Phthalimide modified room temperature vulcanized fireproof silicone rubber and preparation method thereof

A phthalimide, room temperature vulcanization technology, applied in the field of fireproof glue, can solve the problems of affecting human health and the environment, difficult flame retardant performance, adhesion performance and aging resistance, high addition ratio, etc., to achieve flame retardant And the effect of excellent fire-proof and leak-stopping performance, high bonding strength and excellent aging resistance

Active Publication Date: 2022-06-07
HUBEI HUITIAN NEW MATERIALS STOCK CO LTD +2
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, many fire-resistant adhesive products use halogen-based, phosphorus-based and other flame-retardant fillers, but this type of fire-resistant adhesive will release toxic and harmful substances during the flame-retardant process, which will affect human health and the environment.
In addition, some fireproof adhesives use environmentally friendly aluminum-magnesium flame-retardant fillers mainly based on aluminum hydroxide and magnesium hydroxide, but a relatively high addition ratio is required to exert the flame-retardant effect. Composite index requirements for performance and aging resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phthalimide modified room temperature vulcanized fireproof silicone rubber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment provides a phthalimide-modified room temperature vulcanization fire-resistant silicone rubber, which is prepared from the following raw materials in parts by weight: phthalimide-modified hydroxyl-terminated polysiloxane polymer 100 parts, 90 parts of flame retardant filler, 65 parts of nano-activated calcium carbonate, 15 parts of plasticizer, 4 parts of color paste, 1 part of flame retardant accelerator, 10 parts of crosslinking agent, 3 parts of composite silane coupling agent, 0.03 part of catalyst share.

[0034] The preparation method of the phthalimide modified room temperature vulcanization fireproof silicone rubber of the present embodiment comprises the following steps:

[0035] (1) Preparation of N-(3-(dimethoxymethylsilyl)propyl)phthalimide: The phthalimide was reacted with an aqueous potassium hydroxide solution at 25°C for 6h, and the reaction was completed. After filtering, the filter residue was washed with water until it was about neutra...

Embodiment 2

[0039] This embodiment provides a phthalimide-modified room temperature vulcanization fire-resistant silicone rubber, which is prepared from the following raw materials in parts by weight: phthalimide-modified hydroxyl-terminated polysiloxane polymer 100 parts, 75 parts of flame retardant filler, 76 parts of nano-activated calcium carbonate, 18 parts of plasticizer, 4 parts of color paste, 1 part of flame retardant accelerator, 10 parts of crosslinking agent, 3 parts of composite silane coupling agent, 0.03 part of catalyst share.

[0040] The preparation method of a kind of phthalimide modified room temperature vulcanization fireproof silicone rubber of the present embodiment comprises the following steps:

[0041] (1) 100:50:150 of N-(3-(dimethoxymethylsilyl)propyl)phthalimide, methylphenyldimethoxysilane, and hydroxyl-terminated polydimethylene Siloxane, stir and react under vacuum at 100±10°C for 4-5h, then heat up to 170±10°C, remove low boiling point substances and deco...

Embodiment 3

[0044] This embodiment provides a phthalimide-modified room temperature vulcanization fireproof silicone rubber prepared from the following raw materials in parts by weight: 100 parts of phthalimide-modified hydroxyl-terminated polysiloxane polymer , 90 parts of flame retardant filler, 72 parts of nano-active calcium carbonate, 15 parts of plasticizer, 4 parts of color paste, 1 part of flame retardant accelerator, 10 parts of crosslinking agent, 3 parts of composite silane coupling agent, 0.05 part of catalyst .

[0045] The preparation method of a kind of phthalimide modified room temperature vulcanization fireproof silicone rubber of the present embodiment comprises the following steps:

[0046] (1) 100:58:190 N-(3-(dimethoxymethylsilyl)propyl)phthalimide, methylphenyldimethoxysilane, hydroxyl-terminated polydimethyl siloxane, after stirring and reacting under vacuum conditions of 100±10℃ for 4-5h, the temperature was raised to 170±10℃ to remove low-boiling substances and d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to a phthalimide modified room temperature vulcanized fireproof silicone rubber and a preparation method thereof. The modified room temperature vulcanized fireproof silicone rubber is modified by a specific proportion of phthalimide to It is prepared from alkane polymers, flame retardant fillers, reinforcing fillers, plasticizers, colorants, flame retardant accelerators, crosslinking agents, composite silane coupling agents, and catalysts. The phthalimide-modified fireproof silicone adhesive can meet the requirements of various types of doors, windows, curtain walls, sealing and fireproofing. The introduction of N element in dicarboximide-modified hydroxyl-terminated polysiloxane polymer and the addition of environmentally friendly flame-retardant fillers and flame-retardant accelerators in the formula make the product's flame-retardant grade reach FV0 through the synergy of the three.

Description

[0001] Technology neighborhood [0002] The invention relates to the field of fireproof glue, in particular to a phthalimide modified room temperature vulcanization fireproof silicone rubber and a preparation method thereof. Background technique [0003] With the rapid development of urbanization and construction industry in China, more and more high-rise complex buildings have been widely constructed. Safety is the primary factor to be considered in architectural design, and fire protection of high-rise buildings has become the top priority. Once a fire occurs, it is very important to prevent the fire from spreading and make the material have a certain fireproof time. Fire blocking is the most effective fire prevention and smoke isolation method in architectural design at present, and is widely used in door and window systems and various pipes. Sealants are often used in door and window systems and various pipes. Therefore, more requirements are put forward for the sealant,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/08C08L83/04C08K13/06C08K9/06C08K9/04C08K3/26C08K3/22C08K5/544C08K5/5435C08G77/388C08G77/26C08G77/08C08G77/06C09J183/08C09J11/08C09J11/06C09J11/04
CPCC08G77/388C08G77/26C08G77/08C08G77/06C08L83/08C09J183/08C09J11/08C09J11/06C09J11/04C08L2201/02C08L2201/22C08L2205/02C08K2201/003C08K2201/011C08K2003/265C08K2003/2227C08K2201/014C08L83/04C08K13/06C08K9/06C08K9/04C08K3/26C08K3/22C08K5/544C08K5/5435
Inventor 蔡海涛王翠花刘钢章婧张兴龙赵勇刚章锋
Owner HUBEI HUITIAN NEW MATERIALS STOCK CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com