Adhesion testing device and method for coating layer of tin-plated steel sheet

A technology of electroplated tin-plated steel sheet and inspection device, which is applied to the device for coating liquid on the surface, the use of mechanical devices, coatings, etc., which can solve the problems of inaccurate sample detection results, inconvenient sample taking and placing, and inaccurate detection. To achieve the effect of improving market competitiveness, convenient classification and placement, and accurate detection results

Active Publication Date: 2022-06-07
粤海中粤(秦皇岛)马口铁工业有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] One of the main purposes of the present invention is to provide an adhesion test method for the coating layer of electroplated tin-plated steel sheet, so as to solve the insufficient sensitivity of the detection method in the prior art, which cannot distinguish the subtle difference of coating performance and the detection method. inaccurate question
[0004] The second main purpose of the present invention is to provide an adhesion testing device for the coating layer of tin-plated steel sheets, so as to solve the inconvenience of taking and placing the samples and the inability to heat the samples evenly when the oven in the prior art is heating the samples. The problem of inaccurate sample test results

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesion testing device and method for coating layer of tin-plated steel sheet
  • Adhesion testing device and method for coating layer of tin-plated steel sheet
  • Adhesion testing device and method for coating layer of tin-plated steel sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] like Figure 1-Figure 5 As shown in the figure, the present invention proposes an adhesion inspection device for the coating layer of electroplated tin steel sheet, comprising an oven 1, a storage tray 2 is rotated inside the oven 1, and a rotating device is arranged below the storage tray 2, above which A fixing device is provided. The rotating device includes a turntable 3 and a power part arranged under the turntable 3. The power part drives the turntable 3 to rotate. The matching connection hole 19, the storage tray 2 is placed directly above the turntable 3, and the central connection hole 19 is sleeved on the outside of the central shaft 29; the fixing device includes a sleeve 4 and a vertically arranged fixing shaft 5, the fixing shaft 5 and the central shaft 29 are arranged coaxially, the top of the fixed shaft 5 is fixed on the top wall of the oven 1, the center of the sleeve 4 is provided with a vertical through hole, the sleeve 4 is sleeved on the outside of ...

Embodiment 2

[0045] like Figure 1-Figure 5 As shown, a method for inspecting the adhesion of the coating layer of electroplated tin steel sheet, using the adhesion inspection device for the coating layer of electroplated tin steel sheet in Embodiment 1, comprising the following steps:

[0046] S1. Place the samples to be tested in the corresponding baking trays 22 in sequence according to their respective classifications, and place the baking trays 22 on the storage tray 2 correspondingly.

[0047] S2. Pull the pulling part upwards to move the sleeve 4 upward, then place the storage tray 2 on the turntable 3, and then release the pulling part, the sleeve 4 moves down and presses the storage tray 2, and the storage tray 2 is attached to the turntable 3; start the oven 1 and the stepping motor 28, the turntable 3 drives the storage tray 2 to rotate synchronously, wherein the baking temperature is 215 ° C, and the baking time is 24 minutes; wherein the specific use method of the oven 1 is as...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an adhesion inspection device and method for the coating layer of electroplated tin thin steel plate. By adding harsh baking conditions, the sample is first baked at 215°C for 24 minutes, and then the sample is baked with a hundred grid knife. After the sample is baked under this baking condition, it can accurately distinguish the nuances of the coating adhesion of different samples, and the test result is more accurate, which can guide the optimization of the production process and the development of new products. Bring economic benefits and social benefits to enterprises and society, and improve the market competitive advantage of products; secondly, the oven equipment adopted in the present invention can make the storage tray rotate inside the oven by setting a fixing device and a rotating device, so that the oven is baked The baked samples are evenly heated to ensure the consistency of the sample testing conditions and the accuracy of the test results; secondly, the storage tray can be easily taken out and put in from the inside of the oven, and divided into multiple storage areas, which can facilitate the classification and placement of samples.

Description

technical field [0001] The invention relates to the technical field of adhesion inspection of the coating layer of electroplated tin steel sheet, in particular to an adhesion inspection device and method for the coating layer of electroplated tin steel sheet. Background technique [0002] In the prior art, the detection of the adhesion of the coating layer printed on the electroplated tin steel plate usually adopts the ordinary scraping experiment, that is, the tool is used to directly draw a grid on the surface of the sample coating, and then the adhesive tape is pasted, and the adhesion of the tape is observed to judge the adhesion. The sensitivity of this kind of scraping coating experiment is insufficient, and it is impossible to distinguish the subtle differences in coating performance. Although the coating is sometimes pulled off in a large area during the test, there is no peeling, anti-sticking, anti-sticking, etc. in the subsequent process. Grinding and other phenom...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N19/04B05D3/02
Inventor 张俊美马辉郑帅梅华兴
Owner 粤海中粤(秦皇岛)马口铁工业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com