum foil to make stainless steel twisted yarn;

[0044]S4. Preparation of polyurethane adhesive: use the following weight component ratios: 100 parts of toluene diisocyanate (TDI) modified res...

Example Embodiment

[0047]Example 2:

[0048]S1. Preparation of outer protective layer 1: Open, mix and comb the TPU sheath-core monofilament yarns with high abrasion resistance in sequence, and add ultra-high-strength polyethylene fiber to the TPU sheath-core monofilament yarns. Laying and pre-needling processing, thermal bonding and strengthening processing at 180 ℃, the hot pressing speed is 0.5m / min;

[0049]S2. Preparation of puncture-resistant layer 3: Firstly, polyester fiber and PBO fiber are opened, mixed, combed and woven into threads in sequence, and then woven and connected to form a puncture-resistant woven fabric through the "joint bonding method";

[0050]S3. Preparation of connecting layer 2 threads: spun into stainless steel spun yarn by spinning technology, and stainless steel spun yarn is covered with aluminum foil to make stainless steel twisted yarn;

[0051]S4. Preparation of polyurethane adhesive: use the following weight component ratio: 100 parts of toluene diisocyanate (abbreviated as TDI...

Example Embodiment

[0054]Example 3:

[0055]S1. Preparation of outer protective layer 1: Open, mix and comb the TPU sheath-core monofilament yarns with high abrasion resistance in sequence, and add ultra-high-strength polyethylene fiber to the TPU sheath-core monofilament yarns. Laying and pre-needling processing, heat bonding and strengthening processing at 170 ℃, the hot pressing speed is 0.5m / min;

[0056]S2. Preparation of puncture-resistant layer 3: Firstly, polyester fiber and PBO fiber are opened, mixed, combed and woven into threads in sequence, and then woven and connected to form a puncture-resistant woven fabric through the "joint bonding method";

[0057]S3. Preparation of connecting layer 2 threads: spun into stainless steel spun yarn by spinning technology, and stainless steel spun yarn is covered with aluminum foil to make stainless steel twisted yarn;

[0058]S4. Preparation of polyurethane adhesive: use the following weight component ratio: toluene diisocyanate (abbreviated as TDI) modified resin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a puncture-resistant high-wear-resistance woven curtain and a preparation method thereof. The puncture-resistant high-wear-resistant woven curtain is formed by weaving a plurality of tissue circulations, and is characterized in that each tissue circulation comprises an outer protective layer, a puncture-resistant layer, a connecting layer and an inner protective layer, theconnecting layer is arranged between the puncture-resistant layer and the outer protective layer, the connecting layer is connected with the outer protective layer and the puncture-resistant layer ina weaving mode through through a weft and warp connecting method, and the inner protective layer is bonded to the face, away from the outer protective layer, of the puncture-resistant layer through anadhesive layer; the outer protective layer comprises eight pieces of warp yarn and eight pieces of weft yarn, the warp yarn is fibers with tensile strength higher than 150 cN/tex, and the weft yarn is glass fibers. The curtain prepared by the invention has the characteristics of high strength, high modulus, heat resistance and flame retardance; the puncture resistance of the curtain is strong, sothat the whole curtain can be completely protected when people carelessly scratch or stab the curtain with a sharp object.

Description

technical field [0001] The invention relates to the technical field of curtains, in particular to a puncture-resistant and highly wear-resistant woven curtain and a preparation method thereof. Background technique [0002] Curtain is made by materials such as cloth, fiber crops, yarn etc., has the function of sunshading and heat-insulating and adjustment indoor light. Cloth curtains are divided into cotton gauze, polyester cloth, polyester-cotton blended, cotton-linen blended, non-woven fabrics, etc. according to the material. Different materials, textures, colors, patterns, etc. are combined to form different styles of cloth curtains. Interior design curtains. [0003] The origin of puncture-resistant individual armor can be traced back to 2500 BC, the cloaks worn by warriors on the Mesopotamian plains, copper or bronze helmets, and hakamas that may be made of metal and leather. It was later developed to fix metal sheets on soft substrates such as leather or linen. The c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/56D03D13/00B32B27/40B32B27/32B32B27/02B32B27/36B32B27/34B32B9/02B32B9/04B32B7/12B32B37/12B32B38/16
CPCD03D13/00B32B5/02B32B5/26B32B7/12B32B37/1284B32B38/164D10B2503/02D10B2331/04D10B2331/30B32B2262/0253B32B2262/0269B32B2262/103B32B2262/0292B32B2262/08B32B2307/51B32B2307/3065B32B2307/584B32B2601/00
Inventor 王高华戴忠飞邱会杰
Owner 海宁优韵家居有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap