Gas-antirust buffering packing sheet and its making process

A cushioning packaging and vapor phase antirust technology, which is applied in the field of vapor phase antirust cushioning packaging sheet and its manufacturing, can solve the problems of thin film thickness, vapor phase antirust paper without cushioning, and lack of cushioning capacity, so as to enhance the tensile strength , anti-rust effect durable, high cushioning elastic effect

Inactive Publication Date: 2007-02-14
全桂媛
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above two anti-rust packaging materials still have some defects in the practical performance of packaging. For example, the vapor phase anti-rust paper has no cushioning and heat sealing properties, and has limitations in the protection of the smooth surface of metal and metal products and the airtightness of the packaging. ; while the vapor phase antirust plastic film has heat sealing and recyclability, which can provide good packaging airtightness and environmental protection for metal and metal products, but because the film is thin and does not have cushioning capacity, it is suitable for automobiles. It is very important and necessary to provide a packaging material with good anti-rust function and cushioning function in transportation, handling and storage of metal products such as accessories, mechanical parts, weaponry and other metal products that require high protection on the outer surface.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] The raw material components of gas-phase anti-rust cushioning packaging sheet are characterized by mass percentage: polyethylene resin is 70-99%, gas-phase corrosion inhibitor VCI is 0.55-18%, auxiliary agent is 0.05-12%, and the dispersion The additive is 0.5-3%, the auxiliary material is 0-0.5%, and the sum of the mass percentages of the above components is 100%.

[0008] The manufacturing method of the sheet: firstly carry out pretreatment of powder raw materials: mix the selected VCI powder material with dispersant according to the above components, and carry out micronization treatment through a grinder to make the particle size reach more than 600 mesh; Vinyl resin, vapor phase corrosion inhibitor VCI powder and dispersant are mixed evenly, then added to the barrel of polyethylene foam extruder, heated and melted at 140-210°C, mixed with auxiliary materials and auxiliary materials, extruded through polyethylene foam extruder Then, the size of the sheet is fixed by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
melt flow indexaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The antirust buffering packing sheet is prepared with polyethylene resin 70-99 wt%, gaseous corrosion inhibitor VCI 0.55-18 wt%, assistant 0.05-12 wt% and supplementary material 0-0.5 wt%. The antirust buffering packing sheet has thickness 0.5-15 mm, pores of opened or closed structure and size 0.025-0.5 mm, and foaming rate of 10-50 %. The making process includes compounding material based on the ratio, p-treatment to form fine powder, extruding in extruder and foaming. The sheet has the comprehensive effects of preventing rust, buffering, preventing shock, preventing humidity, etc., may be reused and has wide application and low cost.

Description

technical field [0001] The invention relates to a rust-proof, shock-proof, cushioning and smooth surface protection packaging material for metal products and a manufacturing method thereof. Background technique [0002] Metal and metal products are easily corroded by air pollution and other environmental pollution during the months to one or two years of transportation, handling, and storage after they are manufactured and before use. The existing packaging materials mainly focus on anti-corrosion issues . However, there are no practical and effective packaging products for anti-scratch and anti-collision, especially for the protection of precision metal parts with high-gloss surfaces. Traditional antirust packaging materials include vapor phase antirust paper, and in recent years, vapor phase antirust plastic films. However, the above two anti-rust packaging materials still have some defects in the practical performance of packaging. For example, the vapor phase anti-rust...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J5/18C08J9/00C08L23/06
Inventor 白芳刘宏杨松林
Owner 全桂媛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products