Method for manufacturing transition leading tape for rolling dissimilar metal connecting structure and titanium coil

A technology for connecting structures and dissimilar metals, applied in the field of metallurgy, can solve problems such as damage to related equipment, uneven thickness of connecting parts, etc., to improve production efficiency, avoid falling off, and achieve the effect of continuity

Active Publication Date: 2021-07-09
CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
View PDF17 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention firstly provides a connection structure for difficult-to-weld dissimilar metals, which solves the problem that the existing difficult-to-weld dissimilar metals are connected, and the thickness of the connection part is not equal, which may cause damage to related equipment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing transition leading tape for rolling dissimilar metal connecting structure and titanium coil
  • Method for manufacturing transition leading tape for rolling dissimilar metal connecting structure and titanium coil
  • Method for manufacturing transition leading tape for rolling dissimilar metal connecting structure and titanium coil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] First, prepare two industrial pure titanium plates with a width of 1200 mm and a length of 100 mm, both of which are half the thickness of the titanium coil, and prepare two stainless steel plates with the same thickness and width at the same time; one end of the stainless steel plate is cut out by laser 9 trapezoidal notches, the upper bottom of the trapezoidal notches is 100mm, the lower bottom is 50mm, the notch depth is 60mm, the distance between adjacent trapezoidal notches is equal to 160mm plus the thickness of the titanium plate, and the shape of the part between adjacent trapezoidal notches is an inverted trapezoid; Do the same, i.e. make the same notches. Secondly, along the notch of the titanium plate and the stainless steel plate and the edge of the inverted trapezoid between the notches, the groove is processed by grinding, and the groove angle is 45°. Again, a press is used to press the inverted trapezoid of the titanium plate into the gap of the stainless...

Embodiment 2

[0048] First, prepare two industrial pure titanium plates with a width of 1050mm and a length of 100mm, the thickness of which is half of the titanium coil; prepare two stainless steel plates with the same thickness and width;

[0049] One end of the titanium plate is cut with 11 T-shaped notches by laser. The long side of the T-shaped notch is 60mm, the short side is 30mm, the depth of the notch is 20+20mm, and the distance between adjacent trapezoidal notches is 90mm. The shape of the part is an inverted T shape; the same treatment is carried out on the stainless steel plate, that is, the same notch is made. Secondly, along the notch of the titanium plate and the stainless steel plate and the edge of the inverted trapezoid between the notches, the groove is processed by grinding, and the groove angle is 60° and 30°; the inverted trapezoid of the stainless steel plate is moved along the groove by a press Pressed into the gap of the titanium plate, at the same time, the invert...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for manufacturing a transition leading tape for rolling a dissimilar metal connecting structure and a titanium coil, relates to the field of metallurgy, and firstly solves the problem that after existing dissimilar metal which is difficult to weld is connected, the thicknesses of connecting parts are unequal, and related equipment is possibly damaged. According to the technical scheme, the dissimilar metal connecting structure comprises at least two layers of connecting pieces arranged in a stacked mode, each layer of connecting piece comprises a first connecting plate and a second connecting plate which are mutually embedded, the at least two layers of connecting pieces are stacked to form a connecting body, the first connecting plates of every two adjacent layers of connecting pieces are connected in a welded mode, and the second connecting plates of every two adjacent layers of connecting pieces are connected in a welded mode. The first connecting plates and the second connecting plates are mechanically connected through mutual embedding of notches and protruding bodies, and the stress requirement between the two connecting plates is guaranteed. The first connecting plates are titanium plates, the second connecting plates are stainless steel plates, and the connecting body formed by stacking the connecting pieces is the transition leading tape for titanium coil rolling and can be used for titanium coil rolling production.

Description

technical field [0001] The invention relates to the field of metallurgy, in particular to a connection structure of dissimilar metals that are difficult to weld, and a transition leader used when steel plates are switched to titanium plates on a collinear production line between titanium and steel and a manufacturing method thereof. Background technique [0002] In the rolling production of titanium coils, it is a common practice to use rolling equipment to produce titanium coils, and the use of stainless steel leaders can reduce costs. After the titanium coil is connected to the stainless steel leader belt, the connecting joint needs to transmit a large tension and experience the high temperature of the annealing furnace at the same time during the intermediate annealing process. [0003] Conventional welding methods cannot be used to connect titanium coils and steel strips, because the physical and chemical properties of titanium and steel are quite different. When titani...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K26/12B23K26/21B23K33/00B23P15/00
CPCB23K33/00B23P15/00B23K26/12B23K26/123B23K26/21
Inventor 刘正林唐新新王泽龙
Owner CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap