Green tea natural fibre, textile and manufacturing method thereof

A technology of natural fibers and production methods, applied in the fields of fiber processing, textiles and paper making

Inactive Publication Date: 2006-01-04
信阳市浉河区上游环宇服装内衣厂
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are no domestic literature reports on the application of green tea on textiles, and foreign reports are mostly about the product itself. What about the production of fibers and fabrics?

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Green tea natural fibre, textile and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: green tea fiber production

[0011] The cotton fiber is dipped into the catechin solution, the catechin solution is made of 2.5% catechin by weight, puffing agent P-461%, penetrating agent JFC 0.5% and water 96%, at a temperature of 75°C, Pad and roll for 35 minutes at a pressure of 0.20MP to make the water content 65%, take it out and put it in a drying container, preheat it at 98°C for 5 minutes, then bake it at 120°C for 3 minutes, and then put it into the rolling tank Immerse the bridging agent in the middle, the bridging agent is made of ethylene sulfoxide 1% by weight, penetrant JFC 0.5% and water 98.5%, padding at a temperature of 90°C and a pressure of 0.20MP for 55 minutes to make it contain water The rate is 65%, and then rinsed 4 times (passes) under cold water at 25°C, then soaped at 95°C for 10 minutes, then placed in a drying container, and dried at 100°C (moisture content less than 0.5%) .

Embodiment 2

[0012] Example 2: Production of Green Tea Fabric

[0013] Immerse the cotton fabric into the catechin solution made of 4% catechin by weight, 1% swelling agent S-2P, 0.5% penetrant T and 94.5% water, at a temperature of 70°C and a pressure of 0.25MP, Roll for 40 minutes to make its moisture content 75%, put it into a drying container, pre-bake it at 100°C for 3 minutes, then bake it at 120°C for 3 minutes and dry it (moisture content is less than 0.2%). The bridging agent made of ethylene sulfoxide 1.5% by weight, penetrant T 0.5% and water 98% is soaked for 50 minutes at a temperature of 95°C and a pressure of 0.25MP, and the water content is 65%. Rinse 4 times with cold water at 20°C, then soap at 95°C for 10 minutes, then place in a drying container and dry at 100°C.

[0014] The difference between the present invention and current green tea products (such as products from various factories in Japan) is that catechins are connected with cotton cellulose through chemical bo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention is a kind of natural green tea fibre and fabric and its method of produce. It can availably solve the problem of produce natural green tea fibre and fabric using the distill of green tea. The technical precept is solved, fibre and fabric contains cutch via graft technology. Accordingly it becomes natural green tea fibre and fabric. The method is let fibre or fabric dip in the liquid which contains cutch, expander, filter and water. After edosmosis, dry it. And then dip in the bridge liquid which contains ethene sulfoxide, filter and water to graft. And then wash it and dry it. The method is simple, novelty, particular, the manufacture is depended on cutch with the chemical bond and fibrin connected to make natural green tea fibre and fabric. The capability of the production is good. The invention is used widely, environment protected, has economic and great social benefit.

Description

1. Technical field [0001] The invention relates to a production method of green tea natural fiber and fabric. 2. Background technology [0002] With people's continuous pursuit of green consumption and environmental protection products, that is, natural, antibacterial, moisture-absorbing, breathable, cool and comfortable, and health-care products are more and more valued and favored by human beings. [0003] Why tea is welcomed by people, except that it is a kind of good beverage that is welcomed by people, also because it can play certain health care and therapeutic effect to human body. Modern biochemical and medical research has proved that in the chemical composition of tea leaves, there are more than 450 kinds of organic compounds and no less than 15 kinds of inorganic mineral nutrients. It can be seen that tea has both nutritional value and pharmacological effects on the human body. It is closely related to people's health. Various substances have different nutritiona...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M13/10
Inventor 赵鑫荣
Owner 信阳市浉河区上游环宇服装内衣厂