Composite bamboo fiber cloth and preparation method thereof

A technology of composite fiber and bamboo pulp fiber, which is applied in the direction of non-woven fabrics, needle punching machines, textiles and papermaking, can solve the problems of high cost and slippery bamboo fiber, and achieve low raw material cost, good economic benefits and excellent performance Effect

Inactive Publication Date: 2021-07-30
蓝赛斯科技(大连)有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, simple bamboo fiber has the disadvantages of high cost and slippery, so based on this, the technical solution of the present invention is proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite bamboo fiber cloth and preparation method thereof
  • Composite bamboo fiber cloth and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The invention provides a kind of preparation method of composite fiber non-woven fabric, comprises the following steps:

[0027] (1) Carding 25% bamboo pulp fiber, 45% bamboo viscose fiber and 30% PP spunbonded cloth into a web and laying them up to get 20g / m 2 The first fiber mesh cloth;

[0028] (2) Pre-wet and compact the first fiber mesh cloth so that it enters the first spunlace area, so that the water jet acts on one side of the mesh cloth, and the jet boards in the first spunlace area are single-row holes, the pinhole density is 8 holes / cm, and the hole diameter is 0.08mm; the water outlet pressure of the pinholes is 5×10 3 kPa; get the second fiber mesh;

[0029] (3) Make the second fiber mesh cloth enter the second spunlace area, so that the water jet acts on the other side of the mesh cloth. The needle plate in the second spunlace area has double rows of holes, and the needle hole density is 16. hole / cm, the hole diameter is 0.08mm; the outlet pressure of t...

Embodiment 2

[0032] The invention provides a kind of preparation method of composite fiber non-woven fabric, comprises the following steps:

[0033] (1) Combing 35% bamboo pulp fiber, 35% bamboo viscose fiber and 30% PP spunbonded cloth into a web and laying them up to get 100g / m 2 The first fiber mesh cloth;

[0034] (2) Pre-wet and compact the first fiber mesh cloth so that it enters the first spunlace area, so that the water jet acts on one side of the mesh cloth, and the jet boards in the first spunlace area are single-row holes, the pinhole density is 16 holes / cm, and the hole diameter is 0.18mm; the water outlet pressure of the pinholes is 8×10 3 kPa; get the second fiber mesh;

[0035] (3) Let the second fiber mesh cloth enter the second spunlace area, so that the water jet acts on the other side of the mesh cloth. The needle plate in the second spunlace area has double rows of holes, and the needle hole density is 26. hole / cm, the hole diameter is 0.18mm; the water outlet pressu...

Embodiment 3

[0038] The invention provides a kind of preparation method of composite fiber non-woven fabric, comprises the following steps:

[0039] (1) Combing 30% bamboo pulp fiber, 45% bamboo viscose fiber and 25% PP spunbonded cloth into a web and laying them up to get 60g / m 2 The first fiber mesh cloth;

[0040] (2) Pre-wet and compact the first fiber mesh cloth so that it enters the first spunlace area, so that the water jet acts on one side of the mesh cloth, and the jet boards in the first spunlace area are single-row holes, the pinhole density is 12 holes / cm, and the hole diameter is 0.13mm; the water outlet pressure of the pinholes is 6.5×10 3 kPa; get the second fiber mesh;

[0041] (3) Let the second fiber mesh cloth enter the second spunlace area, so that the water jet acts on the other side of the mesh cloth. The needle plate in the second spunlace area has double rows of holes, and the needle hole density is 21. hole / cm, the hole diameter is 0.13mm; the outlet pressure of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to composite bamboo fiber cloth and a preparation method thereof. The composite fiber non-woven fabric comprises bamboo pulp fibers, bamboo viscose fibers and PP spunbond cloth. The preparation method comprises the following steps: carding the bamboo pulp fibers, bamboo viscose fibers and PP spunbond cloth into a net, and laying to obtain first fiber mesh cloth; pre-wetting and compacting the first fiber mesh cloth to enable the first fiber mesh cloth to enter a first spunlace area, and enabling waterflow to jet and act on one side of the mesh cloth to obtain second fiber mesh cloth; enabling the second fiber mesh cloth to enter a second spunlace area, and enabling the waterflow to jet and act on the other side of the mesh cloth to obtain third fiber mesh cloth; and dehydrating, drying and coiling the third fiber mesh cloth to obtain the composite fiber non-woven fabric. According to the composite fiber non-woven fabric, different fibers are entangled, the defect that a single bamboo fiber is slippery is overcome, after detection, the comprehensive index is superior to that of similar products sold in the market, and better performance is achieved; in addition, through compounding of various raw materials, the raw material cost can be reduced, and good economic benefits can be obtained.

Description

technical field [0001] The invention belongs to the field of weaving, and in particular relates to a composite bamboo fiber cloth and a preparation method thereof. Background technique [0002] Bamboo fiber is a cellulose fiber extracted from naturally growing bamboo. Bamboo fiber has the characteristics of good air permeability, instant water absorption, strong wear resistance and good dyeability, and has natural antibacterial, antibacterial, anti-mite, deodorant and anti-ultraviolet functions. [0003] Yet simple bamboo fiber has cost too high, the shortcoming of hair slippery, so based on this, propose technical scheme of the present invention. Contents of the invention [0004] In order to solve the problems in the prior art, the invention provides a composite bamboo fiber cloth and a preparation method thereof. The composite fiber non-woven fabric is composed of bamboo pulp fiber, bamboo viscose fiber and PP spunbonded cloth spunlace, and different fibers are entang...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More