Aramid tying belt for aerospace and preparation method thereof

An aerospace and aramid technology, which is applied in the field of aramid tie for aerospace and its preparation, and can solve problems such as the performance limitation of aramid tie

Inactive Publication Date: 2021-04-06
WUHU HANGTIAN SPECIAL CABLE FACTORY
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the problem that the performance of the aramid lace in the prior art has certain limitations when used in the aerospace field, thereby providing a Aerospace aramid lace with better mechanical properties and better adaptability to harsh environments and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aramid tying belt for aerospace and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] Specific embodiments of the present invention will be described in detail below. It should be understood that the specific embodiments described here are only used to illustrate and explain the present invention, and are not intended to limit the present invention.

[0029] Such as figure 1 As shown, the invention provides a kind of preparation method of aramid fiber tie for aerospace, and described preparation method comprises:

[0030] 1) Preparation of warp: by grafting polar oxygen-containing groups on the surface of the meta-aramid fiber, the modified meta-aramid fiber is obtained, and the obtained modified meta-aramid fiber is sequentially opened and carded. , drawing, roving, spun yarn and shaping process to get the warp;

[0031] 2) Preparation of the weft: After blending the para-aramid fiber and carbon fiber, the weft is obtained after the processes of opening, carding, drawing, roving, spun yarn and setting in sequence;

[0032] 3) After the obtained warp ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses an aramid tying belt for aerospace and a preparation method thereof. The preparation method includes the steps of (1) warp preparation: grafting polar oxygen-containing groups on the surfaces of meta-aramid fibers to obtain modified meta-aramid fibers, and performing cotton opening, cotton carding, drawing, roving, spinning and shaping on the obtained modified meta-aramid fibers in sequence to obtain warps; (2) weft preparation: blending para-aramid fibers and carbon fibers, and sequentially carrying out cotton opening, cotton carding, drawing, roving, spinning and shaping processes to obtain wefts; and (3) respectively stranding and shaping the obtained warps and wefts, weaving and shaping, and carrying out after-treatment to obtain the aramid tying belt for aerospace. The aramid tying belt for aerospace has excellent flame retardancy and better mechanical properties, and can better adapt to the use requirements in severe environments.

Description

technical field [0001] The invention relates to the field of aramid lace materials, in particular to an aramid lace for aerospace and a preparation method thereof. Background technique [0002] Aramid is a high-temperature-resistant, high-strength, high-modulus fiber with good electrical insulation and chemical stability. Therefore, with the continuous advancement of technology, it is also used in more and more fields. [0003] For example, there is a precedent for using aramid fiber to make parachutes in the prior art. It can adapt to harsh environments, and its quality is reduced by 50% compared with ordinary materials. Broad prospects. [0004] With the continuous increase of its use in aerospace, higher requirements are put forward for its mechanical properties and physical and chemical properties. Contents of the invention [0005] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the problem that the performance of the ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/283D03D15/275D03D15/47D06M13/08D06M13/11D06M11/17D06M11/38D06M101/36
CPCD03D15/00D06M11/17D06M11/38D06M13/08D06M13/11D06M2101/36D10B2331/021
Inventor 龚世余周太平谢飞黄群芳陈工明
Owner WUHU HANGTIAN SPECIAL CABLE FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap