A method for producing 3-8mm ultra-thin specifications and x70 pipeline steel plates used under ultra-low temperature conditions by a coiling furnace

An ultra-low temperature, steel plate technology, applied in the manufacturing field of X70 pipeline steel, can solve the problems of easy to produce center segregation, high Mn content, difficult to predict products, etc. Internal tissue uniform effect

Active Publication Date: 2022-05-06
JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the existing pipeline steel research mainly focuses on the research and development of thick-gauge pipeline steel for main lines, and rarely involves research on thin-gauge pipeline steel, especially 10mm and below ultra-thin gauge steel. On the one hand, it is due to the difficulty of producing thin-gauge pipeline steel (Difficulty in plate type control) is extremely high. On the other hand, the low-temperature performance of ultra-thin steel plates is difficult to guarantee, but thin-gauge pipeline steel is just an important material for the construction of urban pipeline networks. For such ultra-thin-gauge and ultra-low temperature pipelines At present, steel still relies on coiling furnaces for production, and has extremely high requirements for blanks, coil rolling, controlled rolling and controlled cooling
[0003] At present, some thin-gauge pipeline steel plates are also produced by the process of low-carbon composition + coil rolling, but it is difficult to guarantee the performance requirements of ultra-low temperature. The main reasons are 1), non-acid-resistant thin-gauge low-carbon type pipeline steel plates generally have high Mn content , easy to produce central segregation; 2), based on cost considerations, acid-resistant pipeline steel does not have high requirements for the control of P and S content in ironmaking-steelmaking-continuous casting, and it is easy to produce central segregation and banded structure; the above production conditions It will greatly affect the internal structure and ultra-low temperature performance of ultra-thin pipeline steel plates
For example, the patent document of patent announcement number CN102230143A discloses a high-strength toughness pipeline steel and its production process based on the production of the steel-steel rolling mill. The various properties can meet the standard requirements, but the standard impact toughness requirement is only -27 ° C impact energy ≥ 40J and 0 ℃ drop hammer shear area ≥ 85%, can not meet the use requirements under the ultra-low temperature environment; as disclosed in the patent announcement number CN103599928A and CN102266866A, a production method for rolling special pipeline steel in a steckel mill and a single-stand furnace The production process of the hot-rolled pipeline steel of the coil rolling mill, neither of these two patents involves elemental composition, the coil rolling + controlled rolling and controlled cooling process does not match the elemental composition, and it is difficult to predict whether the product can meet the requirements of ultra-low temperature conditions in terms of impact toughness and drop weight. service requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for producing 3-8mm ultra-thin specifications and x70 pipeline steel plates used under ultra-low temperature conditions by a coiling furnace
  • A method for producing 3-8mm ultra-thin specifications and x70 pipeline steel plates used under ultra-low temperature conditions by a coiling furnace
  • A method for producing 3-8mm ultra-thin specifications and x70 pipeline steel plates used under ultra-low temperature conditions by a coiling furnace

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-2

[0036] Embodiment 1-2:

[0037] According to the scope of chemical composition and manufacturing method of the present invention, pretreatment of molten iron by KR—BOF smelting—LF refining—RH vacuum degassing—continuous casting of 150mm thick continuous casting slab—continuous casting slab with cover and slow cooling—continuous casting slab inspection and cleaning— Billet heating—high pressure water descaling—rolling—ACC cooling—straightening—steel plate shearing—inspection and warehousing process steps to manufacture 3-8mm ultra-thin specifications and X70M pipeline steel plates used under ultra-low temperature conditions.

[0038] The concrete process of above-mentioned heating, rolling, cooling is: the 150mm thick continuous casting slab is heated to 1200 ℃, soaking section insulation 35min (embodiment 1) or 150mm thickness continuous casting slab is heated to 1200 ℃, soaking section insulation 45min ( Embodiment 2), use high-pressure water descaling after the continuous ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for producing 3-8mm ultra-thin X70 pipeline steel plates used under ultra-low temperature conditions by a coiling furnace. The process flow: KR molten iron pretreatment—BOF smelting—LF refining—RH vacuum degassing—150mm thickness continuous casting slab continuous casting— Slow cooling of continuous casting slab with cover - continuous casting slab inspection and cleaning - casting slab heating - high pressure water descaling - rolling - ACC cooling - straightening - steel plate shearing - inspection and storage process steps, manufacturing 3‑8mm ultra-thin specifications and X70M pipeline steel plate used under ultra-low temperature conditions. The yield strength of the steel plate is 500-630MPa, the tensile strength is 580-750MPa, the elongation is ≥30%, and the yield ratio Rt 0.5 / Rm≤0.90, the product can meet the use requirements of X70M grade pipeline steel under the ultra-low temperature condition of -80°C Charpy impact energy ≥100J and -50°C drop hammer shear area ≥95%.

Description

technical field [0001] The invention relates to a manufacturing method of X70 pipeline steel, in particular to a manufacturing method of the steel plate with an ultra-thin specification of 3-8 mm and under ultra-low temperature conditions. Background technique [0002] Changes in the relationship between energy supply and supply will lead to the construction of new oil and gas pipeline projects, leading to an increase in the market demand for pipeline steel, and at the same time, the requirements for its comprehensive performance are also getting higher and higher. In order to meet the needs of long-distance transportation and storage, a large number of pipeline steels of different steel grades and specifications are required, especially for pipelines in alpine regions, urban pipeline networks, gas compressor stations, gas transmission and distribution stations, storage depots and other facilities. Pipeline steel that meets the requirements of ultra-low temperature service, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C21D8/02C22C38/02C22C38/06C22C38/20C22C38/22C22C38/24C22C38/26C22C38/28C22C38/38C22C38/42C22C38/44C22C38/46C22C38/48C22C38/50C22C38/58
CPCC22C38/38C22C38/02C22C38/06C22C38/26C22C38/24C22C38/20C22C38/22C22C38/28C22C38/42C22C38/48C22C38/46C22C38/44C22C38/58C22C38/50C21D8/0205C21D8/0247C21D8/0226
Inventor 石艾来许晓红白云苗丕峰林涛孙宪进诸建阳
Owner JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products