Waterproof stone-like coating and preparation method thereof

A technology of real stone paint and processing method, applied in the field of building decoration materials, can solve the problems of affecting the decorative effect of real stone paint, affecting the effect of building use, affecting the quality of the project, etc., so as to enhance the water resistance and anti-contamination ability, and achieve the effect of imitating stone. The best effect of improving compatibility

Inactive Publication Date: 2021-10-29
安徽朗凯奇科技股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, at present, in the actual construction of real stone paint for exterior walls of construction projects, due to the influence of various uncertain factors and changes in the external environment, there are many problems in the application of real stone paint for exterior walls, such as: blooming phenomenon will occur after soaking in rainwater, Major quality problems such as large color difference, yellowing when exposed to water, and shedding of bulges. The existence of these problems not only affects the actual decorative effect of real stone paint, but also affects the quality of the entire project and the use effect of buildings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof stone-like coating and preparation method thereof
  • Waterproof stone-like coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0027] In the present embodiment, by weight, the specific formula is:

[0028] Waterborne epoxy resin 15 copies water-based curing agent 3 copies Graphene 5 copies aggregate 80 copies Organic modified bentonite 15 copies Hydroxyethyl cellulose 10 copies Modified siloxane 0.5 parts Wetting and dispersing agent 0.5 parts Coalescent 1 copy Defoamer 0.5 parts thickener 0.5 parts antifungal agent 0.5 parts pH regulator 0.5 parts water Appropriate amount

[0029] Among them, the aggregate is a mixture of natural colored sand and quartz sand, the weight ratio of natural colored sand and quartz sand is 1:1, and the particle size of natural colored sand is 40 mesh, and the particle size of quartz sand is 80 mesh; It is a polycarboxylic acid-alkyl ammonium salt; the film-forming aid is ethylene glycol; the defoamer is selected from organosilicon modified defoamers; the thickener is ...

specific Embodiment 2

[0037] In the present embodiment, by weight, the specific formula is:

[0038] Waterborne epoxy resin 35 copies water-based curing agent 15 copies Graphene 18 copies aggregate 120 copies Organic modified bentonite 20 copies Hydroxyethyl cellulose 25 copies Modified siloxane 2 copies Wetting and dispersing agent 1.5 servings Coalescent 4 parts Defoamer 0.8 parts thickener 1.2 parts antifungal agent 1.5 servings pH regulator 3 copies water Appropriate amount

[0039] Among them, the aggregate is a mixture of natural colored sand and quartz sand, the weight ratio of natural colored sand and quartz sand is 3:2, and the particle size of natural colored sand is 80 mesh, and the particle size of quartz sand is 120 mesh; It is an unsaturated fatty acid polyamine amide; the film-forming aid is lauryl alcohol ester film-forming aid; the defoamer is selected from mineral oil modified...

specific Embodiment 3

[0047] In the present embodiment, by weight, the specific formula is:

[0048] Waterborne epoxy resin 25 copies water-based curing agent 10 copies Graphene 12 copies aggregate 100 copies Organic modified bentonite 18 copies Hydroxyethyl cellulose 23 copies Modified siloxane 1.5 servings Wetting and dispersing agent 0.8 parts Coalescent 2 copies Defoamer 0.6 parts thickener 0.8 parts antifungal agent 1.0 copies pH regulator 1.5 servings water Appropriate amount

[0049] Among them, the aggregate is a mixture of natural colored sand and quartz sand, the weight ratio of natural colored sand and quartz sand is 2:1, and the particle size of natural colored sand is 60 mesh, and the particle size of quartz sand is 100 mesh; It is an unsaturated fatty acid polyamine amide; the film-forming aid is ethylene glycol; the defoamer is selected from polyether modified defoamers; the thic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of building decoration materials, in particular to a waterproof stone-like coating. The stone-like coating is prepared from the following ingredients in parts by weight: 15 to 35 parts of waterborne epoxy resin, 3 to 15 parts of a waterborne curing agent, 5 to 18 parts of graphene, 80 to 120 parts of aggregates, 15 to 20 parts of organic modified bentonite, 10 to 25 parts of hydroxyethyl cellulose, 0.5 to 2 parts of modified siloxane, 0.5 to 1.5 parts of a wetting dispersant, 1 to 4 parts of a coalescing agent, 0.5 to 0.8 part of a defoaming agent, 0.5 to 1.2 parts of a thickening agent, 0.5 to 1.5 parts of a mildew preventive, 0.5 to 3 parts of a pH regulator and a proper amount of water, wherein the aggregate is composed of natural colored sand and quartz sand according to a weight ratio of (1-3): (1-2), the particle size of the natural colored sand is 40-80 meshes, and the particle size of the quartz sand is 80-120 meshes. The invention also provides a preparation method of the waterproof stone-like coating. The waterproof stone-like coating is greatly enhanced in water resistance, weather resistance and stain resistance, so the development and application of the stone-like coating are promoted.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, in particular to waterproof genuine stone paint and a preparation method thereof. Background technique [0002] Real stone paint has rich colors and strong colorability, which can create a harmonious and elegant architectural atmosphere. It has strong adhesion, fire resistance and corrosion resistance. Compared with traditional architectural coatings, it has wider environmental adaptability, making it widely used. For use on exterior walls. As one of the fastest-growing exterior wall paints in the current market demand, real stone paint is more and more favored by the market. [0003] However, at present, in the actual construction of real stone paint for exterior walls of construction projects, due to the influence of various uncertain factors and changes in the external environment, there are many problems in the application of real stone paint for exterior walls, such as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/61C09D7/62C09D7/63C09D7/65
CPCC09D1/00C09D7/61C09D7/62C09D7/63C09D7/65
Inventor 乔启信朱华林
Owner 安徽朗凯奇科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com