High-performance inorganic alkali-free chlorine-free waterproof anti-cracking agent

A high-performance, anti-cracking agent technology, applied in the field of cement concrete waterproof, moisture-proof and anti-cracking agent, can solve the problems of passivation film damage, unstable passivation film, difficult passivation film, etc.

Inactive Publication Date: 2006-09-13
廖志伟
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the pH<11.5, the passivation film begins to be unstable (critical value); when the pH<9.88, the passivation film is difficult to form or the passivation film that has already been formed is gradually destroyed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] High-performance inorganic non-alkali and chlorine-free waterproof, moisture-proof and anti-cracking agent. + 、Na + Chemical raw materials.

[0038] The first composition consists of Al 2 (SO 4 ) 3 , FeSO 4 ·7H 2 O, Co(NH 2 ) 2 、CuSO 4 ·5H 2 O, water composition, the weight percent of each component is:

[0039] Al 2 (SO 4 ) 3 10,

[0040] FeSO 4 ·7H 2 O 45,

[0041] Co(NH 2 ) 2 0.1,

[0042] Food grade CuSO 4 ·5H 2 O 0.1,

[0043] water 44.8;

[0044] The second composition includes Al 2 (SO 4 ) 3 , triethanolamine, FeSO 4 ·7H 2 O, calcium stearate, CuSO 4 ·5H 2 O, CaCO 3 , water, the weight percent of each component is:

[0045] Al 2 (SO 4 ) 3 10,

[0046] Triethanolamine 16,

[0047] FeSO 4 ·7H 2 O 0.1,

[0048] Calcium stearate 0.1,

[0049] Food grade CuSO 4 ·5H 2 O 0.1,

[0050] CaCO 3 0.01,

[0051] Water 73.69.

[0052] The preparation of the first composition is to...

Embodiment 2

[0054] High-performance inorganic alkali-free, chlorine-free, waterproof, moisture-proof and anti-cracking agent. + 、Na + Chemical raw materials.

[0055] The first composition consists of Al 2 (SO 4 ) 3 , FeSO 4 ·7H 2 O, Co(NH 2 ) 2 、CuSO 4 ·5H 2 O, water composition, the weight percent of each component is:

[0056] Al 2 (SO 4 ) 3 45,

[0057] FeSO 4 ·7H 2 O 1,

[0058] Co(NH 2 ) 2 1,

[0059] Food grade CuSO 4 ·5H 2 O 1,

[0060] water 52;

[0061] The second composition includes Al 2 (SO 4 ) 3 , triethanolamine, FeSO 4 ·7H 2 O, calcium stearate, CuSO 4 ·5H 2 O, CaCO 3 , water, the weight percent of each component is:

[0062] Al 2 (SO 4 ) 3 50,

[0063] Triethanolamine 2,

[0064] FeSO 4 ·7H 2 O 1,

[0065] Calcium Stearate 1,

[0066] Food grade CuSO 4 ·5H 2 O 1,

[0067] CaCO 3 1,

[0068] water 44.

[0069] The preparation of the first composition is to stir the raw mate...

Embodiment 3

[0071] High-performance inorganic non-alkali and chlorine-free waterproof, moisture-proof and anti-cracking agent. + 、Na + Chemical raw materials.

[0072] The first composition (mortar type) consists of Al 2 (SO 4 ) 3 , FeSO 4 ·7H 2 O, Co(NH 2 ) 2 、CuSO 4 ·5H 2 O, water composition, the weight percent of each component is:

[0073] Al 2 (SO 4 ) 3 20,

[0074] FeSO 4 ·7H 2 O 20,

[0075] Co(NH 2 ) 2 10,

[0076] Food grade CuSO 4 ·5H 2 O 10,

[0077] water 40;

[0078] The second composition (concrete type) consists of Al 2 (SO 4 ) 3 , triethanolamine, FeSO 4 ·7H 2 O, calcium stearate, urea, CuSO 4 ·5H 2 O, CaCO 3 , water composition, the weight percent of each component is:

[0079] Al 2 (SO 4 ) 3 10,

[0080] Triethanolamine 2,

[0081] FeSO 4 ·7H 2 O 30,

[0082] Calcium Stearate 3,

[0083] Food grade CuSO 4 ·5H 2 O 3,

[0084] CaCO 3 5,

[0085] Urea 7,

[0086] water 40....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a cement water-proof damp-proof agent comprising two matching compositions, wherein the the first composition consists of Al2(So4)3, FeSO4*7H2O, Co(NH2)2, CuSO4*5H2O and water, the second composition consists of Al2(SO4)3, triethanolamine, FeSO4*7H2O, calcium stearate, urea, CuSO4*5H2O, CaCO3 and water. The advantages of the invention include water-proof, anticracking and high reliability in moisture protection.

Description

technical field [0001] The invention relates to a waterproof, moisture-proof and anti-cracking agent for cement concrete in various construction projects and water conservancy projects. Background technique [0002] In actual engineering, many roads and bridges cannot reach the designed service life, and some of them have only been used for a few years and have been seriously damaged, so they need to be repaired on a large scale. Practice has proved that Cl - It is an important reason for the deterioration of the durability of roads, bridges and other structures, and now many cement concrete admixtures such as waterproofing agents, plugging agents, early strength agents, and water reducing agents contain a lot of Cl - , when mixed into cement concrete, it will accelerate the corrosion of steel bars and lead to cracking and damage of cement concrete. [0003] Cl - The corrosion effect on the steel bars inside the concrete is multifaceted, including: (1) Destruction of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B22/08C04B22/14C04B24/08C04B24/12
Inventor 廖志伟
Owner 廖志伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com