Dyeing and finishing production process of flame-retardant polyester fiber cut pile fabric

A flame-retardant polyester and production process technology, which is applied in the dyeing and finishing production process of flame-retardant polyester fiber cut pile fabrics, can solve the problems of irregular fluff length of double-faced fleece fabrics, cumbersome production steps of double-faced fleece fabrics, etc., and achieve fluff The length is neat, the production steps are simple, and the effect of improving production efficiency

Inactive Publication Date: 2021-11-05
苏州飞涛户外用品有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a dyeing and finishing production process of flame-retardant polyester fiber cut pile fabrics, to solve the problem that the length of fluff on the existing double-faced fleece fabrics proposed in the above-mentioned background technology is not uniform, and at the same time, the existing The production steps of double-sided fleece fabrics are relatively cumbersome

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dyeing and finishing production process of flame-retardant polyester fiber cut pile fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The production steps are as follows: weaving embryo, embryonic bleaching, embryonic softening, embryo, embryonic, embryonic, embryo, embryo, embryo, packaging, can receive a double-sided velvet fabric of fluffy Finished product;

[0028] In the woven embryo step, the embryo is formed by the polyester chamber, and the proportion of the polyester accumulation is woven on the spray loom of 80:20, and the routine width is 140 cm-250cm, and the square meters is gravy at 170GSM-300GSM. between.

[0029] The embryonic bubble is in turn, including: embryonic burning, embryonic immersion, embryonic cold heap, embryo cooking, initial stacked embryo, initial hydrostatic cloth, embryo bleaching, secondary stack embryo and Secondary water washing embryu, the conditions of cold stacks were 10 ° C - 30 ° C in ambient temperature.

[0030] The embryonic softening is inserted to soak the embryonic 40-50 ° C in the fulating agent, and the soaking time is 30 min.

[0031] The embryonic step i...

Embodiment 2

[0036] The production steps are as follows: weaving embryo, embryonic bleaching, embryonic softening, embryo, embryonic, embryonic, embryo, embryo, embryo, packaging, can receive a double-sided velvet fabric of fluffy Finished product;

[0037] In the woven embryo step, the embryo is made of polyester chamber, and the polyester chamber uses 70:30 comparison on the water spray loom, which is routinely width of 140 cm-250cm, and square meters at 170 GSM-300GSM. between.

[0038] The embryonic bubble is in turn, including: embryonic burning, embryonic immersion, embryonic cold heap, embryo cooking, initial stacked embryo, initial hydrostatic cloth, embryo bleaching, secondary stack embryo and Secondary water washing embryo, the conditions for cold stacks are ambient temperature 20 ° C to 40 ° C.

[0039] The embryonic is soft to soften to soak the temperature conditions of the embryo 30-40 ° C in the furcase, and the soaking time is 20 min.

[0040] The embryonic step is to pull the ...

Embodiment 3

[0045] The production steps are as follows: weaving embryo, embryonic bleaching, embryonic softening, embryo, embryonic, embryonic, embryo, embryo, embryo, packaging, can receive a double-sided velvet fabric of fluffy Finished product;

[0046] In the woven embryo step, the embryo is woven from the polyester chamber, and the polyester chamber uses 50:50 ratios to woven on the spray loom, and the routine width is 130 cm-230cm, and the square meters is gravy at 175GSM-315GSM. between.

[0047] The embryonic bubble is in turn, including: embryonic burning, embryonic immersion, embryonic cold heap, embryo cooking, initial stacked embryo, initial hydrostatic cloth, embryo bleaching, secondary stack embryo and Secondary water washing embryu, the conditions of cold stacks were at ambient temperature of 15 ° C -25 ° C.

[0048] The embryonic softening was soaked in a temperature condition of 10-30 ° C for 10-30 ° C, and the soaking time was 30 min.

[0049] The embryonic step is to pull t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a dyeing and finishing production process of a flame-retardant polyester fiber cut pile fabric, and belongs to the technical field of double-faced pile fabric production. The process comprises the following production steps of weaving gray cloth, re-bleaching the gray cloth, softening and finishing the gray cloth, napping the gray cloth, primarily shearing the gray cloth, secondarily shearing the gray cloth, dyeing the gray cloth, and carrying out finishing and packaging. The finished double-sided pile fabric with pile uniformity can be obtained. Compared with a double-sided pile fabric on the market, the double-sided pile fabric produced by the production process has the advantages that the pile length is relatively regular, workers only need to perform production according to the production steps in the production process, the production efficiency of the workers is greatly improved, and meanwhile, the production steps are relatively simple.

Description

Technical field [0001] The present invention relates to the technical field of double-sided velvet fabric production, and in particular, to a dyeing and whole production process of flame retardant polyester fiber cutting fabrics. Background technique [0002] Double velvet is one of the fabric, is a natural plush surface of the fabric in the production process, and the polyester single yarn, the polyester composite wire passes through special processing, and the fabric is fluffy and soft. The surface area and a rich capillary effect. The product has water absorption, dry and comfortable, strong defective, antibacterial hygiene. Its water absorbing capacity is twenty times of ordinary cotton fabrics, and the life is twenty times of ordinary cotton fabrics, suitable for families clean cloth, wipe, bathrobe, clothing fabric, etc. Fiber residues with strong water absorption and cotton fabric, are also ideal for optical glass, glass products, and high-grade merchandise surfaces. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/283D03D15/47D06B3/10D06C11/00D06C13/00D06C7/02D06P3/82
CPCD03D15/283D03D15/47D06B3/10D06C11/00D06C13/00D06C7/02D06P3/8214D10B2331/04D10B2331/02
Inventor 覃振华覃孟瀚
Owner 苏州飞涛户外用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com