Collagen-DNA-Ag composition with bacteriostatic function and preparation thereof
A compound, collagen technology, applied in botanical equipment and methods, medical preparations containing active ingredients, drug combinations, etc., can solve problems such as inactivation and denaturation of heavy metal ions, achieve inhibition of bacterial infection, good flexibility, enhanced The effect of mechanical strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0040] Dissolve 1 g of DNA in 1000 ml of deionized water precooled to 4°C under stirring. Add 1% AgNO 3 2g. Stir for 10 minutes. The solution was placed in a dialysis bag and dialyzed for 24-96h.
[0041] Take 300ml of 0.7% collagen solution, and dialyze at 4°C for 24-96h. Degas at 13.3KPa for 10 minutes. Then use a diameter of 1cm, a hole diameter of 0.4mm, and the number of holes is 50 / cm 2 Spray it into the DNA solution above under a pressure of 0.15MPa. Put the obtained gel on a 100-mesh sieve to drain the water, wash it three times with 200ml deionized water pre-cooled to 4°C, put it into a 10×10×0.5cm model, freeze at -20°C, and use P 2 o 5 , KOH as a desiccant, and vacuum-dried to obtain 10 collagen sponge films with a total weight of 3.1 g and an Ag content of 0.21% (W / W). Packaging, Co. 60 irradiated.
Embodiment 2
[0043] Dissolve 5g of DNA in 100ml of deionized water pre-cooled to 4°C under stirring, adjust the pH of the solution to 8-10, add saturated AgNO 3 0.5g, stirred for 20min, dialyzed for 24-96h.
[0044] Take 2000ml of 0.5% collagen solution, dialyze at 4°C for 24-96h, and degas at 13.3KPa for 10min. Then use a diameter of 1cm, a hole diameter of 0.5mm, and a number of holes of 50 / cm 2 Spray it into the DNA solution above under a pressure of 0.1MPa. The obtained gel was placed on a 100-mesh sieve to drain off the water, washed three times with 2000ml of deionized water pre-cooled to 4°C, and packed into a 10×10×0.5cm model, and the freezing temperature was -20°C. with P 2 o 5 , KOH as a desiccant, dry to get 55 collagen sponge films, weighing 16.2g, Ag content 0.25% (W / W), packaging, Co 60 irradiated.
Embodiment 3
[0046] Dissolve 1 g of DNA in 100 ml of deionized water pre-cooled to 4 °C under stirring, add 2% AgNO 3 Solution 1g, stirred for 10min, dialyzed for 24-96h.
[0047] Take 400ml of 0.5% collagen solution, dialyze at 4°C for 24-96h, degas at 13.3KPa for 10min, and then use 1cm diameter, 0.5mm pore size, 50 holes / cm 2 Spray it into the above DNA solution under the pressure of 0.1MPa, stir, and spray the obtained colorless transparent latex with air with a pressure of 0.5MPa and a temperature of 120°C to obtain a collagen-DNA-Ag complex Powder 1.8g, Ag content 0.20% (W / W), package, Co 60 irradiated.
[0048] Antibacterial test
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap