Aqueous silylated urethane composition, aqueous adhesives for wrapping, and aqueous contact adhesives

A water-based composition, polyurethane-based technology, applied in the direction of adhesives, etc., can solve the problems of not being able to say enough, and the scope of use is limited.

Inactive Publication Date: 2007-08-08
KONISHI CO
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this silylated polyurethane-based water-based composition, since an alkoxysilyl-terminated polymer containing anionic groups is used, the time to achieve adhesion and the adhesive force are better than conventional water-based adhesives. Although it has been improved, it cannot be said to be sufficient when compared with solvent-based adhesives, so it can be said that the range of use is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous silylated urethane composition, aqueous adhesives for wrapping, and aqueous contact adhesives
  • Aqueous silylated urethane composition, aqueous adhesives for wrapping, and aqueous contact adhesives
  • Aqueous silylated urethane composition, aqueous adhesives for wrapping, and aqueous contact adhesives

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0212] Mix polyol (A1-a): 150 parts, polyol (A2-b): 20 parts, polyol (A3-a) in a 4-neck flask equipped with a nitrogen inlet tube, thermometer, condenser, and stirring device : 8 parts, polyisocyanate (A4-a): 75.2 parts and methyl ethyl ketone (MEK): 100 parts, carried out the reaction for 6 hours at a temperature of 80 to 85° C. under a nitrogen stream to obtain a carboxyl group-containing and Reaction mixture of isocyanate-terminated polyurethane prepolymers with tertiary amino groups.

[0213] Next, in the total amount of the reaction mixture of the isocyanate group-terminated polyurethane prepolymer containing carboxyl groups and tertiary amino groups, 6.5 parts of alkoxysilanes (A5-a) containing amino groups: The reaction was carried out under temperature and nitrogen flow for 1 hour to obtain a reaction mixture containing isocyanate groups containing carboxyl groups and tertiary amino groups and alkoxysilyl-terminated polyurethane prepolymers.

[0214] Furthermore, afte...

Embodiment 2～13

[0216] Except having made the composition shown in Table 1 or 2, it carried out similarly to Example 1, and obtained the silylated polyurethane type aqueous composition which concerns on Examples 2-13, respectively.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

An aqueous silylated urethane composition useful as an aqueous adhesive which is highly safe, develops excellent tack in a short time, and is excellent in initial bond strength. The aqueous silylated urethane composition is characterized by comprising (A) an alkoxysilyl-terminated urethane prepolymer having an anionic group and a tertiary amino group which prepolymer is produced by reacting a polyol compound (A1) free from anionic groups, a polyol compound (A2) having an anionic group, a compound (A3) having a tertiary amino group and an isocyanate-reactive group, a polyisocyanate compound (A4), an alkoxysilane compound (A5) having an isocyanate-reactive group, and an amine chain extender (A6), (B) a basic compound, and (C) water.

Description

technical field [0001] The present invention relates to a silylated polyurethane water-based composition, a water-based encapsulating adhesive, and a water-based contact adhesive. More specifically, it relates to high safety and a short time required to express excellent adhesion , a silylated polyurethane-based aqueous composition, an aqueous encapsulating adhesive, and an aqueous contact adhesive that exhibit excellent initial adhesiveness and productivity equivalent to that of solvent-based adhesives. Background technique [0002] Conventionally, solvent-type polyurethane resin-based adhesives excellent in initial adhesiveness and cohesive force have been mainly used as adhesives for encapsulation. However, in recent years, there has been a demand for highly safe adhesives from the viewpoint of environmental issues, disease-causing housing issues, and the like. Therefore, although various water-based adhesives have been proposed so far as adhesives for encapsulation, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/38C08L75/04C08K5/17C09J175/04C09J201/10
Inventor 原田邦治森茂树福本好央
Owner KONISHI CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com