Water-proof liquid rubber

A liquid rubber, styrene-butadiene rubber technology, applied in other chemical processes, chemical instruments and methods, etc., can solve the problems of not being environmentally friendly, troublesome to use, expensive, etc., to achieve simple use, wide application range, low cost. Effect

Inactive Publication Date: 2005-03-02
BEIJING JIANGUO WEIYE WATERPROOF MATERIAL
View PDF1 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the existing waterproof materials are not environmentally friendly, and emit various toxic and harmful gases to the human bo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] [Example 1] Used in building surface waterproofing engineering

[0026] The weight formula is: EPDM rubber 15, styrene-butadiene rubber 5, activator 0.1-0.5, softener 5-10, ZNO 0.1, softener 5, px 0.2, vulcanizing agent 0.2, anti-aging agent 0.1, talcum powder 20 .

[0027] The preparation method is as follows:

[0028] (1) Forcibly dissolve EPDM rubber and styrene-butadiene rubber with 80-160 parts of No. 100 gasoline solvent oil;

[0029] (2) Add various activators, softeners, accelerators, vulcanizing agents, anti-aging agents, fillers and other auxiliary components;

[0030] (3) This product is a white odorless liquid, which can be made into various colors by adding various coloring agents according to the needs of users during actual production;

[0031] (4) Stir evenly at room temperature and pack.

[0032] Usage method: pour the product of the present invention on the building surface that needs to be waterproofed, and use the existing smear tool to make it c...

Embodiment 2

[0033] [Example 2] Used in building surface waterproofing engineering

[0034] The weight formula is: EPDM rubber 20, styrene-butadiene rubber 10, chlorinated polyethylene 5, neoprene 5, M 0.5, softener 10, cz 0.5, vulcanizing agent 0.4, anti-aging agent 0.2, calcium carbonate 30.

Embodiment 3

[0035] [Example 3] Used in the waterproofing project of the building surface

[0036] The weight formula is: EPDM rubber 18, styrene-butadiene rubber 8, chlorinated polyethylene 0.5, neoprene rubber 0.5, activator 0.35, softener 8, accelerator 0.35, vulcanizing agent 0.3, anti-aging agent 0.15, filler 25 .

[0037] The product that makes is through testing, and result is as follows:

[0038] Tensile strength >1.65MPI

[0039] Low temperature flexibility (-40°C) Passed

[0040] Elongation 500%

[0041] Acid resistance 10% nitric acid, sulfuric acid immersion for 7 days without change

[0042] Alkali resistance 10% calcium hydroxide soaked for 7 days without change

[0043] Heat aging (168 hours) Tensile strength retention rate ≥ 80%

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses one kind of waterproof paint prepared with ethylene propylene terpolymer, styrene butadiene rubber, curing agent, softening agent, promoter, sulfurizing agent, anti-ageing agent and stuffing. The present invention is environment friendly, may be produced into various products with different colors, and has simple preparation process, low cost, wide application range and wide application.

Description

technical field [0001] The invention relates to a building material, in particular to a waterproof liquid rubber. Background technique [0002] Most of the existing waterproof materials are not environmentally friendly, and emit various gases that are poisonous and harmful to the human body. And those environmentally friendly waterproof materials have unsatisfactory places in performance and use, such as expensive, troublesome use and so on. Contents of the invention [0003] The purpose of the present invention is to overcome the defects of the prior art and provide an environment-friendly and easy-to-use waterproof liquid rubber. [0004] The present invention is realized through the following technical solutions. [0005] The weight formula of the waterproof liquid rubber of the present invention is different according to the different parts of use. details as follows: [0006] 1. When used in building surface waterproofing projects: EPDM rubber 15-20, styrene-butad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C09K3/18
Inventor 杨太龙
Owner BEIJING JIANGUO WEIYE WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap