Single-component water-based waterproof coating and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A waterproof coating, one-component technology, used in cement coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of short construction operation time, poor storage stability, easy sagging of exterior walls, etc. Fast drying speed on the wall, good operating time, good storage stability
Active Publication Date: 2021-11-30
BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD +1
View PDF8 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0015] The purpose of the present invention is to solve the above problems, to provide a single-component water-based waterproof coating and its preparation method, which is convenient for storage and transportation, and the coating can be prepared after mixing with cement in a certain proportion on the construction site, which has excellent mechanical properties and good environmental protection. Solved the problems of poor storage stability, short construction and operation time, and easy sagging and cracking of external walls.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment
[0083] Specific examples are as follows:
[0084] Table 1
[0085]
[0086]
[0087] The preparation method of above-mentioned one-component water-based waterproof paint comprises:
[0088] ① Measure deionized water, Mingling 730 hydrophobic agent, water-based wear-resistant additive and Yuhong CR-P100 into the liquid material mixing tank, turn on the disperser of the mixing tank, adjust the speed at 300r / min, and stir for 2 minutes .
[0089] ② Measure WACKER 7070 emulsion, DINCH plasticizer, self-crosslinking PVAE solution and raw tung oil into the liquid material mixing tank, adjust the speed to 500r / min and stir for 10 minutes.
[0090] ③Measure Mingling A203E defoamer and sodium hydroxymethyl cellulose solution NC-60 thickener and pre-mix evenly, slowly add to the liquid material mixing tank, and stir at 500r / min for 2 minutes.
[0091] ④ After measuring Hantai Chemical 1130 thickener, Dow RM-8W thickener, and Thor MBS preservative, slowly add it to the liquid ma...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
glass transition temperature
aaaaa
aaaaa
particle size
aaaaa
aaaaa
Login to view more
Abstract
The invention belongs to the field of waterproof materials, and particularly relates to a single-component water-based waterproof coating and a preparation method thereof. The coating is prepared from the following raw materials: VAE emulsion, an environment-friendly plasticizer, a self-crosslinking PVA solution, tung oil, a water repellent agent, a water-based wear-resistant additive, polycarboxylic acid mother liquor, water, a defoaming agent, a carboxymethyl cellulose sodium solution, an associated alkali swelling thickener, an associated polyurethane thickener and a preservative. The high-performance VAE emulsion is used as a main film forming substance, the environment-friendly plasticizer and a small amount of tung oil are added, and the prepared single-component water-based waterproof coating is convenient to store and transport, capable of being mixed with pure cement for use on a construction site, free of formaldehyde, odorless, good in environment friendliness and high in paint film elasticity. A self-crosslinked PVA solution is prepared, and the water-based wear-resistant auxiliary agent is added so that the thixotropy, the binding power and the wear resistance of the coating are improved, and the coating can be used for external wall construction. Sodium hydroxyethyl cellulose is dissolved in a mineral oil defoaming agent, so that the problem of easy agglomeration in addition is solved. By adding polycarboxylic acid mother liquor, the openness of the coating is prolonged.
Description
technical field [0001] The invention belongs to the field of waterproof materials, and more specifically relates to a single-component water-based waterproof coating and a preparation method thereof. Background technique [0002] (1) Technical background [0003] Waterproof material is one of the important components of building construction materials. According to the material, it can be divided into asphalt waterproof material, rubber plastic waterproof material, cement waterproof material and metal waterproof material. With the improvement of modern building requirements, modern waterproof material selection and construction technology are becoming more and more standardized, and water-based cement-based waterproof coatings represented by polymer cement waterproof coatings are simple in construction and good in environmental protection. The ratio of cement to meet different engineering environments, has been widely used in waterproof materials in recent years. [0004] ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.