ag-mno 2 /ac composite aldehyde removal material, its preparation method, aldehyde removal module and air purification equipment

A stirring and mixing, manganese dioxide technology, used in metal/metal oxide/metal hydroxide catalysts, separation methods, other chemical processes, etc., can solve the problem of inability to combine silver, manganese and activated carbon to form purification and aldehyde removal materials. , to achieve the effect of overcoming the short lifespan, enriching the pore structure and reducing the risk

Active Publication Date: 2022-01-07
GREE ELECTRIC APPLIANCES INC
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The main purpose of the present invention is to provide a kind of Ag-MnO 2 / AC composite aldehyde removal material, its preparation method, aldehyde removal module and air purification equipment to solve the problem that silver, manganese and activated carbon cannot be combined to form a purification aldehyde removal material in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] In a typical embodiment of the present application, a Ag-MnO 2 / AC composite formaldehyde removal material preparation method, the preparation method includes: step S1, potassium permanganate solution and porous carbon are mixed and continued for the first predetermined time, to obtain the first composite system; step S2, the first composite system with Ag + The solutions are mixed for a second predetermined time to obtain a second composite system; step S3, the second composite system is subjected to solid-liquid separation to obtain a solid isolate and a separated liquid; step S4, the solid isolate is subjected to a temperature of 60-100°C Dry to get Ag-MnO 2 / AC composite aldehyde removal material.

[0023] This application adopts the method of first loading manganese oxide on porous carbon and then loading silver, so that three kinds of aldehyde-removing materials can be effectively combined. Firstly, manganese oxides were supported on porous carbon using potassi...

Embodiment 1

[0043] 1) Select activated carbon with a particle size of 0.2 to 0.6 mm as the carrier, mix 5 mL of the above-mentioned configured potassium permanganate mother solution with 45 mL of deionized water to form a concentration of 0.05 mol / L potassium permanganate solution, and use the high Potassium manganate solution and 1 g of activated carbon were mixed and fully stirred at a stirring speed of 500 r / min and a stirring time of 60 min to obtain the first composite system.

[0044] 2) Take the Ag configured above + Mix 1mL of mother solution and 1mL deionized water to form Ag + The concentration is 0.05mol / L Ag + The solution was added into the first composite system, and the stirring was continued at a stirring rate of 500 r / min for 30 minutes to obtain the second composite system.

[0045] 3) Suction filtration and water washing of the second composite system obtained above to obtain a solid isolate, and then dry the obtained solid isolate in an oven at 80°C for 6 hours to ob...

Embodiment 2

[0047] 1) Select activated carbon with a particle size of 0.2 to 0.6 mm as the carrier, mix 5 mL of the above-mentioned configured potassium permanganate mother solution with 45 mL of deionized water to form a concentration of 0.05 mol / L potassium permanganate solution, and use the high Potassium manganate solution and 1 g of activated carbon were mixed and fully stirred at a stirring rate of 300 r / min and a stirring time of 60 min to obtain the first composite system.

[0048] 2) Take the Ag configured above + Mix 1mL of mother solution and 1mL deionized water to form Ag + The concentration is 0.05mol / L Ag + The solution was added into the first composite system, and the stirring was continued at a stirring rate of 500 r / min for 30 minutes to obtain the second composite system.

[0049] 3) Suction filtration and water washing of the second composite system obtained above to obtain a solid isolate, and then dry the obtained solid isolate in an oven at 80°C for 6 hours to obt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention provides a Ag-MnO 2 / AC composite aldehyde removal material, its preparation method, aldehyde removal module and air purification equipment. The preparation method includes: step S1, mixing potassium permanganate solution and porous carbon for a first predetermined time to obtain a first composite system; step S2, mixing the first composite system with Ag-containing + The solutions are mixed and continued for a second predetermined time to obtain a second composite system; Step S3, the second composite system is subjected to solid-liquid separation to obtain a solid isolate and a separated liquid; Step S4, the solid isolate is subjected to a temperature of 60-100°C dried to give Ag‑MnO 2 / AC composite aldehyde removal material. The method of loading manganese oxide on the porous carbon first and then loading silver is used to form an effective composite of the three aldehyde-removing materials. The formed formaldehyde-removing material uses activated carbon to absorb formaldehyde, and manganese oxide and nano-silver catalyze the oxidation of formaldehyde to form carbon dioxide and water, which prolongs the service life and avoids the problem of producing toxic substances.

Description

technical field [0001] The invention relates to the technical field of aldehyde-removing materials, in particular to an Ag-MnO 2 / AC composite aldehyde removal material, its preparation method, aldehyde removal module and air purification equipment. Background technique [0002] Formaldehyde (HCHO) is a common volatile organic compound in indoor air, which seriously endangers human health. Therefore, the removal and treatment of formaldehyde pollutants in indoor air has very important research significance. The main component used in air purifier filters today is activated carbon. Pure activated carbon filter materials mainly rely on adsorption to remove formaldehyde, and their service life is limited by the amount of adsorption saturation. Moreover, once activated carbon reaches adsorption saturation, toxic substances may be produced, endangering human health. . Studies have shown that formaldehyde can be completely converted into non-toxic and harmless CO through catalyt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D53/86B01D53/88B01D53/72B01J20/20B01J23/68B01D46/00
CPCB01D53/8668B01D53/885B01J20/20B01J23/688B01D46/0027B01D46/0028B01D46/0036B01D2255/2073B01D2255/104B01D2253/102B01D2258/06
Inventor 金星王贤波刘江王天龙胡康泽
Owner GREE ELECTRIC APPLIANCES INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More