Quantum dot modified iron cobalt oxide and its preparation method and application

A technology of quantum dots and oxides, applied in the field of environmental treatment, can solve problems such as low catalytic efficiency, and achieve the effects of high catalytic efficiency, simple operation and wide temperature range

Active Publication Date: 2021-03-30
HUNAN UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional metal oxide catalysts have the disadvantage of low catalytic efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quantum dot modified iron cobalt oxide and its preparation method and application
  • Quantum dot modified iron cobalt oxide and its preparation method and application
  • Quantum dot modified iron cobalt oxide and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A quantum dot modified iron cobalt oxide of the present invention, mainly by iron-containing cobalt Blew Blue analog, benzyl alcohol, cobalt-containing ion organic compound with ammonia water, and heat treatment, iron-containing Cobalt Push Blue Similar The substance is a metal organic frame compound which is mainly made of iron cobalt oxide and the CO loaded on the iron cobalt oxide. 3 O 4 Quantum point consists.

[0040] In this embodiment, the iron-containing Cobalt Blewass Blue enumeration is prepared from the potassium hydrocarbonate solution and the cobalt ion solution.

[0041] In this embodiment, CO 3 O 4 The particle diameter of the quantum dot is 5 nm to 10 nm.

[0042] A method of preparing a quantum point modified iron cobalt oxide in the present embodiment, comprising the steps of:

[0043] S1, a 1L concentration of 20 mM a cobalt cyanide solution was mixed with a 1L concentration of 40 mm, magnetic force for 2 h, centrifugal, and centrifugally, the iron-contai...

Embodiment 2

[0050] An application of the quantum dot modified iron cobalt oxide in the treatment of antibiotic wastewater, specifically, the quantum point modified iron cobalt oxide produced by the first embodiment of the present invention removes tetracycline in the water body, including the following steps:

[0051] The volume of 1 l, a concentration of 50 mg / L was taken, and 1.0 g of quantum dot modified iron cobalt oxide and 1 g of sodium sulfate solids, after mixing, adjust the initial pH of the resulting mixture of 7, at room temperature conditions The sulfate activated oxidation reaction was carried out to complete degradation of tetracycline.

[0052] The control group was 1 to a tetracycline solution having a volume of 1 L, a concentration of 50 mg / L, and a sodium sulfate solid was added. After mixing is uniform, the initial pH of the resulting mixture was 7, and the sulfate was carried out under room temperature. Reaction, complete degradation of tetracycline.

[0053] The contr...

Embodiment 3

[0058] Taking a quantum dotted iron cobalt oxide prepared in the water body in the water body, a quantum dot modified iron cobalt oxide prepared in Example 1, including the following steps:

[0059] The quantum dot modified iron cobalt oxide prepared in 0.5 g, 1.0 g, 2.0 g, 3.0 g and 4.0 g of Example 1 was added 5 parts by volume of 50 mg / L, and the quantum dot modified iron cobalt oxide prepared in Example 1 was added. After adding 1 g of sodium sulfate, after mixing, the initial pH of the resulting mixture was 7, and the sulfate activated oxidation reaction was carried out under room temperature conditions, and the degradation treatment of tetracycline was completed.

[0060] After 10 min, 20 min, 30 min, 45min, 60min, 75min, 90min, 45min, 60min, 75min, 90min, and 120min, 60min, 75min, 90min, and 120min, 60 min, 75min, 90min, and 120min, respectively, using high performance liquid chromatography to detect the content of tetracycline in the solution, see the measurement results...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
clearance rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a quantum dot modified iron cobalt oxide and its preparation method and application. The quantum dot modified iron cobalt oxide is mainly composed of iron-cobalt Prussian blue analogues, benzyl alcohol, cobalt ion-containing organic compounds and ammonia water. It is obtained by heat treatment after oil bath reaction. The preparation method includes coordinating potassium ferricyanide solution and cobalt ion solution to synthesize an iron-cobalt Prussian blue analog, dispersing it in benzyl alcohol, adding cobalt ion-containing organic compounds to dissolve, mixing with ammonia water for oil bath reaction, and then heat treatment. The product is obtained. The quantum dot modified iron cobalt oxide of the present invention has good dispersion, large specific surface area, many catalytic sites, high catalytic efficiency, good magnetism, easy separation and reuse, simple and convenient preparation process, low cost, and It is environmentally friendly and can be used to treat antibiotic wastewater. It has high removal efficiency, thorough removal effect, and no secondary pollution. It has good application prospects.

Description

Technical field [0001] The present invention belongs to the field of environmental governance, involving a quantum dot modified iron cobalt oxide and its preparation method and application thereof. Background technique [0002] Antibiotics is a kind of secondary metabolite produced by microorganisms (including bacteria, fungi, amplifier) ​​or high moving plants in life, is a class of unscrupulous. Chemical substances of normal development of cells. Antibiotics have been widely used due to the advantages of simple use of simple, stable chemical properties, high antibacterial spectrum, low price, small toxicity, and wide application. However, after the use of antibiotics, it cannot be completely absorbed by organisms, and most of them are discharged into water and soil environments with uretaries and feces in the form of protogah or metabolites (such as conjugate, hydrolyzate, etc.). Since antibiotic contaminants are not easily degraded, some antibiotics also have biological enrich...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/75B01J35/10C02F1/72C02F101/38C02F103/34
CPCB01J23/75C02F1/725C02F2101/38C02F2103/343B01J35/394B01J35/61
Inventor 刘洋刘智峰程敏邵彬彬梁清华张魏吴婷罗崧豪彭赞潘园周成赟汪文军
Owner HUNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com