Preparation method of metal glaze rock plate

A technology of metal glaze and slate, applied in the field of architectural ceramic tiles, can solve the problems of poor decorative effect, achieve the effects of saving manufacturing costs, simple and fast operation, and improving development efficiency

Active Publication Date: 2021-12-07
广东东唯新材料有限公司 +1
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is to provide a method for preparing metal glazed slate, which aims to solve the problem that the original craft decoration is simply copied to the slate, and the decorative effect is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of metal glaze rock plate
  • Preparation method of metal glaze rock plate
  • Preparation method of metal glaze rock plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0131] Undercoat color: black;

[0132] Rubber roller preset texture engraving parameters: dot diameter is 1.1mm, dot spacing is 0.5mm;

[0133] Metal glaze formula: metal material 1: 60%; metal material 2: 8%; metal material 3: 30%; metal material 4: 2%;

[0134] Specific gravity of metallic glaze: 1.65;

[0135] Metal glaze flow rate: 37 seconds;

[0136] The second pattern decoration layer: made by sequential inkjet printing of inks with five grayscales of 0%, 5%, 10%, 15%, and 20%;

[0137] Ink type: Glossy ink.

Embodiment 2

[0139] Base glaze color: brown;

[0140] The first pattern decoration layer: made by sequentially ink-jet printing inks of four gray scales of 10%, 20%, 30%, and 40%;

[0141] Ink type: glossy ink;

[0142] Rubber roller preset texture engraving parameters: dot diameter is 1.3mm, dot spacing is 0.7mm;

[0143] Metal glaze formula: metal material 1: 55%; metal material 2: 13%; metal material 3: 30%; metal material 4: 2%;

[0144] Specific gravity of metallic glaze: 1.68;

[0145] Metallic glaze flow rate: 32 seconds.

Embodiment 3

[0147] Base glaze color: blue;

[0148] The first pattern decoration layer: made by sequentially inkjet printing inks of five grayscales of 0%, 15%, 25%, 35%, and 45%;

[0149] Ink type: blue ink;

[0150] Rubber roller preset texture engraving parameters: dot diameter is 1.3mm, dot spacing is 0.7mm;

[0151] Metal glaze formula: metal material 1: 55%; metal material 2: 13%; metal material 3: 32%;

[0152] Specific gravity of metallic glaze: 1.68;

[0153] Metallic glaze flow rate: 35 seconds.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a metal glaze rock plate. The preparation method comprises the following steps: providing a green body layer; forming a ground coat layer on the surface of the green body layer; sequentially carrying out ink-jet printing on ink with different gray levels, and forming a first pattern decoration layer on the surface of the ground coat layer; forming a metal glaze layer on the surface of the first pattern decoration layer; sequentially carrying out ink-jet printing on ink with different gray levels, and forming a second pattern decoration layer on the surface of the metal glaze layer; and conducting sintering in a kiln to obtain the metal glaze rock plate. By the adoption of the method, the prepared metal glaze rock plate has varied texture, color, texture and layering effects, and the decoration effect of a product is enriched.

Description

technical field [0001] The invention relates to the field of architectural ceramic tiles, in particular to a method for preparing metal glazed rock panels. Background technique [0002] In recent years, as the homogenization of ceramic tile products in the building materials market has become increasingly serious, many ceramic manufacturers have begun product transformation, investing a lot of money in the construction of ceramic rock slab lines, and developing and producing rock slab products. Most of these newly invested ceramic rock slab lines are based on the raw materials and process platforms of the original ceramic tile production, upgrading equipment and technology, making the appearance of the product larger and thinner to 2.5mm to 3.5mm. These large and thin rock slab products have subverted the concept of traditional ceramic tiles and raised the technical and investment thresholds of production enterprises. Even the industry jokingly called it "making bricks in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)