Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Aluminium based interlayer alloy for liquid phase diffusion weld

A liquid phase diffusion and interlayer technology, which is applied in the field of aluminum-based interlayer alloys in liquid phase diffusion welding of aluminum and aluminum alloys, can solve the problem of incomplete interaction between solder and base metal, difficulty in ensuring uniform solder wetting, low welding strength, etc. Problems, achieve the effect of reducing discontinuity, enhancing bonding force, and low welding cost

Inactive Publication Date: 2006-09-13
SHANDONG HUADIAN ENERGY SAVING TECH
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, vacuum brazing technology is very sensitive to slight changes in parameters, it is difficult to ensure uniform solder wetting, the interaction between solder and base metal is incomplete, the welding strength is low, and the pass rate is low; in addition, the use of vacuum equipment has high cost, long cycle and low efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] Specific examples of the present invention are given below.

[0012] An aluminum-based intermediate layer alloy for liquid phase diffusion welding, the weight percentage of each component is 8% of silicon, 2.5% of copper, 2% of magnesium, 0.03% of gallium, 0.02% of cerium, and the balance is Al.

[0013] The aluminum-based interlayer alloy was prepared as a thin film with a thickness of 0.05 mm.

[0014] The aluminum-based intermediate layer of this composition is used in the liquid phase diffusion welding of φ60×8 aluminum-silicon alloy pipe (LF2), and the result is: when stretched, it breaks on the base material, and the tensile strength is σ b =215MPa, reaching the tensile strength of base metal (σ b ≥170MPa); bending 90° without breaking.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
melting pointaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aluminum base middle-layer alloy for liquid phase diffusion welding. The weight percentage of each element is: aluminum 60-95%, silicon 0.5-10%, copper 0.5-35%, magnesium 0.5-10%, gallium 0.001-1%, rare earth 0.001-0.1%. It can be applied to the weld of each kind of aluminum and aluminum alloy product.

Description

technical field [0001] The invention relates to an aluminum-based interlayer alloy for liquid-phase diffusion welding, in particular to an aluminum-based interlayer alloy for liquid-phase diffusion welding of aluminum and aluminum alloys. Background technique [0002] Aluminum and aluminum alloys are widely used in aviation, aerospace, military and civil fields due to their low density, good corrosion resistance, and excellent thermal and electrical conductivity. Because there is a very dense oxide film on the surface of aluminum and its alloys, the property of this oxide film is very stable, it can fully resist the erosion of the atmosphere, and it can form a new film at any time when the old film is broken, so aluminum and its alloys are very Difficult to solder. [0003] Someone used vacuum brazing technology to weld aluminum and its alloys. Mg was added to the solder as the main element to remove the oxide film, and the oxide film was removed under vacuum conditions. H...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/28C22C21/12
Inventor 李辛庚王学刚严黔
Owner SHANDONG HUADIAN ENERGY SAVING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com