Preparation method of photocatalytic complexing agent with high light conductivity and high adsorption performance for purifying air

A technology for air purification and light conductivity, which is applied in the direction of catalyst activation/preparation, physical/chemical process catalysts, chemical instruments and methods, etc., can solve problems affecting the efficiency of photocatalytic degradation of organic pollutants, etc., to promote photocatalytic reactions, Improves light absorption rate and promotes the effect of improving efficiency

Active Publication Date: 2020-04-10
绍兴蓝竹新材料科技有限公司
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the adsorption performance of activated carbon particles on water molecules will affect the efficiency of photocatalytic degradation of organic pollutants.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of photocatalytic complexing agent with high light conductivity and high adsorption performance for purifying air
  • Preparation method of photocatalytic complexing agent with high light conductivity and high adsorption performance for purifying air

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 1) Synthesis of composite adsorption carrier: Mix and stir the following components by weight, granulate and shape, and dry at 100°C: 50 parts of bamboo activated carbon powder, 20 parts of nano-titanium dioxide powder, 10 parts of glass fiber, and 30 parts of pumice powder , 15 parts of silica sol with a solid content of 20%, 2 parts of hydrogen peroxide with a mass fraction of 30%; the particle size range of the bamboo activated carbon powder is 1-150um, and the average particle diameter is 40um; the nano titanium dioxide powder is anatase crystal form, particle size less than 5nm; the size of the glass fiber is 200-400um in length and 20-40um in diameter; the glass fiber is quartz glass fiber; the particle size of the pumice powder is 100-200 mesh; The particle size of molding is 5-20mm.

[0028] 2) Synthesis of Pd / TiO 2 Composite colloid solution: first dissolve palladium nitrate in concentrated nitric acid, stir well and heat to 60°C, add titanium salt precursor d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a photocatalytic complexing agent with high light conductivity and high adsorption performance for purifying air. The preparation method comprises the following steps: (1) synthesizing a composite adsorption carrier; (2) synthesizing a Pd / TiO2 composite colloidal solution, wherein the content of Pd in the Pd / TiO2 composite colloidal solution is controlled to be 0.001-0.1 wt%; and (3) immersing the composite adsorption carrier prepared in the step (1) into the Pd / TiO2 composite colloidal solution prepared in the step (2) for 10-120 minutes, takingout the composite adsorption carrier, and drying the composite adsorption carrier at 25-100 DEG C to obtain the photocatalytic complexing agent with high light conductivity and high adsorption performance for purifying air. The photocatalytic complexing agent with high light conductivity and high adsorption performance for purifying air has high purification efficiency, good water resistance andhigh adsorption performance.

Description

technical field [0001] The invention relates to the technical field of air purification materials, in particular to a preparation method of a photocatalytic composite agent for purifying air with high light conductivity and high adsorption performance. Background technique [0002] At present, there are various products for air purification such as activated carbon, photocatalyst (photocatalysis), aldehyde remover and other products on the market, but there are relatively few photocatalytic activated carbon particles or photocatalytic composite porous adsorption products, and some photocatalytic composite products are also prepared. Mainly use titanium-based liquid or titanium dioxide sol liquid as the precursor liquid to undergo soaking, drying, high-temperature treatment and other processes. Some photocatalytic air purification effects are not very ideal. The photocatalytic loading methods mainly include powder sintering method, dipping and pulling method, Sol-gel method, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/44B01J37/02B01J37/34B01D53/86B01D53/72B01J20/20B01J20/30
CPCB01J23/44B01J37/0063B01J37/345B01J37/0201B01J35/004B01J20/20B01J20/103B01D53/8668B01D2255/802B01D2257/70Y02A50/20
Inventor 金小燕曾亮亮方桂煌张国栋
Owner 绍兴蓝竹新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap