Novel inorganic environment-friendly bone slurry modeling paint and preparation method thereof

An inorganic and environmentally friendly technology, applied in the direction of coating, etc., can solve the problems of unsmooth spraying, easy cracking of too thick spraying, high production cost, etc., and achieve the improvement of viscosity and thixotropy, excellent heat storage stability, and increased stability Effect

Active Publication Date: 2021-03-16
深圳广田高科新材料有限公司
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. Too thick spraying is easy to crack, which will bring certain harm to the beauty and waterproof of the wall in the later stage;
[0004] 2. The content of mineral powder is high, reaching 60% of the powder, resulting in serious mining of mineral resources and damage to the ecological environment;
[0005] 3. The cost of raw materials is too high, resulting in high production costs and a waste of money;
[0006] 4. The spraying shape is easy to hang or the gun is not smooth, resulting in too many bumps in the effect, and the overall spraying effect is not ideal;
[0007] 5. Conventional bone pulp modeling paints release a large amount of VOC, causing pollution to the environment and seriously affecting people's physical and mental health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel inorganic environment-friendly bone slurry modeling paint and preparation method thereof
  • Novel inorganic environment-friendly bone slurry modeling paint and preparation method thereof
  • Novel inorganic environment-friendly bone slurry modeling paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The present embodiment provides a method for making a novel inorganic environment-friendly bone paste modeling paint, and the steps are as follows:

[0034] Step 1: Add 150kg of deionized water to the pre-dissolving tank, start stirring, then slowly add 1kg of hydroxyethyl cellulose of Cruzolone 250HBR under stirring, and then disperse at 600 rpm for 10 minutes, then at 600 rpm Add 5kg of LOPON827 dispersion stabilizer in the state of / min. Disperse for 5 minutes until the cellulose has no particles, no agglomeration, and a transparent gel. After completion, it will be used in step 2.

[0035] Step 2: Add 180kg of RS-837-1 organic-inorganic composite emulsion to the production tank under the stirring state of 600 rpm, and disperse for 5 minutes to a uniform state. After completion, it will be used in step 3.

[0036] Step 3: Adjust the speed of the disperser to 500 rpm in the completed step 2, slowly add 100kg of 60# ~ 120# aeolian sand in this state, adjust the spee...

Embodiment 2

[0039] Step 1: Add 200kg of deionized water to the pre-dissolving tank, start stirring, then slowly add 2kg of hydroxyethyl cellulose of Cruzolone 250HBR under stirring, and then disperse at 600 rpm for 10 minutes, then at 600 rpm 4kg of LOPON827 dispersion stabilizer was added in the state of / min. Disperse for 5 minutes until the cellulose has no particles, no agglomeration, and a transparent gel. After completion, it will be used in step 2.

[0040] Step 2: Add 150kg of RS-837-1 organic-inorganic composite emulsion to the production tank under the stirring state of 600 rpm, and disperse for 5 minutes to a uniform state. After completion, it will be used in step 3.

[0041]Step 3: Adjust the speed of the disperser to 500 rpm in the completed step 2, slowly add 150kg of 60#~120# aeolian sand in this state, and adjust the speed to 800 rpm after the addition is completed. Disperse for 15min to uniform state. Then add 491kg of 80#~120# soil bleaching quicksand. The speed is...

Embodiment 3

[0044] Step 1: Add 250kg of deionized water into the pre-dissolving tank, start stirring, then slowly add 3kg of hydroxyethyl cellulose of Cruzolone 250HBR under stirring, and then disperse at 600 rpm for 10 minutes, and then at 600 rpm 3kg of LOPON827 dispersion stabilizer was added in the state of / min. Disperse for 5 minutes until the cellulose has no particles, no agglomeration, and a transparent gel. After completion, it will be used in step 2.

[0045] Step 2: Add 120kg of RS-837-1 organic-inorganic composite emulsion to the production tank under the stirring state of 600 rpm, and disperse for 5 minutes to a uniform state. After completion, it will be used in step 3.

[0046] Step 3: Adjust the speed of the dispersing machine to 500 rpm in the completed step 2, slowly add 200kg of 60#~120# aeolian sand in this state, and adjust the speed to 800 rpm after the addition is completed. uniform state. Then add 423kg of 80#~120# soil bleaching quicksand. The speed is adjus...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a novel inorganic environment-friendly bone slurry modeling paint. The novel inorganic environment-friendly bone slurry modeling paint is prepared by mixing and blending the following components in parts by weight: 150-250 parts of water, 120-180 parts of organic-inorganic composite emulsion, 1-3 parts of hydroxyethyl cellulose, 3-5 parts of a dispersion stabilizer, 1-3 parts of a thickener, 100-200 parts of aeolian sand and 423-562 parts of soil whitening quicksand. The modeling paint has the characteristics of low cost, environmental friendliness, good spraying effectand ecological resource saving.

Description

technical field [0001] The invention relates to the technical field of architectural decoration functional coatings, in particular to a novel inorganic environment-friendly bone paste modeling paint and a preparation method thereof. Background technique [0002] In the interior and exterior wall decoration materials of modern buildings, the artistic effect texture paint is more and more popular among the general public, and the bone pulp modeling has become the mainstream product of the decorative effect, but the bone pulp modeling paint sold in the market has the following shortcomings: [0003] 1. Too thick spraying is easy to crack, which will cause certain harm to the beauty and waterproofing of the wall in the later stage; [0004] 2. The content of mineral powder is high, reaching 60% of the powder, which causes serious mining of mineral resources and damage to the ecological environment; [0005] 3. The cost of raw materials is too high, resulting in high production ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/61C09D7/65
CPCC09D1/00C09D7/61C09D7/65
Inventor 谷二宁胡基如蒋瑞霞刘述敏徐新祥付超
Owner 深圳广田高科新材料有限公司