Preparation method of AF coated glass with antibacterial effect

A coating glass, antibacterial technology, applied in the direction of coating, can solve the problems of increasing, breeding bacteria, affecting people's health, etc., to achieve the effect of improving adhesion, slowing shedding, and enhancing anti-fingerprint effect

Active Publication Date: 2021-03-09
江苏中新瑞光学材料有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

AF coated glass is coated with a layer of chemical materials on the outer surface of the glass to reduce the surface tension of the glass, so that the glass has strong hydrophobicity, oil resistance and fingerprint resistance. Bacteria will grow on the surface, which will affect people's health. At present, the demand for AF coated glass with antibacterial effect is gradually increasing in all walks of life.
For bacteria problems such as touch screens, the common method is to use alcohol and ultraviolet light for disinfection and sterilization, but both alcohol and ultraviolet disinfection have certain limitations, and corresponding alcohol materials or ultraviolet equipment are required

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A preparation method of AF coated glass with antibacterial effect, comprising the steps of:

[0020] S1. Ultrasonic cleaning of the glass substrate with a weak alkaline solvent or cleaning agent, and then rinse with deionized water for 3 times, and dry the glass substrate with nitrogen. The weak alkaline solvent or cleaning agent helps to remove the glass substrate Oil, moisture and other stains on the surface;

[0021] S2. Place the treated glass substrate on a coating machine, and coat a layer of SiO on the glass substrate by vacuum coating. 2 Film base layer, SiO 2 The thickness of the film base layer is controlled to be about 15nm;

[0022] S3, adding nano-silver to the anti-fingerprint agent, spraying the treated anti-fingerprint agent evenly onto the SiO on the surface of the glass substrate by a spraying machine 2 on the base layer of the film, and then put the sprayed glass substrate in an oven for drying. The temperature of the oven is 120°C, and the drying ...

Embodiment 2

[0025] A preparation method of AF coated glass with antibacterial effect, comprising the steps of:

[0026] S1. Ultrasonic cleaning of the glass substrate with a weak alkaline solvent or cleaning agent, and then rinse with deionized water for 3 times, and dry the glass substrate with nitrogen. The weak alkaline solvent or cleaning agent helps to remove the glass substrate Oil, moisture and other stains on the surface;

[0027] S2. Place the treated glass substrate on a coating machine, and coat a layer of SiO on the glass substrate by vacuum coating. 2 Film base layer, SiO 2 The thickness of the film base layer is controlled to be about 20nm;

[0028] S3, adding nano-silver to the anti-fingerprint agent, spraying the treated anti-fingerprint agent evenly onto the SiO on the surface of the glass substrate by a spraying machine 2 on the base layer of the film, and then put the sprayed glass substrate in an oven for drying. The temperature of the oven is 120°C, and the drying ...

Embodiment 3

[0031] A preparation method of AF coated glass with antibacterial effect, comprising the steps of:

[0032] S1. Ultrasonic cleaning of the glass substrate with a weak alkaline solvent or cleaning agent, and then rinse with deionized water for 3 times, and dry the glass substrate with nitrogen. The weak alkaline solvent or cleaning agent helps to remove the glass substrate Oil, moisture and other stains on the surface;

[0033] S2. Place the treated glass substrate on a coating machine, and coat a layer of SiO on the glass substrate by vacuum coating. 2 Film base layer, SiO 2 The thickness of the film base layer is controlled to be about 20nm;

[0034] S3, adding nano-silver to the anti-fingerprint agent, spraying the treated anti-fingerprint agent evenly onto the SiO on the surface of the glass substrate by a spraying machine 2 on the base layer of the film, and then put the sprayed glass substrate in an oven for drying. The temperature of the oven is 120°C, and the drying ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of AF coated glass with an antibacterial effect. The preparation method comprises the following steps: S1, carrying out ultrasonic cleaning on a glass substrate by using a solvent or a cleaning agent, washing with deionized water, and blow-drying with nitrogen; S2, coating a SiO2 film base layer on the glass substrate in a vacuum coating manner; S3, adding nano-silver into an anti-fingerprint agent, uniformly spraying the treated anti-fingerprint agent onto the SiO2 film base layer on the surface of the glass substrate through a spraying machine, then drying the glass substrate, taking out the glass substrate, and cooling so as to form an antibacterial anti-fingerprint layer; and S4, dispersing SiO2 particles and nano-silver in a solvent to prepare an antibacterial solution, uniformly spraying the antibacterial solution on the antibacterial anti-fingerprint layer of the glass substrate through a spraying machine, drying the glass substrate, taking out the glass substrate, and cooling the glass substrate to form an antibacterial SiO2 film layer. The coated glass provided by the invention has anti-fingerprint and antibacterial effects.

Description

technical field [0001] The invention belongs to the technical field of glass coating, and in particular relates to a preparation method of AF coated glass with antibacterial effect. Background technique [0002] With the continuous development of social economy and the continuous improvement of human living standards, glass has developed from a single lighting, perspective and shelter from wind and rain to multifunctional glass products with various special purposes. AF coated glass is coated with a layer of chemical materials on the outer surface of the glass to reduce the surface tension of the glass, so that the glass has strong hydrophobicity, oil resistance and fingerprint resistance. Bacteria will grow on the surface, which will affect people's health. At present, the demand for AF coated glass with antibacterial effect is gradually increasing in all walks of life. For bacteria problems such as touch screens, the common method is to use alcohol and ultraviolet to disi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C17/34
CPCC03C17/3411C03C17/008C03C17/006C03C2217/40C03C2217/70C03C2218/112C03C2218/151
Inventor 陈珂珩
Owner 江苏中新瑞光学材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com