Preparation method of titanium alloy dental implant surface composite coating

A dental implant and surface composite technology, which is applied in coatings, prostheses, medical science, etc., can solve the problems of being unable to clean up impurities on the surface of titanium alloy dental implants, unable to dry and dry, and not having the function of immersion and rinsing. , to improve long-term stability and service performance, improve implant effect, and improve osseointegration performance
CN112843331AInactive Publication Date: 2021-05-28SHANDONG MAIER DENTAL MATERIALS CO LTD
7 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
SHANDONG MAIER DENTAL MATERIALS CO LTD
Publication Date
2021-05-28
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention provides a preparation method of a titanium alloy dental implant surface composite coating, and belongs to the field of surface modification of oral titanium alloy dental implants. The preparation method of the titanium alloy dental implant surface composite coating comprises the specific steps of titanium alloy dental implant preparation, titanium alloy dental implant cleaning treatment, titanium alloy dental implant blow-drying and airing treatment, storage treatment after a composite coating is generated on the surface of the titanium alloy dental implant, titanium alloy dental implant implanting and using, and titanium alloy dental implant subsequent detection. The method is mature in process and simple to operate, the process of cleaning the surface of the titanium alloy dental implant for many times is added to ensure the cleanliness of the surface of the titanium alloy dental implant and further ensure the adhesiveness of the coating, meanwhile, the use effect of the titanium alloy dental implant is ensured through the clear transportation and use process, unnecessary damage can be avoided, the utilization rate of the titanium alloy dental implant is guaranteed, the implanting effect is improved, and the implanting rate is guaranteed.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention belongs to the technical field of surface modification of oral titanium alloy dental implants, and in particular relates to a method for preparing a composite coating on the surface of titanium alloy dental implants. Background technique

[0002] Modern oral implant technology originated in the 1930s. In the mid-1950s, Professors Branemark and Albrektsson of the University of Gothenburg in Sweden used high-purity titanium as the implant material in the study of microvascular blood flow in the bone marrow cavity. Long-term observations have been made on titanium materials that have been injected into animals, and it is found that pure titanium has good biocompatibility with the body, and pure titanium has an unusually strong bond with the tibia of rabbits. Professor Branemark proposed the concept of osseointegration, which refers to a direct and firm combination between the load-bearing implant and the living bone tissue. The theory of os...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More