Al-Ca-Fe alloy for final deoxidisation of molten steel and its preparation
A technology of ferroalloy and final deoxidation, which is applied in the field of ferroalloy, which can solve the problems of unfavorable continuous casting, easy pulverization of aluminum-iron alloy, blockage of nozzle, etc., and achieve the effect of avoiding nozzle nodule blockage, improving comprehensive mechanical properties and improving alloy hardness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment
[0010] Prepare wood-invented aluminum-calcium-iron alloy according to the following steps:
[0011] (1) According to the batching ratio of 40Kg of silica, 135Kg of lime, 35Kg of coke, and 60Kg of iron filings, it is smelted into low-silicon calcium with a chemical composition (weight ratio) of Si 16%, Ca 33%, and a balance of Fe with a 2500KVA submerged arc furnace. iron;
[0012] (2) Low-silicon-calcium-iron 50Kg obtained by the above-mentioned steps, metal aluminum 200Kg, iron 150Kg batching ratio batching, melting with industrial frequency furnace, the obtained weight ratio is Al 50%, Ca 4%, Si 2%, surplus Aluminum-calcium-iron alloy of Fe.
[0013] The Al-Ca-Fe alloy is used for the final deoxidation of 0 8 Al steel. After deoxidation, the oxygen content in the steel can reach below 30ppm, and the total amount of inclusions in the steel is below 60ppm. Dosage was significantly improved. The nozzle does not form nodules during continuous casting.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com