Cement paste for hydrate well cementation and preparation method thereof

A technology of cement slurry and hydrate, which is applied in the direction of drilling compositions, chemical instruments and methods, etc., can solve the problems of long thickening time and inability to guarantee, and achieve the effect of reducing waiting setting time and fast strength

Active Publication Date: 2020-04-24
BC P INC CHINA NAT PETROLEUM CORP +2
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above cement slurries have good strength development at low temperature, but they cannot guarantee a longer thickening time at a higher temperature of 30°C

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cement paste for hydrate well cementation and preparation method thereof
  • Cement paste for hydrate well cementation and preparation method thereof
  • Cement paste for hydrate well cementation and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] In the second aspect, the embodiment of the present invention also provides a method for preparing cement slurry for hydrate cementing related to the first aspect, the preparation method comprising the following steps:

[0042] Step a, mixing the oil well cement, lightening reinforcement material, drag reducer, and expansion agent evenly to form a dry mixture,

[0043] Step b, mixing the enhancer and water to form a mixed liquid;

[0044] Step c. Uniformly mixing the dry mixture and the mixing solution to form cement slurry.

[0045]The cement slurry prepared by the method provided in the embodiment of the present invention can be used for the cementing of hydrates in sea areas with a temperature of 4-30°C through the synergistic compounding of the above-mentioned components. The thickening time of the cement slurry is It can meet the safety construction requirements at 30°C, and the strength develops faster at a low temperature of 4°C, reducing the waiting time for se...

Embodiment 1

[0048] This example provides a cement slurry for hydrate cementing, which is prepared by the following components in weight ratio: 100 parts of oil well cement, 0.5 part of drag reducer, 0.5 part of expansion agent, 3 parts of reinforcing agent and 43 parts of water. The density of the cement slurry prepared by this formula is 1.90g / cm 3 .

Embodiment 2

[0050] This example provides a cement slurry for hydrate cementing, which is prepared by the following components in weight ratio: 100 parts of oil well cement, 10 parts of lightening and reinforcing materials, 0.3 parts of drag reducer, 1.5 parts of expansion agent, 2 parts enhancer and 45 parts water. The density of the cement slurry prepared by this formula is 1.80g / cm 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cement paste for hydrate well cementation and a preparation method thereof, and belongs to the field of well cementation operation. The cement paste is prepared from the following components in parts by weight: 100 parts of oil well cement, 0-60 parts of a lightening and reinforcing material, 0.1-1.0 part of a drag reducer, 0.5-1.5 parts of an expanding agent, 2-7 parts of a reinforcing agent and 43-80 parts of water, wherein the lightening and reinforcing material is prepared from the following components in parts by weight: 50 parts of hollow microspheres, 35 partsof superfine cement, 5 parts of nano calcium carbonate and 10 parts of superfine meta-kaolin. Through synergistic compounding of the aforementioned components, the prepared cement paste can be used for exploitation and well cementation of hydrates in sea areas at the temperature of 4-30 DEG C, the thickening time of the cement paste can meet the safety construction requirement at the temperature of 30 DEG C, the strength development is faster at the low temperature of 4 DEG C, the waiting time is shortened; and after the cement paste is solidified, the requirements of supporting a wellhead device and annulus sealing can be met.

Description

technical field [0001] The invention relates to the field of well cementing operations, in particular to a cement slurry for hydrate well cementing and a preparation method thereof. Background technique [0002] The cementing operation during hydrate exploitation is the prerequisite and important guarantee for the effective exploration and development of hydrate resources. The annulus of hydrate cementing is large, and plug flow or near plug flow is generally used to replace it. The construction time is long, and the cement slurry needs to have enough pumping time to meet the safe construction, which requires the cement slurry to be operated at a higher temperature (such as 30°C). It has a longer thickening time and develops strength quickly at low temperature (eg 4°C). [0003] Currently, there are many cement slurries that can be used for hydrate cementing. For example, the patent application number 201710010738.X discloses a low-density cement slurry system for deep-wate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/02C09K8/467
CPCC04B28/026C09K8/467C04B2111/00008C04B2201/20C04B2111/00724C04B2201/50C04B20/002C04B7/00C04B14/28C04B14/106C04B24/30C04B22/148C04B22/06C04B24/121C04B22/124C04B22/085
Inventor 席方柱孙富全杨昆鹏刘爱萍王友华宋本岭黄志刚熊钰丹李鹏晓石凌龙
Owner BC P INC CHINA NAT PETROLEUM CORP