Sports daily protective mask
A technology for sports and face masks, applied in protective clothing, applications, clothing, etc., can solve the problems of no effective improvement of the adverse effects of the protective performance of masks, poor use effect, and reduced protective effect, etc., to achieve excellent performance , block the spread of viruses and bacteria, and promote the rapid development of the effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0013] A sports protective mask for daily use, comprising the following steps:
[0014] Add the prepared penetrating agent to the spinning precursor, the added mass ratio accounts for 0.4%; heat and stir in a constant temperature heating magnetic stirrer for 2 hours, the stirring temperature is 66 ° C, after natural cooling, shake evenly and use the syringe It was sucked and placed on an electrospinning device, and spun to obtain a fiber membrane with a grammage of 11 g / m2. The prepared fiber membrane is used as the sandwich filter layer of the mask, the surface layer and the back layer are made of non-woven materials, and it can be processed into a folded flat mask with a thickness of 0.6 mm.
[0015] The spinning precursor is made of the following components in parts by weight: 1.4 parts of polyvinylidene fluoride, 5.0 parts of dimethylformamide, and 1.5 parts of dimethyl sulfoxide.
[0016] The preparation method of the penetrating agent comprises the following steps:
[...
Embodiment 2
[0020] A sports protective mask for daily use, comprising the following steps:
[0021] Add the prepared penetrating agent to the spinning precursor, the added mass ratio accounts for 0.4%; heat and stir in a constant temperature heating magnetic stirrer for 2.5 hours, the stirring temperature is 68 ° C, after natural cooling, shake evenly and use a syringe It was sucked and placed on an electrospinning device, and spun to obtain a fiber film with a grammage of 12 g / m2. The prepared fiber membrane is used as the sandwich filter layer of the mask, the surface layer and the back layer are made of non-woven materials, and it can be processed into a folded flat mask with a thickness of 0.7 mm. The spinning precursor is made of the following components in parts by weight: 1.5 parts of polyvinylidene fluoride, 5.8 parts of dimethylformamide, and 2.0 parts of dimethyl sulfoxide.
[0022] The preparation method of the penetrating agent comprises the following steps:
[0023] Weigh 1...
Embodiment 3
[0026] A sports protective mask for daily use, comprising the following steps:
[0027] Add the prepared penetrating agent to the spinning precursor, the added mass ratio accounts for 0.5%; heat and stir in a constant temperature heating magnetic stirrer for 3 hours, the stirring temperature is 70 ° C, after natural cooling, shake evenly and use the syringe It was sucked and placed on an electrospinning device, and spun to obtain a fiber film with a grammage of 14 g / m2. The prepared fiber membrane is used as the sandwich filter layer of the mask, and the surface layer and the back layer are made of non-woven materials, which can be processed into a folded flat mask with a thickness of 0.75 mm. The spinning precursor is made of the following components in parts by weight: 1.7 parts of polyvinylidene fluoride, 6.6 parts of dimethylformamide, and 2.5 parts of dimethyl sulfoxide.
[0028] The preparation method of the penetrating agent comprises the following steps:
[0029]Weig...
PUM
Property | Measurement | Unit |
---|---|---|
Basis weight | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Basis weight | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap