Epoxy curing agent as well as preparation method and application thereof
An epoxy curing agent and reaction technology, applied in the direction of epoxy resin coatings, coatings, etc., can solve the problems of unsuitable curing agent, expensive polythiol, and low crosslinking density, so as to increase the curing speed and improve Low curing agent activity, effect of improving low temperature surface state
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0040] Example 1
[0041] The hexamine 20g is first placed in the reactor with thiourea 8g, and the reaction temperature is controlled at 120 ° C to 150 ° C, reacting 2H, adding a polyether amine D400 22G, continuous reaction for 1 h, adding polypropylene glycol dihydrate glycerol ether 9g reaction, control The temperature was at 70 ° C to 90 ° C, reactive 2H, sequentially added trietanolamine 5g, lithoxol 16g, benzyl alcohol 20g, mix well, and the mixture was mixed.
Example Embodiment
[0042] Example 2:
[0043] The alone diamine is first placed in the reactor with thiourea 7g, and the reaction temperature is controlled at 120 ° C to 150 ° C, and the reaction is 2 h, and the polyether amine D230 20g is added, and the reaction is continued for 1 h, and the addition of pentanediol dihydrate glycerol. The ether 8g reaction was reacted, and the control temperature was at 70 ° C to 90 ° C, reaction 2H, and tenthanolamine 8 g, nonylphenol 16g, and benzyl alcohol were sequentially added to the reactor, and mixed uniform, and the discharge was obtained to obtain an epoxy curing agent.
Example Embodiment
[0044] Example 3:
[0045] First, 20 g of the methylcyclopentamine was placed in the reaction vessel, and the reaction temperature was controlled at 120 ° C to 150 ° C, and the reaction was 2 h, and the polyether amine T403 30g was added, and the reaction was continued for 1 h, and polyethylene glycol dihydrate glycerol was added. The ether 8g reacts, the control temperature is 70 ° C to 90 ° C, reaction 2H, sequentially add 2, 4, 6-three (dimethylaminomethyl) phenol 5g, n-butanol 10g, xylene 20g, mix uniform mixing into the reactor It is discharged to obtain an epoxy curing agent.
PUM
Property | Measurement | Unit |
---|---|---|
Shore d hardness | aaaaa | aaaaa |
Shore d hardness | aaaaa | aaaaa |
Shore d hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap