A kind of highly flame-retardant art coating and its preparation

An art coating, high flame-retardant technology, applied in fire-resistant coatings, multi-color effect coatings, coatings, etc., can solve the problems of easy combustion and damage of products, and achieve strong layering, good hand feeling, and excellent scratch resistance. Effect

Active Publication Date: 2022-01-28
GUANGDONG MAYDOS BUILDING MATERIALS LTD CO
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention aims at the problem that the product is easily combusted and damaged, and provides a kind of flame-retardant environment-friendly art paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of highly flame-retardant art coating and its preparation
  • A kind of highly flame-retardant art coating and its preparation
  • A kind of highly flame-retardant art coating and its preparation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 4

[0050] The pearlescent effect material of embodiment 4 is colorful art resin, and concrete preparation method is as follows:

[0051] The preparation method of colorful artistic resin of the embodiment of the present invention is as follows:

[0052] Step 1: Take 25 parts by weight of hydroxyacrylate and 25 parts by weight of aminoacrylate in 30 parts by weight of water, add 5 parts by weight of 1-100nm mica powder, and shake to form a uniform mixed solution;

[0053] Step 2: Take the mixed solution for coating and curing, and dry at 150°C for 4 hours to form a coating;

[0054] Step 3: crushing, grinding, and sieving the coating to obtain resin particles of 300-400 mesh;

[0055] Step 4: Soak the resin particles in 50 parts by weight of water, add 10 parts by weight of pigment and 100 parts by weight of hydroxyacrylate and shake and mix well; the pigment is mixed with titanium dioxide and fluorescent green powder in a weight ratio of 1:0.5 .

[0056] Step 5: Take the mixed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a high flame-retardant art paint, which is composed of the following raw materials in parts by weight: 10-50 parts by weight of acrylic acid copolymer; 0.1-5 parts by weight of rheological additive; 0.1-0.6 parts by weight of dispersant; ‑0.6 parts by weight; 2‑10 parts by weight of film-forming aids; 1‑5 parts by weight of antifreeze; 0.1‑0.5 parts by weight of defoamers; 0.1‑0.3 parts by weight of preservatives; PH regulator 0.1-0.8 parts by weight; water 1-40 parts by weight; filler 10-30 parts by weight; pearlescent effect of 10-20 parts by weight; 100-150 parts of oxygen compound monomer, 2-5 parts of starter, 5-20 parts of flame retardant catalyst; the halogen-containing epoxy compound monomer is selected from 4,4,4-trichloro-1,2-ring One or more of oxybutane, 4,4,4,-tribromo-1,2-epoxybutane or epichlorohydrin; the flame retardant catalyst is selected from phosphorus oxychloride, dioxypentoxide One or more of antimony and tetrakis hydroxymethyl phosphorus chloride; the initiator is selected from propylene glycol. The invention has excellent scratch resistance, high hardness, good hand feeling and strong layering.

Description

technical field [0001] The invention relates to the field of art paints, in particular to a pearlescent art paint, which belongs to the field of deployment and construction application of architectural art decoration materials. Background technique [0002] With the continuous increase of the public's individual requirements for the color and effect of interior wall decoration materials, the white and simple color matching of traditional latex paints have been difficult to meet the individualized decoration needs of consumers. Therefore, pearlescent art paints emerged as the times require, which can be customized and have the decorative effect of wallpaper, becoming the most popular category of art paints. Pearlescent art paints can be selected according to different types, different colors, and different particle sizes. , Different dosages of pearlescent powders present colorful, novel and luxurious decorative effects. However, it is damaged due to the flammability of comm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/14C09D5/18C09D5/36C09D5/29C09D7/61
CPCC09D133/14C09D5/18C09D5/36C09D5/29C09D7/61C08L2205/035C08L2205/025C08L2201/02C08K2201/014C08L33/14C08K3/34
Inventor 周伟建符传杰张旭黄理荣罗俊君
Owner GUANGDONG MAYDOS BUILDING MATERIALS LTD CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap