A kind of mercerized elastic fabric coated with flax and XLA fiber and preparation method thereof
A flax fiber and flax technology, applied in the field of mercerized elastic fabric and its preparation, can solve the problems of poor adhesion between flax fiber and elastic fiber filament, product quality problems, separation of flax fiber and elastic fiber filament, etc., and achieve improvement Effects of adhesion, improvement of connection strength, and improvement of uniform dispersion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0023] A kind of mercerized elastic fabric covered with linen XLA fiber, described elastic fabric is woven by flax elastic core-spun yarn; Described flax elastic core-spun yarn comprises flax fiber, XLA elastic fiber, intermediate layer; Described intermediate layer is attached to Around the outside of the XLA elastic fiber; the flax fiber is wrapped around the outside of the middle layer; the components and parts by weight of the middle layer are as follows: 10 parts of nano aluminum oxide, 5 parts of hexagonal boron nitride, 20 parts of bamboo fiber part, 10 parts of epoxy resin.
[0024] A preparation method of a mercerized elastic fabric coated with flax XLA fiber, the steps are as follows:
[0025] S1. Flax treatment: select raw flax with a splitting degree greater than or equal to 250 pieces, and beat the raw flax into flax; spray the flax with an aqueous solution containing a humidifying agent for humidification; then use a sliver machine to make flax, and flax successi...
Embodiment 2
[0031] A kind of mercerized elastic fabric covered with linen XLA fiber, described elastic fabric is woven by flax elastic core-spun yarn; Described flax elastic core-spun yarn comprises flax fiber, XLA elastic fiber, intermediate layer; Described intermediate layer is attached to Around the outside of the XLA elastic fiber; the flax fiber is wrapped around the outside of the middle layer; the components and parts by weight of the middle layer are as follows: 15 parts of nano aluminum oxide, 16 parts of hexagonal boron nitride, 25 parts of bamboo fiber part, 15 parts of epoxy resin.
[0032] A preparation method of a mercerized elastic fabric coated with flax XLA fiber, the steps are as follows:
[0033] S1. Flax treatment: select raw flax with a splitting degree greater than or equal to 250 pieces, and beat the raw flax into flax; spray the flax with an aqueous solution containing a humidifying agent for humidification; then use a sliver machine to make flax, and flax success...
Embodiment 3
[0039] A kind of mercerized elastic fabric covered with linen XLA fiber, described elastic fabric is woven by flax elastic core-spun yarn; Described flax elastic core-spun yarn comprises flax fiber, XLA elastic fiber, intermediate layer; Described intermediate layer is attached to Around the outside of the XLA elastic fiber; the flax fiber is wrapped around the outside of the middle layer; the components and parts by weight of the middle layer are as follows: 20 parts of nano aluminum oxide, 10 parts of hexagonal boron nitride, 30 parts of bamboo fiber part, 15 parts of epoxy resin.
[0040] A preparation method of a mercerized elastic fabric coated with flax XLA fiber, the steps are as follows:
[0041] S1. Flax treatment: select raw flax with a splitting degree greater than or equal to 250 pieces, and beat the raw flax into flax; spray the flax with an aqueous solution containing a humidifying agent for humidification; then use a sliver machine to make flax, and flax success...