Preparation method of aluminum alloy
An aluminum alloy and component adjustment technology, applied in the field of aluminum alloy, can solve problems such as poor surface quality and white lines, and achieve the effect of not increasing production costs
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0055] Aluminum alloys were prepared as follows:
[0056]Batching, smelting, composition adjustment, melt purification, grain refinement, casting, sawing, milling, rolling, packaging, delivery (user), slitting, capping and anodizing are carried out in sequence;
[0057] In the batching process, the mass content of Si is controlled to be ≤0.10%, and the mass content of Fe is ≤0.18wt%;
[0058] During the smelting process, the alloy raw materials were sampled and analyzed after melting, and the mass content of the Ti element was adjusted to 0.005%; the temperature of the furnace refining was 730°C, and the time of the furnace refining was 15 minutes; the refining gas of the online degassing and refining It is argon, the temperature of online degassing and refining is 720°C, and the temperature of online filtration is 710°C; the mass content of Ti element in front of the furnace is controlled at 0.005%; Produce alloys with low content of Fe and Ti elements, and appropriately red...
Embodiment 2
[0072] Aluminum alloys were prepared as follows:
[0073] Batching, smelting, composition adjustment, melt purification, grain refinement, casting, sawing, milling, rolling, packaging, delivery (user), slitting, capping and anodizing are carried out in sequence;
[0074] In the batching process, the mass content of Si is controlled to be ≤0.10%, and the mass content of Fe is ≤0.18wt%;
[0075] During the smelting process, the alloy raw materials were sampled and analyzed after melting, and the mass content of the Ti element was adjusted to 0.005%; the temperature of the furnace refining was 740°C, and the time of the furnace refining was 25 minutes; the refining gas of the online degassing and refining It is argon, the temperature of online degassing and refining is 730°C, and the temperature of online filtration is 720°C; the mass content of Ti element in front of the furnace is controlled at 0.005%; Produce alloys with low content of Fe and Ti elements, and appropriately re...
Embodiment 3
[0089] Aluminum alloys were prepared as follows:
[0090] Batching, smelting, composition adjustment, melt purification, grain refinement, casting, sawing, milling, rolling, packaging, delivery (user), slitting, capping and anodizing are carried out in sequence;
[0091] In the batching process, the mass content of Si is controlled to be ≤0.10%, and the mass content of Fe is ≤0.18wt%;
[0092] During the smelting process, the alloy raw materials were sampled and analyzed after melting, and the mass content of the Ti element was adjusted to 0.005%; the temperature of the furnace refining was 750° C., and the time of the furnace refining was 30 minutes; the refining gas of the on-line degassing and refining It is argon, the temperature of online degassing and refining is 745°C, and the temperature of online filtration is 730°C; the mass content of Ti element in front of the furnace is controlled at 0.005%; Produce alloys with low content of Fe and Ti elements, and appropriately...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com