Hot-dip galvanized dual-phase steel with good bake hardening performance and preparation method thereof

A bake-hardening and hot-dip galvanizing technology, which is applied in the field of steel preparation, can solve problems such as deficiencies and achieve good bake-hardening properties

Active Publication Date: 2021-11-19
SHOUGANG CORPORATION
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the domestic automobile industry has not required the BH value of high-strength steel for a long time. There has been a lack of detailed research and reports on how to stably control the increase in the bake-hardening value of ultra-high-strength steel and other materials used in automotive structural parts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot-dip galvanized dual-phase steel with good bake hardening performance and preparation method thereof
  • Hot-dip galvanized dual-phase steel with good bake hardening performance and preparation method thereof
  • Hot-dip galvanized dual-phase steel with good bake hardening performance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] The present invention also provides a preparation method of the hot-dip galvanized dual-phase steel with good bake hardening performance, the preparation method comprising:

[0045] Using the chemical composition of the hot-dip galvanized dual-phase steel with good bake hardening performance, continuous casting after smelting in a converter to obtain continuous casting slabs;

[0046] Heating the continuous casting slab, then performing rough rolling and finishing rolling, and coiling after cooling to obtain a hot-rolled finished product;

[0047] Pickling and cold-rolling the hot-rolled finished product to obtain chilled steel strip;

[0048] Annealing the chilled steel strip, followed by hot-dip galvanizing and finishing, to obtain the hot-dip galvanized dual-phase steel with good bake hardening performance; wherein the annealing includes a heating section, a soaking section, a slow cooling section and a rapid cooling section, the dew point in the heating section and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a hot-dip galvanized dual-phase steel with good baking hardening performance and a preparation method thereof. The chemical composition of the steel is calculated by mass fraction: C: 0.08%-0.12%, Si: 0.1%-0.4% , Mn: 1.8%~2.6%, Cr: 0.2%~0.7%, Mo: 0.1%~0.4%, P: ≤0.010%, S: ≤0.006%, Ti: 0.01%~0.04%, Al: 0.1%~ 0.4%, the balance is iron and other unavoidable impurities; the metallographic structure of the steel is: ferrite, martensite and bainite, and the carbon content in the ferrite reaches above 20ppm. The invention ensures that the carbon content dissolved in the ferrite reaches more than 20ppm, suppresses the surface decarburization of the steel plate during the heating process, and has no obvious decarburization layer between the finished plate substrate and the coating layer, thereby obtaining good bake hardening performance BH2 ≥80MPa.

Description

technical field [0001] The invention relates to the technical field of steel preparation, in particular to a hot-dip galvanized dual-phase steel with good bake hardening performance and a preparation method thereof. Background technique [0002] As the automotive industry has increasingly stringent requirements for lightweight, safety, and low emissions, the proportion of high-strength steel used in new automotive models continues to increase. A typical representative, in the body structure designed by the project of "ultra-light steel car body-advanced car concept", high-strength steel with a tensile strength of 1000MPa accounts for the largest proportion, accounting for 29% to 30% of the weight of the car body about. [0003] Now the car body needs to be painted during the production process, including drying and bonding paint during the body baking. The baking process not only helps the painting work, but also has a certain impact on the mechanical properties of the mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/06C22C38/22C22C38/28C22C38/38C21D8/02
CPCC21D8/0205C21D8/0226C21D8/0236C21D8/0247C21D2211/002C21D2211/005C21D2211/008C22C38/02C22C38/06C22C38/22C22C38/28C22C38/38
Inventor 邱木生韩赟刘华赛阳锋姜英花邹英滕华湘于孟章军朱国森李钊
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap