A kind of anti-polarity algainp red LED tube core structure and manufacturing method thereof

A production method and reverse polarity technology, which is applied to semiconductor devices, electrical components, circuits, etc., can solve problems such as limited yield rate of bonding wires and difficulty in the production of main electrode ITO, so as to improve the yield rate of bonding wires and improve the welding performance. The effect of enhancing the line yield and adhesion performance

Active Publication Date: 2021-06-08
SHANDONG INSPUR HUAGUANG OPTOELECTRONICS
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to the traditional packaging process, the wire bonding is carried out on the main electrode. From the design method of the present invention, it is difficult to realize the production of ITO on the main electrode, and only make the ITO film on the extended electrode. Improvement is relatively limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-polarity algainp red LED tube core structure and manufacturing method thereof
  • A kind of anti-polarity algainp red LED tube core structure and manufacturing method thereof
  • A kind of anti-polarity algainp red LED tube core structure and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] A reverse polarity AlGaInP red LED tube core structure, such as Figure 14 As shown, it includes N-face electrode 18, permanent silicon substrate 11, second mirror layer 12, metal adhesion layer 13, first mirror layer 10, SiO2 barrier layer 8 and ohmic contact layer 9 from bottom to top. , P-GaAs layer 7, P-AlGaInP layer 6, MQW quantum well layer 5, N-AlGaInP layer 4, N-GaAs layer 3 and ITO film layer 15 and SiO2 protective layer 17, extended electrode 14, main electrode 16;

[0067] The surface of the P-AlGaInP layer 6 has been roughened; the main electrode 16 is arranged on part of the ITO film layer 15; the SiO2 protection layer 17 fills the gap between the part of the ITO film layer 15 and the remaining part of the ITO film layer 15, and covers the remaining part The ITO film layer 15 and the extended electrode 14 are arranged on the N-GaAs layer 3 .

[0068] Use the ITO film layer 15 to replace the AlGaInP layer to directly contact the main electrode 16, and utili...

Embodiment 2

[0074]According to a kind of reverse polarity AlGaInP red light LED pipe core structure described in embodiment 1, its difference is that, the thickness of ITO film layer 15 is 20 angstroms;

Embodiment 3

[0076] According to a kind of reverse polarity AlGaInP red light LED pipe core structure described in embodiment 1, its difference is that, the thickness of ITO film layer 15 is 50 angstroms;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a reverse polarity AlGaInP red light LED tube core structure and a manufacturing method thereof, belonging to the technical field of semiconductor processing, comprising the following specific steps: (1) wafer bonding; (2) substrate removal; (3) expanding electrodes Production; (4) roughening layer production; (5) ITO adhesion layer production; (6) main electrode production; (7) protective layer production; (8) tube core production. The present invention enhances the adhesion firmness between the metal main electrode and ITO by making a thin ITO film layer, and realizes a substantial increase in the yield rate of the welding wire. Reflection increases the light output efficiency of the tube core, the principle of the whole manufacturing process is simple, and the process method is convenient; the tube core produced by the method of the present invention has stable overall quality, high yield rate, and good overall stability. This method is applicable to all reflectors. Manufacturing process of polar AlGaInP-based red LED chips.

Description

technical field [0001] The invention relates to a reverse polarity AlGaInP red light LED tube core structure and a manufacturing method thereof, belonging to the technical field of semiconductor processing. Background technique [0002] A light-emitting diode, referred to as LED (Light Emitting Diode), is a solid-state electroluminescent (EL) semiconductor device that converts electrical energy into light energy. High-brightness and high-power AlGaInP red light LED is a common visible light LED that has been widely developed in recent years. AlGaInP quaternary red light LED has many advantages such as strong current bearing capacity, high luminous efficiency and high temperature resistance. The application in has an irreplaceable position and is widely used in various fields of lighting. [0003] At present, there are still two major problems in large-scale production of high-power AlGaInP reverse polarity red LEDs, one is the luminous brightness, and the other is the probl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01L33/06H01L33/40H01L33/46H01L33/30H01L33/00
CPCH01L33/0062H01L33/06H01L33/30H01L33/40H01L33/46
Inventor 徐晓强张兆喜吴向龙闫宝华王成新
Owner SHANDONG INSPUR HUAGUANG OPTOELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap