A kind of preparation method of recycled gh4169 alloy cold drawn bar

A technology of GH4169 and cold-drawn rods, which is applied in the field of preparation of recycled GH4169 alloy cold-drawn rods, can solve problems such as unsatisfactory, and achieve the effects of reducing growth, reducing adjustment time, and reducing interference

Active Publication Date: 2022-03-29
AVIC SHANGDA METAL REGENERATION TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As the customer's requirements for the strength of GH4169 alloy rods are greatly improved, the traditional hot rolling can no longer meet the strength requirements of the model standard (room temperature tensile strength ≥ 1515Mpa, room temperature yield strength ≥ 1380Mpa)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of recycled gh4169 alloy cold drawn bar
  • A kind of preparation method of recycled gh4169 alloy cold drawn bar
  • A kind of preparation method of recycled gh4169 alloy cold drawn bar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The standard parts used in the present invention can be purchased from the market, and the special-shaped parts can be customized according to the instructions and the accompanying drawings. The specific connection methods of each part adopt mature bolts, rivets, welding in the prior art , pasting and other conventional means, will not be described in detail here.

[0024] A preparation method for recycling GH4169 alloy cold-drawn rods, comprising the following steps:

[0025] A. Use the blanking machine to roll the GH4169 alloy steel billet of Φ160mm once; the heating temperature is 1090°C, and the billet is opened to a 58mm billet; the Φ160mmGH4169 alloy steel billet contains 70% recycled materials; the surface is polished after billeting deal with;

[0026] B. Use the blanking machine to carry out secondary rolling and blanking of the steel billet processed in step A; the heating temperature is 1010°C, the rolling deformation is 75%, water cooling within 1 minute af...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for recycling GH4169 alloy cold-drawn rods, which comprises the following steps: A. using a billet cutting machine to perform rolling and billeting of a Φ160mm GH4169 alloy steel rolling billet; B. using a billet cutting machine to The steel slab treated in step A is subjected to secondary rolling; C, solution annealing; D, surface polishing treatment after solution; E, cold drawing. The invention can improve the deficiencies of the prior art and improve the strength performance of the material.

Description

technical field [0001] The invention relates to the technical field of alloy material preparation, in particular to a preparation method for recycling GH4169 alloy cold-drawn rods. Background technique [0002] GH4169 alloy is a nickel-based deformed superalloy, which is widely used in the core components of engines such as aero-engine turbine disks, turbine shafts, and fasteners. As the customer's requirements for the strength of GH4169 alloy rods are greatly improved, the traditional hot rolling can no longer meet the strength requirements of the model standard (room temperature tensile strength ≥ 1515Mpa, room temperature yield strength ≥ 1380Mpa). Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a preparation method for recycling GH4169 alloy cold-drawn rods, which improves the strength performance of the material. [0004] In order to solve the above technical problems, the technical solutions adopted by the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21C37/04C22F1/10C21D8/06
CPCB21C37/04C22F1/10C21D8/06
Inventor 刘猛栾吉哲李爱民田水仙张震管庆阳
Owner AVIC SHANGDA METAL REGENERATION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap