A kind of mercerized elastic fabric coated with high elastic linen XLA fiber and preparation method thereof
A technology of high elasticity and elastic fiber, which is applied in the direction of textile, yarn, textile and paper making, and can solve the problems of separation of flax fiber and elastic fiber filament, product quality problems, poor adhesion of flax fiber and elastic fiber filament, etc. , to achieve the effect of improving the degree of adhesion, stabilizing the connection, and improving the connection strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0025] A kind of mercerized elastic fabric of high elastic linen covering XLA fiber, described elastic fabric is woven by flax elastic core-spun yarn; Described linen elastic core-spun yarn comprises flax fiber, XLA elastic fiber, middle layer; Said middle layer Attached to the outer periphery of the XLA elastic fiber; the flax fiber is wrapped around the outer periphery of the middle layer; the components and parts by weight of the middle layer are as follows: 10 parts of nano aluminum oxide, 5 parts of hexagonal boron nitride, bamboo 20 parts of fiber, 4 parts of magnesium carbonate, 10 parts of epoxy resin.
[0026] A preparation method of a mercerized elastic fabric coated with high-elasticity linen XLA fiber, the steps are as follows:
[0027] S1. Flax treatment: select raw flax with a splitting degree greater than or equal to 250 pieces, and beat the raw flax into flax; spray the flax with an aqueous solution containing a humidifying agent for humidification; then use a ...
Embodiment 2
[0033] A kind of mercerized elastic fabric of high elastic linen covering XLA fiber, described elastic fabric is woven by flax elastic core-spun yarn; Described linen elastic core-spun yarn comprises flax fiber, XLA elastic fiber, middle layer; Said middle layer Attached to the outer periphery of the XLA elastic fiber; the flax fiber is wrapped around the outer periphery of the middle layer; the components and parts by weight of the middle layer are as follows: 15 parts of nano aluminum oxide, 16 parts of hexagonal boron nitride, bamboo Fiber 25 parts, magnesium carbonate 6 parts, epoxy resin 15 parts.
[0034] A preparation method of a mercerized elastic fabric coated with high-elasticity linen XLA fiber, the steps are as follows:
[0035]S1. Flax treatment: select raw flax with a splitting degree greater than or equal to 250 pieces, and beat the raw flax into flax; spray the flax with an aqueous solution containing a humidifying agent for humidification; then use a sliver ma...
Embodiment 3
[0041] A kind of mercerized elastic fabric of high elastic linen covering XLA fiber, described elastic fabric is woven by flax elastic core-spun yarn; Described linen elastic core-spun yarn comprises flax fiber, XLA elastic fiber, middle layer; Said middle layer Attached to the outside of the XLA elastic fiber around the outside; the flax fiber is wrapped around the outside of the middle layer; the components and parts by weight of the middle layer are as follows: 20 parts of nano aluminum oxide, 10 parts of hexagonal boron nitride, bamboo Fiber 30 parts, magnesium carbonate 8 parts, epoxy resin 15 parts.
[0042] A preparation method of a mercerized elastic fabric coated with high-elasticity linen XLA fiber, the steps are as follows:
[0043] S1. Flax treatment: select raw flax with a splitting degree greater than or equal to 250 pieces, and beat the raw flax into flax; spray the flax with an aqueous solution containing a humidifying agent for humidification; then use a slive...