Polyurethane material for curtain wall, building curtain wall profile and preparation method of building curtain wall profile

A polyurethane material and polyurethane technology, which is applied in buildings, building components, building structures, etc., can solve problems such as poor flame retardant performance, poor mechanical strength, and inability to meet, achieve excellent mechanical properties, improve aesthetics and applicability performance, long service life

Pending Publication Date: 2022-08-09
广东五恒新材料有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the current polyurethane materials for curtain walls still have the problems of poor mechanical strength and poor flame retardancy, and high energy consumption in the production process, which cannot meet the needs of areas with higher energy-saving requirements and higher-end buildings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyurethane material for curtain wall, building curtain wall profile and preparation method of building curtain wall profile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] The polyurethane material for curtain wall described in this embodiment includes 50 parts of bicomponent fibers, 50 parts of polyol, 70 parts of polyisocyanate, 0.1 part of catalyst, 0.1 part of foaming agent, and 0.1 part of foam stabilizer in terms of mass fraction. parts, 5 parts of flame retardants, 15 parts of colorants, 10 parts of antistatic additives, 40 parts of sound-absorbing materials, 5 parts of preservatives, and 50 parts of water.

[0060] When the bicomponent fibers are side-by-side bicomponent fibers, the side-by-side bicomponent fibers are carbon fiber-polyurethane fibers;

[0061] The polyol is a polyether polyol; the catalyst is an amine catalyst; the foaming agent is monofluorodichloroethane; the foam stabilizer is a polyether modified organosilicon surfactant; the coloring The agent is manganese salt; the flame retardant is nitrogen-based flame retardant; the antistatic auxiliary agent is cetyltrimethylammonium chloride; the sound-absorbing materia...

Embodiment 2

[0072] The polyurethane material for curtain wall described in this embodiment includes 80 parts of fibers, 70 parts of polyols, 90 parts of polyisocyanates, 2.5 parts of catalysts, 2.5 parts of foaming agents, 2.5 parts of foam stabilizers, and 2.5 parts of foam stabilizers. 30 parts of burning agent, 50 parts of coloring agent, 30 parts of antistatic additives, 60 parts of sound-absorbing materials, 25 parts of preservatives, and 90 parts of water.

[0073] When the bicomponent fiber is a side-by-side bicomponent fiber, the bicomponent is glass fiber / polyurethane fiber.

[0074] The polyol is a polyester polyol; the catalyst includes an organic metal catalyst; the foaming agent is cyclopentane; the foam stabilizer is a polyether modified organosilicon surfactant; Valence iron salt; the flame retardant is phosphorus flame retardant; the antistatic auxiliary is octadecyl dimethyl hydroxyethyl quaternary ammonium nitrate; the sound-absorbing material is foam metal; the preserva...

Embodiment 3

[0080] The polyurethane material for curtain wall described in this embodiment, in terms of mass fraction, includes 60 parts of bicomponent fibers, 60 parts of polyol, 90 parts of polyisocyanate, 2 parts of catalyst, 2 parts of foaming agent, and 2 parts of foam stabilizer. parts, 10 parts of flame retardants, 30 parts of colorants, 25 parts of antistatic additives, 50 parts of sound-absorbing materials, 10 parts of preservatives, and 80 parts of water. That is, when the flame retardant is 10 parts, the mass ratio of antistatic additives and preservatives is 5:2; when the added colorant is 30 parts, the mass ratio of bicomponent fiber: polyol: polyisocyanate: colorant is 1:1:1.5:0.5.

[0081] When the bicomponent fibers are sheath-core fibers, the sheath / core structure is polyurethane fibers / carbon fibers.

[0082] Polyol is polyether polyol; catalyst organometallic catalyst; foaming agent isopentane; foam stabilizer is polyether modified silicone surfactant; colorant is copp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a polyurethane material for a curtain wall, which is prepared from the following components in parts by mass: 50 to 70 parts of polyol, 70 to 90 parts of polyisocyanate, 0.1 to 2.5 parts of catalyst, 0.1 to 2.5 parts of foaming agent, 0.1 to 2.5 parts of foam stabilizer, 50 to 80 parts of bi-component fiber, 5 to 30 parts of flame retardant, 15 to 50 parts of coloring agent, 10 to 30 parts of antistatic aid, 40 to 60 parts of sound absorbing material, 5 to 25 parts of preservative and 10 to 500 parts of water. The invention further discloses a building curtain wall profile and a preparation method thereof. The obtained building curtain wall profile has excellent mechanical property, good flame retardant property, shock resistance and sound insulation, normal-temperature forming is achieved, energy consumption in the production process is saved, attractiveness and elegance are achieved, and application and popularization of the environment-friendly curtain wall profile are facilitated.

Description

technical field [0001] The invention belongs to the technical field of new materials, and particularly relates to a polyurethane material for curtain walls, a building curtain wall profile and a preparation method thereof. Background technique [0002] The curtain wall is the outer wall of the building. It is not load-bearing and hangs like a curtain, so it is also called "curtain wall". It is a lightweight wall with decorative effects commonly used in modern large and high-rise buildings. It is composed of a panel and a supporting structure system, which can have a certain displacement ability relative to the main structure or a certain deformation ability itself, and does not undertake the role of the main structure. Water tightness, air tightness, shock resistance, thermal insulation, sound insulation, fire prevention, sound absorption, aesthetics, decoration and other aspects have high requirements. [0003] Polyurethane is an organic polymer material with high strength...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04B2/88E04B1/98E04B1/94E04B1/88E04B1/64C08L75/08C08L75/06C08L81/02C08L75/04C08K7/06C08K7/14C08K7/24C08J9/14B29C70/42
CPCE04B2/88E04B1/98E04B1/942E04B1/88E04B1/644C08J9/141C08J9/144C08J9/0095C08J9/0085C08J9/0066B29C70/42C08J2375/08C08J2375/06C08J2475/04C08J2481/02C08K7/06C08K7/14C08K7/24C08J2203/14C08J2203/142Y02A30/00Y02B30/90
Inventor 刘艳斌
Owner 广东五恒新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap