A kind of anti-cracking calcium silicate board and its preparation process

A calcium silicate board and a preparation process technology, applied in the field of calcium silicate board, can solve the problems of human health hazards, affecting the performance of calcium silicate board, causing cancer, etc., and achieve the effect of being friendly to the human body and the environment

Active Publication Date: 2022-03-25
广东雄塑环保板业有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional calcium silicate board production raw materials contain asbestos fibers, which are easy to cause harm to human health and cause cancer. The performance of calcium acid board

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-cracking calcium silicate board and its preparation process
  • A kind of anti-cracking calcium silicate board and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An anti-cracking calcium silicate board made of raw materials of the following quality: 35kg of alkali slag, 6kg of slaked lime, 14kg of cement, 22kg of quartz powder, 1.5kg of yttria-stabilized zirconia, 0.5kg of sodium polyacrylate, and β-eucryptite Glass fiber 4kg, pulp 6kg, anhydrous sodium sulfate 2kg.

[0024] The β-eucryptite glass fiber is made of the following raw materials in parts by weight: 9 parts of β-eucryptite, 37 parts of quartz sand, 18 parts of kaolin, 2 parts of soda ash, 2 parts of calcium oxide, and 1 part of magnesium oxide. The method is: take β-eucryptite, quartz sand, kaolin, soda ash, calcium oxide, and magnesium oxide and mix them into a high-temperature kiln for melting at 1200°C to obtain molten glass, then cool the molten glass to 850°C and then draw wire to form a Glass fiber filaments of 6-12mm are soaked in acetone and hydrochloric acid solutions, washed and dried.

[0025] A preparation process for the anti-cracking calcium silicate b...

Embodiment 2

[0030] An anti-cracking calcium silicate board made of raw materials of the following quality: 30kg of alkali slag, 4kg of slaked lime, 12kg of cement, 20kg of quartz powder, 1kg of yttria-stabilized zirconia, 0.3kg of sodium polyacrylate, and β-eucryptite glass Fiber 3kg, pulp 5kg, anhydrous sodium sulfate 1kg.

[0031] The β-eucryptite glass fiber is made of the following raw materials in parts by weight: 8 parts of β-eucryptite, 35 parts of quartz sand, 15 parts of kaolin, 2 parts of soda ash, 1 part of calcium oxide, and 1 part of magnesium oxide. The method is: take β-eucryptite, quartz sand, kaolin, soda ash, calcium oxide, and magnesium oxide and mix them into a high-temperature kiln for melting at 1100°C to obtain molten glass, then cool the molten glass to 800°C and then draw wire to form a Glass fiber filaments of 6-12mm are soaked in acetone and hydrochloric acid solutions, washed and dried.

[0032] A preparation process for the anti-cracking calcium silicate boar...

Embodiment 3

[0037] An anti-cracking calcium silicate board made of raw materials of the following quality: 40kg of alkali slag, 8kg of slaked lime, 16kg of cement, 24kg of quartz powder, 2kg of yttria-stabilized zirconia, 0.7kg of sodium polyacrylate, and β-eucryptite glass Fiber 6kg, pulp 7kg, anhydrous sodium sulfate 3kg.

[0038] The β-eucryptite glass fiber is made of the following raw materials in parts by weight: 10 parts of β-eucryptite, 40 parts of quartz sand, 20 parts of kaolin, 3 parts of soda ash, 2 parts of calcium oxide, and 2 parts of magnesium oxide. The method is: take β-eucryptite, quartz sand, kaolin, soda ash, calcium oxide, and magnesium oxide and mix them into a high-temperature kiln for melting at 1300°C to obtain molten glass, then cool the molten glass to 900°C and then draw wire to form a Glass fiber filaments of 6-12mm are soaked in acetone and hydrochloric acid solutions, washed and dried.

[0039] A preparation process for the anti-cracking calcium silicate b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-cracking calcium silicate board and a preparation process thereof, which is prepared from the following raw materials in parts by weight: 30-40 parts of alkali slag, 4-8 parts of slaked lime, 12-16 parts of cement, and 20-24 parts of quartz powder , 1-2 parts of yttria-stabilized zirconia, 0.3-0.7 parts of sodium polyacrylate, 3-6 parts of β-eucryptite glass fiber, 5-7 parts of pulp, and 1-3 parts of anhydrous sodium sulfate. The calcium silicate board of the present invention uses β-eucryptite glass fiber and pulp fiber to replace the traditional asbestos fiber on the fiber raw material, which is non-toxic, more friendly to the human body and the environment, and can well prevent the crack from expanding and change the expansion. direction, increase the expansion path, and achieve the anti-cracking effect of the calcium silicate board.

Description

technical field [0001] The invention belongs to the technical field of calcium silicate boards, and in particular relates to an anti-cracking calcium silicate board and a preparation process thereof. Background technique [0002] Calcium silicate board is a new type of inorganic building decoration material. Because of its high strength, light weight, good processability and non-combustibility, it is widely used in ship bulkheads, suspended ceilings and non-load-bearing buildings. Walls, and other places with fire protection requirements. As a new green and environmentally friendly building material, in addition to the functions of traditional gypsum boards, it also has the advantages of superior fire resistance, moisture resistance, and long service life. It is widely used in suspended ceilings and partition walls of industrial and commercial engineering buildings, home decoration, and furniture linings. , billboard lining board, ship partition board, warehouse shed board,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/20C04B14/42C03C13/00C03C6/04C04B111/20C04B111/34C04B14/30C04B18/24
CPCY02W30/91
Inventor 黄淦雄
Owner 广东雄塑环保板业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap