Austenitic stainless steel fillet weld ultrasonic detection method

A technology of austenitic stainless steel and detection method, which is applied to the analysis of solids using sonic/ultrasonic/infrasonic waves, material analysis using sonic/ultrasonic/infrasonic waves, and measuring devices, etc. To achieve the effect of ensuring the quality of the weld

Active Publication Date: 2020-07-28
NANJING CHENGUANG GRP
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the large difference in thickness in the direction of transillumination, defect position and direction angle, etc., some defects may not be detected by the radiographic inspection method, and the depth of the defect cannot be located.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Austenitic stainless steel fillet weld ultrasonic detection method
  • Austenitic stainless steel fillet weld ultrasonic detection method
  • Austenitic stainless steel fillet weld ultrasonic detection method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0052] Defects in austenitic fillet welds are mainly pores and slag inclusions in the weld, lack of fusion on the flange side, lack of fusion on the web side and incomplete penetration at the root. Insufficient fusion and incomplete penetration are the main defect types in this type of fillet weld, and they must be detected first. In order to solve this problem, the present invention proposes a method for ultrasonic testing of austenitic stainless steel fillet welds, comprising the following steps:

[0053] Step 1: Select the instrument. A type A pulse reflection ultrasonic flaw detector is adopted, and the working frequency of the flaw detector includes at least 0.5MHz-5MHz.

[0054] Step 2: Select the detection probe. According to different detection locations and objects, three types of probes are required: 1) dual-element longitudinal wave straight probe; 2) dual-element longitudinal wave oblique probe; 3) creeping wave probe.

[0055] 1) Double crystal longitudinal wav...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an austenitic stainless steel fillet weld ultrasonic detection method. The method comprises the steps that: an A-type pulse reflection type ultrasonic flaw detector is adopted;different types of probes are adopted according to different detection positions and objects; reference blocks are selected and manufactured; detection sensitivity is adjusted; a workpiece is prepared; scanning is performed through probes; defect quantification and evaluation are performed. A longitudinal wave bicrystal angle probe, a longitudinal wave bicrystal straight probe and a bicrystal creeping wave probe are comprehensively used; an angle butt joint comparison sample is developed; a set of special detection method is formed; the ultrasonic detection requirement of an austenitic stainless steel fillet weld is met; and the quality of the weld is guaranteed.

Description

technical field [0001] The invention relates to weld detection technology, in particular to an ultrasonic detection method for austenitic stainless steel fillet welds. Background technique [0002] Austenitic stainless steel grows up to form columnar grains when heated during the welding process, but there is no phase change during the subsequent cooling and solidification process, so the austenite at room temperature retains the coarse grains of austenite at high temperature. The columnar crystals formed during the welding process have the same orientation in the local area of ​​the weld, but their orientation will vary in different areas of the weld, which leads to the inhomogeneity and anisotropy of the entire weld area. [0003] The columnar grain structure, anisotropy and inhomogeneity of austenitic stainless steel welds bring difficulties to ultrasonic testing. When the direction of the sound beam is not selected properly, the displayed waveform will be disordered, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N29/04G01N29/24
CPCG01N29/04G01N29/24G01N2291/0289G01N2291/267
Inventor 许有昌孟哲耿永健张振单政马凯平德佳
Owner NANJING CHENGUANG GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com