High-ball-pressure flame-retardant PC/ABS material as well as preparation method and application thereof

A technology of ABS material and ABS resin, which is applied in the field of high-ball pressure flame-retardant PC/ABS material and its preparation, can solve the problems of flame retardancy and heat resistance that cannot meet the requirements of heat resistance, and can ensure flame retardancy and mechanical properties. performance, the effect of increasing the high ball pressure temperature

Pending Publication Date: 2022-04-12
KINGFA SCI & TECH CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to overcome the defects and deficiencies that the existing PC / ABS material flame retardancy and heat resistance cannot meet the requirements of products with higher heat resistance requirements, and provide a kind of heat resistance, flame retardancy, mechanical properties Better high ball pressure flame retardant PC / ABS material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-ball-pressure flame-retardant PC/ABS material as well as preparation method and application thereof
  • High-ball-pressure flame-retardant PC/ABS material as well as preparation method and application thereof
  • High-ball-pressure flame-retardant PC/ABS material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～3

[0050] Embodiments 1-3 A high ball pressure flame-retardant PC / ABS material

[0051] See Table 1 for the components and proportions of the high ball pressure flame-retardant PC / ABS material.

[0052] Table 1 Embodiment 1~3 components and formula (kg)

[0053]

[0054] Preparation:

[0055] Add each component into the mixer according to the formula and mix evenly to obtain a premix; the obtained premix is ​​sent to an extruder for kneading, extrusion, and post-processing; wherein, the setting temperature is 190-210°C, The rotating speed is 250r / min, and the feeding is 40kg / h.

Embodiment 4～6

[0056] Embodiments 4-6 A kind of high ball pressure flame-retardant PC / ABS material

[0057] See Table 2 for the component distribution ratio of the high ball pressure flame-retardant PC / ABS material.

[0058] Table 2 embodiment 4~6 components and formula (kg)

[0059]

[0060] Preparation:

[0061] Add each component into the mixer according to the formula and mix evenly to obtain a premix; the obtained premix is ​​sent to an extruder for kneading, extrusion, and post-processing; wherein, the setting temperature is 190-210°C, The rotating speed is 250r / min, and the feeding is 40kg / h.

Embodiment 7～9

[0062] Embodiments 7-9 A high ball pressure flame-retardant PC / ABS material

[0063] See Table 3 for the component distribution ratio of the high ball pressure flame-retardant PC / ABS material.

[0064] Table 3 Embodiment 7~9 components and formula (kg)

[0065]

[0066] Preparation:

[0067] Add each component into the mixer according to the formula and mix evenly to obtain a premix; the obtained premix is ​​sent to an extruder for kneading, extrusion, and post-processing; wherein, the setting temperature is 190-210°C, The rotating speed is 250r / min, and the feeding is 40kg / h.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of modified plastics, and particularly relates to a high-ball-pressure flame-retardant PC / ABS (polycarbonate / acrylonitrile-butadiene-styrene) material as well as a preparation method and application thereof. The material is mainly prepared from the components such as the polymeric high-molecular flame retardant, the antimony flame retardant, the heat-resistant agent and the organic silicon / acrylic acid composite rubber flexibilizer, all the components have a synergistic effect, the polymeric high-molecular flame retardant and the heat-resistant agent can jointly increase the ball pressure temperature of the ABS material, the toughness of the ABS material can be improved by combining with the flexibilizer, and the toughness of the ABS material is improved. The high ball pressure temperature of the flame-retardant PC / ABS material is remarkably improved, meanwhile, the flame retardance and the mechanical property of the flame-retardant PC / ABS material can be guaranteed, and the flame-retardant PC / ABS material is very suitable for manufacturing high-temperature-resistant products.

Description

technical field [0001] The invention belongs to the technical field of modified plastics. More specifically, it relates to a high ball pressure flame-retardant PC / ABS material and its preparation method and application. Background technique [0002] Acrylonitrile-butadiene-styrene terpolymer (ABS), a material with both rigidity and toughness, is widely used in home appliances, office equipment and automobiles. At the same time, ABS is also a flammable material, and its heat resistance and flame retardancy are not very good. It needs to be transformed into a flame retardant material by adding a flame retardant. Since low-molecular bromine, phosphorus and nitrogen flame retardants have certain plasticizing properties for ABS resins, adding them will lead to a significant reduction in the heat resistance of ABS materials. For example, the ball pressure (heat resistance) of general ABS materials is only about 85°C, and the ball pressure temperature is lower after adding flame ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L69/00C08L55/02C08L25/18C08L25/06C08L35/06C08K3/22C08K5/526
Inventor 刘凯陈平绪叶南飚秦旺平王亮付锦锋杨霄云
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com