Matt repairable BMC material and preparation method thereof

A repairing method and a technology of repairing materials, which are applied in the field of sanitary ware, can solve the problems of molded sanitary ware products such as irreparability and lower product qualification rate, and achieve the effect of high strength, uniform particle distribution, and elegant shape

Inactive Publication Date: 2021-06-04
华南涌
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to provide a matte repairable BMC material and its preparation method, which solves the problem of the reduction of the final pass rate of the product due to the irreparable or polished surface of the molded sanitary ware product in the prior art. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The invention provides a matte repairable BMC material and a preparation method thereof, which comprises the following ingredients in weight percent raw materials: 15% to 25% of unsaturated polyester resin, 5% to 10% of additives, 50% to 60% of fillers, Glass fiber 10%~20%, initiator 1%~2%, internal release agent 1%~2%, thickener 1%~2%, colorant 0.5%~1%, dispersant 1%~2% .

[0032] Further improved raw materials comprising the weight percent of the following components: 25% unsaturated polyester resin, 10% additive, 60% filler, 20% glass fiber, 2% initiator, 2% internal mold release agent, 2 thickeners %, colorant 1%, dispersant 2%.

[0033] As a further improvement, the additive is one of low-shrinkage additives or low-profile additives, and the filler is a mineral filler.

[0034] As a further improvement, the glass fibers have different lengths.

[0035] Further improved, the preparation method includes the following steps:

[0036] Step 1: Weigh half of the fill...

Embodiment 2

[0057] The invention provides a matte repairable BMC material and a preparation method thereof, which comprises the following ingredients in weight percent raw materials: 15% to 25% of unsaturated polyester resin, 5% to 10% of additives, 50% to 60% of fillers, Glass fiber 10%~20%, initiator 1%~2%, internal release agent 1%~2%, thickener 1%~2%, colorant 0.5%~1%, dispersant 1%~2% .

[0058] Further improved raw materials comprising the weight percent of the following components: 20% unsaturated polyester resin, 7% additive, 55% filler, 15% glass fiber, 1.5% initiator, 1.5% internal release agent, thickener 1 %, colorant 0.5%, dispersant 1.5%.

[0059] As a further improvement, the additive is one of low-shrinkage additives or low-profile additives, and the filler is a mineral filler.

[0060] As a further improvement, the glass fibers have different lengths.

[0061] Further improved, the preparation method includes the following steps:

[0062] Step 1: Weigh half of the fil...

Embodiment 3

[0083] The invention provides a matte repairable BMC material and a preparation method thereof, which comprises the following ingredients in weight percent raw materials: 15% to 25% of unsaturated polyester resin, 5% to 10% of additives, 50% to 60% of fillers, Glass fiber 10%~20%, initiator 1%~2%, internal release agent 1%~2%, thickener 1%~2%, colorant 0.5%~1%, dispersant 1%~2% .

[0084] Further improved raw materials comprising the weight percent of the following components: 15% unsaturated polyester resin, 5% additive, 50% filler, 10% glass fiber, 1% initiator, 1% internal release agent, thickener 1 %, colorant 1%, dispersant 1%.

[0085] As a further improvement, the additive is one of low-shrinkage additives or low-profile additives, and the filler is a mineral filler.

[0086] As a further improvement, the glass fibers have different lengths.

[0087] Further improved, the preparation method includes the following steps:

[0088] Step 1: Weigh half of the fillers and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a matte repairable BMC material and a preparation method thereof. The matte repairable BMC material comprises the following raw materials in percentage by weight: 15%-25% of unsaturated polyester resin, 5%-10% of an additive, 50%-60% of filler, 10%-20% of glass fiber, 1%-2% of an initiator, 1%-2% of an internal release agent, 1%-2% of a thickening agent, 0.5%-1% of a coloring agent and 1%-2% of a dispersing agent. According to the invention, previous ingredients are re-proportioned, a new kneading technology is applied, and then high-temperature mould pressing is carried out, so that the product has specific glass fiber lines and more uniform particle distribution, and more importantly, the product has unique characteristics and is polishable and repairable, and a sanitary appliance product produced by the reformed technology is fine, smooth, clean and moist in surface, good in durability, good in durability, elegant in shape, comfortable in body feeling, high in strength and durable in service.

Description

technical field [0001] The invention relates to the technical field of sanitary ware, in particular to a matte repairable BMC material and a preparation method thereof. Background technique [0002] Existing sanitary ware, building materials and wall panels are of a great variety, such as metal products, ceramic products, glass products, and composite products. Especially in the field of composite materials, the production process includes pouring, RTM, acrylic blister and molded composite products, but because the molded sanitary ware products are not repairable or the surface is polished, the final pass rate of the product is reduced due to surface defects. It is often difficult to apply the molding technology to the production technology of civil sanitary ware products and change it to industrial intermediate products. Therefore, need provide a kind of new technical scheme and give solution. Contents of the invention [0003] The object of the present invention is to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/06C08K7/14
CPCC08K7/14C08L67/06
Inventor 华南涌
Owner 华南涌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap