A kind of chiral menthol-based liquid crystal oligomer film and preparation method thereof

A menthol-based and oligomer technology, applied in liquid crystal materials, chemical instruments and methods, etc., can solve the problem of inability to retain color, and achieve the effect of easy industrial production, bright colors, and wide liquid crystal interval.

Active Publication Date: 2021-11-16
XUZHOU UNIV OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the chiral menthol-based liquid crystal small molecule monomer does not retain its selective reflection color at room temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of chiral menthol-based liquid crystal oligomer film and preparation method thereof
  • A kind of chiral menthol-based liquid crystal oligomer film and preparation method thereof
  • A kind of chiral menthol-based liquid crystal oligomer film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Step 1, preparing a chiral menthyl liquid crystal monomer.

[0043] Add 0.10 mol of adipic acid to a 150 mL single-necked bottle, add 30 mL of thionyl chloride, heat up to 64°C, heat to reflux for 6 hours, and distill under reduced pressure to obtain Intermediate 1 after the reaction is complete.

[0044] Move Intermediate 1 to a 250 mL three-neck flask, add 150 mL of chloroform as a solvent, heat to reflux, slowly add 0.10 mol of menthol chloroform solution dropwise, and heat to reflux for 6 hours. After the reaction is completed, filter under reduced pressure to obtain intermediate Body 2.

[0045] Add 0.12mol of p-hydroxybenzoic acid, 200mL of tetrahydrofuran and 0.1mol of pyridine into a 500mL three-neck flask, heat to reflux, slowly add the above intermediate 2 dropwise, and heat to reflux for 6h. After the reaction, cool and filter under reduced pressure, spin the filtrate to dryness, add dichloromethane, heat to reflux for 0.5h, cool and filter. The dichloromet...

Embodiment 2

[0066] Polymethyl hydrogen-containing linear siloxane PMHS, chiral menthyl liquid crystal monomer (M 1 ), (E)-1-(4-(2-(4-(allylcyclohexyl)vinyl)cyclohexyl)-4-methoxybenzene (M 2 ) was dissolved in 50mL xylene, stirred, and 0.8mL tetrahydrofuran solution of hexachloroplatinic acid (5mg·mL -1 ), N 2 Under protection, the temperature was raised to 65°C, and the reaction was carried out for 10 hours. After the reaction, the reaction solution was cooled to room temperature, poured into a beaker filled with about 100mL of methanol, left to stand overnight to precipitate a precipitate, filtered with suction, recrystallized from the filter cake with methanol, and dried to obtain a chiral menthyl liquid crystal oligomer, see Formula VI.

[0067]

[0068] Prepare O1-O8 series of chiral mint-based liquid crystal oligomers according to the above method, and the feed ratio is shown in Table 2 below:

[0069] Table 2 Feed ratio of chiral menthol-based liquid crystal oligomers

[007...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a chiral menthyl-based liquid crystal oligomer film and a preparation method thereof, which comprises copolymerizing chiral menthyl-based liquid crystal monomers, achiral rod-shaped monomers and polymethyl hydrogen-containing linear siloxane in different molar ratios. , to prepare chiral menthyl liquid crystal oligomer, the structural formula of which is formula III, after high-temperature quenching, a chiral menthyl liquid crystal oligomer film with bright colors at room temperature is obtained. The chiral menthol-based liquid crystal oligomer film has high thermal stability, wide liquid crystal interval, can retain the color of cholesteric liquid crystal at room temperature, presents bright colors, and has wide applications.

Description

technical field [0001] The invention relates to a chiral menthol-based liquid crystal oligomer film and a preparation method thereof, belonging to the technical field of optical materials. Background technique [0002] Chiral liquid crystals can form a helical structure due to the existence of chiral centers, so that chiral liquid crystal molecules have optical properties that ordinary liquid crystal molecules do not have, such as optical rotation, selective reflection, circular dichroism, etc., in nonlinear optics, It has potential application value in fast optical transfer switch, measurement of interface temperature, medicine, photosensitive ink, anti-counterfeiting label and color-changing clothing. This kind of chiral liquid crystal has been paid more and more attention due to its unique electro-optical properties. Menthol has three chiral centers, strong optical activity, relatively small volume and steric hindrance, and is an excellent chiral mesogen. However, the c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J5/18C08L83/06C08G77/38C09K19/38
CPCC08G77/045C08G77/38C08J5/18C08J2383/06C09K19/0403C09K19/3833C09K2019/0407
Inventor 罗丛丛么冰陈艳堵锡华贾迎钢周俊董黎明丁跃孙华
Owner XUZHOU UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap