Single-component acrylic adhesive as well as preparation method and application thereof

An acrylic and adhesive technology, applied in the direction of adhesives, non-polymer adhesive additives, adhesive types, etc., can solve problems that affect production efficiency, glue is easy to gel, and coating time is short, so as to improve production efficiency, Easy peeling, extended coating time and storage time effect

Pending Publication Date: 2022-03-11
襄阳三沃航天薄膜材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the existing high-temperature resistant and antistatic acrylic adhesives are multi-component, and the glue is easy to gel when applied. The short distribution time will seriously affect the production efficiency, and the storage time is also short, and it will cause serious waste if it is not used or not used up within the effective time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Single-component acrylic adhesive as well as preparation method and application thereof
  • Single-component acrylic adhesive as well as preparation method and application thereof
  • Single-component acrylic adhesive as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A one-component acrylic adhesive, calculated in parts by weight, including 70 parts of isobutyl acrylate, 4 parts of methyl acrylate, 1 part of diallyl maleate, and 3 parts of methacryloxytrimethoxysilane , 0.1 parts of azobisisobutyronitrile, 100 parts of toluene, 0.3 parts of Cyastat LS, 0.033 parts of glacial acetic acid and 0.067 parts of aluminum acetylacetonate.

[0025] The preparation method is as follows:

[0026] S1, add 70 parts of isobutyl acrylate, 4 parts of methyl acrylate, 1 part of diallyl maleate and 3 parts of methacryloxytrimethoxysilane to the reaction vessel I in sequence, stir evenly to obtain a mixed Material A;

[0027] S2, add 5% of the weight of the mixture A and 50 parts of toluene in sequence in the reaction vessel II, stir evenly, and heat the mixture to 70°C, then slowly add 0.02 parts of azobisisobutyronitrile dropwise to the mixture , the dropping time is 0.5h, and the reaction is kept at 70°C for 1h to obtain the mixture B;

[0028] ...

Embodiment 2

[0032] A one-component acrylic adhesive, calculated in parts by weight, including 40 parts of n-butyl acrylate, 50 parts of ethyl acrylate, 4 parts of methyl methacrylate, 6 parts of n-butyl methacrylate, 2 parts of pentaerythritol triallyl 3 parts of diallyl terephthalate, 5 parts of acrylic acid, 4 parts of trifluoroethyl methacrylate, 4 parts of hexafluorobutyl ester, 0.3 parts of azobisisobutyronitrile, 0.2 parts of dibenzoyl peroxide Parts, 70 parts of ethyl acetate, 80 parts of butanone, 6091 parts of Cyast, 0.25 parts of glacial acetic acid, 0.25 parts of aluminum acetylacetonate.

[0033] The preparation method is as follows:

[0034] S1, add 40 parts of n-butyl acrylate, 50 parts of ethyl acrylate, 4 parts of methyl methacrylate, 6 parts of n-butyl methacrylate, 2 parts of pentaerythritol triallyl, terephthalic acid 3 parts of diallyl ester, 5 parts of acrylic acid, 4 parts of trifluoroethyl methacrylate and 4 parts of hexafluorobutyl ester, stirred evenly to obtain ...

Embodiment 3

[0040] A one-component acrylic adhesive, calculated in parts by weight, including 30 parts of isobutyl acrylate, 50 parts of isooctyl acrylate, 4 parts of acrylonitrile, 6 parts of styrene, 2 parts of methacrylic acid, and 2 parts of itaconic acid , 2 parts of maleic acid, 2 parts of fumaric acid, 3 parts of N-vinylpyrrolidone, 4 parts of N-vinylcarbazole, 0.2 parts of benzoyl peroxide, 0.2 parts of azobisisoheptanonitrile, 40 parts of toluene, Acetone 80 parts, Cyastat SP 0.8 parts, glacial acetic acid 0.2 parts and aluminum acetylacetonate 0.2 parts.

[0041] The preparation method is as follows:

[0042] S1, add 30 parts of isobutyl acrylate, 50 parts of isooctyl acrylate, 4 parts of acrylonitrile, 6 parts of styrene, 2 parts of methacrylic acid, 2 parts of itaconic acid and 2 parts of maleic acid in the reaction vessel I , 2 parts of fumaric acid, 3 parts of N-vinylpyrrolidone, 4 parts of N-vinylcarbazole, stir evenly to obtain the mixture A;

[0043] S2, add 10% of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a single-component acrylic adhesive which comprises the following components in parts by weight: 70-90 parts of a soft monomer, 4-10 parts of a hard monomer, 1-10 parts of a functional monomer, 3-8 parts of a heat-resistant modified monomer, 0.1-0.5 part of an initiator, 100-150 parts of a solvent, 0.3-1 part of an antistatic agent and 0.1-0.5 part of a curing agent, the curing agent is glacial acetic acid and aluminum acetylacetonate. The aluminum acetylacetonate curing agent compounded by glacial acetic acid is added in the preparation process, so that on one hand, the stability of the adhesive is improved, on the other hand, the coating time and the storage time of the adhesive are prolonged, the coating time of the adhesive is prolonged to 8.5-10.5 h, the adhesive does not gel, the storage time reaches 6-8 months, the production efficiency is effectively improved, and the production cost is reduced. And the production cost is saved.

Description

technical field [0001] The invention relates to the technical field of acrylic adhesives, in particular to a one-component acrylic adhesive and its preparation method and application. Background technique [0002] PET protective film is widely used in various fields, such as automobile manufacturing, electronic component manufacturing and life, etc., especially in the process of manufacturing and shipping protection of FPC, PCB and mobile phone electronic components, when encountering high temperature environment, it is required to use pressure sensitive The adhesive has high temperature resistance, and there is no residual adhesive on the protected surface after high temperature use, and the peeling force does not increase significantly after high temperature and is easy to peel off. During the use of the PET protective film, static electricity is generated by mutual contact and friction. Especially in a dry environment, static electricity is a great safety hazard, which wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C09J11/06C09J7/30C09J7/25C08F220/18C08F220/14C08F222/28C08F230/08C08F222/14C08F220/24
CPCC09J143/04C09J133/16C09J139/06C09J11/06C09J7/30C09J7/255C08F220/1804C08F220/1808C08F220/1802C08K5/09C08K5/07C08F220/14C08F222/28C08F230/085C08F222/104C08F222/26C08F222/14C08F220/06C08F220/24Y02E10/50
Inventor 李莹李二威刘鎏梁立明尹鹏贾永华张行颖周志豪
Owner 襄阳三沃航天薄膜材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap