Rare earth solid welding wire with excellent low-temperature impact toughness
A technology of low-temperature impact toughness and solid welding wire, which is applied in the field of metallurgy, can solve the problems of low-temperature impact toughness of welds, achieve excellent low-temperature impact toughness, and improve the effect of weld microstructure
Pending Publication Date: 2021-12-17
BAOTOU IRON & STEEL GRP
View PDF7 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] 600MPa welding wire is a commonly used high-strength welding wire, but when welding, the low-temperature impact toughness of the weld is low, which has always been the bottleneck restricting its wide use
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
example 1
[0022] Example 1 does not add rare earth, and example 2 adds rare earth, and the finished welding wire is subjected to welding test, and its low-temperature impact toughness is as follows:
[0023] Table 2 Weld impact test results
[0024]
[0025] The low-temperature impact performance of the welding seam welded by the rare earth solid welding wire of the present invention is obviously higher than that of the solid welding wire without adding rare earth.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more
Abstract
The invention discloses a rare earth solid welding wire with excellent low-temperature impact toughness. The rare earth solid welding wire comprises the following chemical components including, by mass, 0.06 to 0.10 percent of C, 1.40 to 1.55 percent of Mn, 0.80 to 0.95 percent of Si, 0.10 to 0.20 percent of Cr, 0.05 to 0.12 percent of Ti, 5 to 30 ppm of a rare earth element Ce and the balance Fe and inevitable impurities, wherein P in the impurities is less than or equal to 0.025 percent, and S in the impurities is less than or equal to 0.025 percent. The invention is suitable for 600 Mpa-level solid welding wires, the rare earth element Ce is transited into welding seams, and the welding seams have more excellent low-temperature-resistant impact toughness on the basis of high strength through the effects of refining welding seam grains, improving welding seam structures and purifying welding seam metal microalloying treatment.
Description
technical field [0001] The invention relates to the technical field of metallurgy, in particular to a rare earth solid welding wire with excellent low-temperature impact toughness. Background technique [0002] 600MPa welding wire is a commonly used high-strength welding wire, but when welding, the low-temperature impact toughness of the weld is low, which has always been a bottleneck restricting its wide use. Contents of the invention [0003] In order to solve the above technical problems, the object of the present invention is to provide a rare earth solid welding wire with excellent low temperature impact toughness. [0004] In order to solve the problems of the technologies described above, the present invention adopts the following technical solutions: [0005] A rare earth solid welding wire with excellent low-temperature impact toughness, the chemical composition of which is: C0.06-0.10%, Mn1.40-1.55%, Si0.80-0.95%, Cr0.10-0.20%, Ti0.05 -0.12%, rare earth element...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/30B23K35/40
CPCB23K35/3053B23K35/40
Inventor 吕刚赵晓敏杨鲁明白月琴
Owner BAOTOU IRON & STEEL GRP
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap