Unlock instant, AI-driven research and patent intelligence for your innovation.

Modification method of hydrotalcite powder and its application in calcium zinc stabilizer

A talc and talc technology, applied in chemical instruments and methods, dyeing high molecular organic compound treatment, dyeing low molecular organic compound treatment and other directions, can solve the problems of poor production stability, waste of raw materials, and decreased gloss of products, etc. Achieve the effect of reducing precipitation, avoiding non-smooth, and good stability of lubricating components

Inactive Publication Date: 2021-11-05
LINAN HUALI PLASTIC +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And it also has some insurmountable shortcomings, that is, the thermal stability is extremely poor, and its thermal decomposition leads to the darkening of the product color and the decline of various indicators. It is necessary to use a thermal stabilizer to improve its thermal stability.
[0003] Calcium-zinc composite stabilizer is a composite stabilizer made of calcium, zinc and other metal soaps and salts as the main body, and other additives such as phosphite. It is an environmentally friendly stabilizer and is the main PVC-U environmental protection profile. The stabilizer used is mainly composed of calcium stearate and zinc stearate. In the production of PVC-U profiles, there are the following disadvantages: 1. There are needle-like precipitations in the production process, the gloss of the product decreases, and the production stability becomes poor. ;2. Poor welding in the inner cavity of the product, prone to broken tendons, requires irregular mold cleaning, which affects production efficiency and causes waste of raw materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modification method of hydrotalcite powder and its application in calcium zinc stabilizer
  • Modification method of hydrotalcite powder and its application in calcium zinc stabilizer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The preparation method of modified hydrotalcite powder is as follows:

[0030] Step S1: Raw material hydrotalcite is roughly selected, crushed to a certain particle size, and a certain amount of water and pulping aids are added to make a slurry. The pulping aids are composed of ethylhexyl phosphoric acid, sodium lauryl sulfate and Polyethylene glycol with a molecular weight of 200;

[0031] Step S2: purification;

[0032] Step S3: organic activation, adding a certain amount of organic ammonium salt and an activation auxiliary agent for a certain period of time, and the activation auxiliary agent is 1-ethyl-(3-dimethylaminopropyl)carbodiimide hydrochloride;

[0033] Step S4: filtering, drying, crushing and sieving to obtain modified hydrotalcite powder.

[0034] Among the present invention, the addition amount of pulping auxiliary agent is 3% of raw material hydrotalcite quality, and the mass ratio of sodium lignosulfonate in pulping auxiliary agent is 30%, and the mas...

Embodiment 2

[0036] The preparation method of modified hydrotalcite powder is as follows:

[0037] Step S1: Raw material hydrotalcite is roughly selected, crushed to a certain particle size, and a certain amount of water and pulping aids are added to make a slurry. The pulping aids are composed of ethylhexyl phosphoric acid, sodium lauryl sulfate and Polyethylene glycol with a molecular weight of 600;

[0038] Step S2: purification;

[0039] Step S3: organic activation, adding a certain amount of organic ammonium salt and an activation auxiliary agent for a certain period of time, and the activation auxiliary agent is 1-ethyl-(3-dimethylaminopropyl)carbodiimide hydrochloride;

[0040] Step S4: filtering, drying, crushing and sieving to obtain modified hydrotalcite powder.

[0041] Among the present invention, the addition amount of pulping auxiliary agent is 8% of raw material hydrotalcite quality, and the mass ratio of sodium lignosulfonate in pulping auxiliary agent is 40%, and the mas...

Embodiment 3

[0043] The preparation method of modified hydrotalcite powder is as follows:

[0044] Step S1: Raw material hydrotalcite is roughly selected, crushed to a certain particle size, and a certain amount of water and pulping aids are added to make a slurry. The pulping aids are composed of ethylhexyl phosphoric acid, sodium lauryl sulfate and Polyethylene glycol with a molecular weight of 400;

[0045] Step S2: purification;

[0046] Step S3: organic activation, adding a certain amount of organic ammonium salt and an activation auxiliary agent for a certain period of time, and the activation auxiliary agent is 1-ethyl-(3-dimethylaminopropyl)carbodiimide hydrochloride;

[0047] Step S4: filtering, drying, crushing and sieving to obtain modified hydrotalcite powder.

[0048]In the present invention, the mass ratio of sodium lauryl sulfate in the pulping aid is 35%, the mass percentage of ethylhexyl phosphoric acid is 4%, and the balance is polyethylene glycol. In the organic activa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a modification method of hydrotalcite powder and its application in calcium zinc stabilizer. Slurry, the pulping aid is composed of ethylhexyl phosphoric acid, sodium lauryl sulfate and polyethylene glycol with a molecular weight of 200-600; step S2: purification; step S3: organic activation, adding a certain amount of organic ammonium Salt and activation auxiliary agent, activation reaction for a certain period of time, the activation auxiliary agent is 1-ethyl-(3-dimethylaminopropyl) carbodiimide hydrochloride; step S4: filter, dry, pulverize and sieve, Obtain modified hydrotalcite powder. The inventors of the present application found that the modified hydrotalcite powder has a good lubricating component stability effect, and the highly dispersed adsorption and / or anchoring of the lubricating component in the modified hydrotalcite powder greatly reduces the precipitation and avoids PVC ‑U roughness of the sheet.

Description

technical field [0001] The invention relates to a method for modifying hydrotalcite powder and its application in calcium-zinc stabilizers, and belongs to the technical field of composite calcium-zinc stabilizer processing. Background technique [0002] PVC is one of the five general-purpose plastics, widely used in industry, construction, agriculture and other fields. And it also has some insurmountable shortcomings, that is, its thermal stability is extremely poor, and its thermal decomposition causes the color of the product to become darker, and various indicators drop, so it is necessary to use a thermal stabilizer to improve its thermal stability. [0003] Calcium-zinc composite stabilizer is a composite stabilizer made of calcium, zinc and other metal soaps and salts as the main body, and other additives such as phosphite. It is an environmentally friendly stabilizer and is the main PVC-U environmental protection profile. The stabilizer used is mainly composed of cal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09C1/40C09C3/04C09C3/08C09C3/10C08K9/04C08K3/26C08L27/06C08L33/04C08L23/28C08K13/06C08K3/22
CPCC01P2006/37C08K3/26C08K9/04C08K9/08C08K2003/2241C08K2003/265C08L27/06C08L2201/08C08L2205/03C09C1/407C09C3/006C09C3/04C09C3/08C09C3/10C08L33/04C08L23/286C08K13/06C08K3/22
Inventor 楼超民陈云海刘忠清杨家成
Owner LINAN HUALI PLASTIC
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com