High strength abrasion resistant steel and method for producing the same

A technology of high-strength wear-resistant steel and its manufacturing method, which is applied in the field of alloy steel, can solve the problems of increased production cost of wear-resistant steel, hydrogen accumulation of parts, and hazards of railway transportation, etc., and achieves low production cost, stable internal quality, and extended The effect of dwell time

Active Publication Date: 2005-11-23
ZHEJIANG DESHENG RAILWAY EQUIP
View PDF1 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, experiments have proved that the addition of the main alloying element Ni has no obvious effect on improving the performance of wear-resistant steel, and because Ni alloy materials are expensive, it will also lead to an increase in the production cost of wear-resistant steel
In addition, due to the lack of refining process in the manufacturing process of wear-resistant steel, especially the lack of measures to remove harmful gas hydrogen, there is a possibility of hydrogen accumulation inside the product, so that the product has delayed cracking that poses a great hazard to railway transportation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Chemical composition and content are proportioned according to the following ratio (weight %):

[0045] C 0.27, Si 0.8, Mn 1.0, Cr 1.1, Mo 0.35, V 0.17, Ti 0.09, P≤0.03, S≤0.025.

[0046] After deformation oil quenching, temper at 480 to obtain tempered sorbite structure.

[0047] The mechanical properties are as follows:

[0048] Intensity σ b =1410Mpa, hardness HRC=43, impact toughness α ku =51J / cm 2 , elongation δ 5 = 10%.

Embodiment 2

[0050] Chemical composition and content are proportioned according to the following ratio (weight %):

[0051] C 0.36, Si 1.1, Mn 1.2, Cr 1.2, Mo 0.4, V 0.18, Ti 0.08, P≤0.03, S≤0.025.

[0052] After deformation normalizing, temper at 380°C to obtain bainite + retained austenite structure.

[0053] The mechanical properties are as follows:

[0054] Intensity σ b =1420Mpa, hardness HRC=42, impact toughness α ku =65J / cm 2 , elongation δ 5 = 9.5%.

Embodiment 3

[0056] Chemical composition and content are proportioned according to the following ratio (weight %):

[0057] C 0.45, Si 0.7, Mn 0.8, Cr 1.15, Mo 0.36, V 0.19, Ti 0.10, P≤0.03, S≤0.025.

[0058] After deformation oil quenching, temper at 520°C to obtain tempered sorbite structure.

[0059] The mechanical properties are as follows:

[0060] Intensity σ b =1620Mpa, hardness HRC=48, impact toughness α ku =50J / cm 2 , elongation δ 5 = 9%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
strengthaaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a high strength and wear resistant steel and its production process, which is particularly suitable for application in railway intersections. The compositions (wt%) are : C 0.25-0.55, Si 0.6-1.5,Mn 0.8-1.5,Cr 1-1.5,Mo 0.3-0.5, V 0.15-0.25, Ti 0.05-0.15, P<=0.03, S<=0.025. The production flow sheet is as follows: refining by arc furnace - refining by vacuum furnace - ladle refining outside of furnace - casting ingot - primary rolling in billet - forging in form - deforming heat treatment. As compared with the existing technologies, the present steel has the advantages of excellent wear resistance, high strength, high toughness, stable quality and low production cost.

Description

technical field [0001] The invention relates to alloy steel, in particular to a high-strength wear-resistant steel that can be used for railway turnouts and a manufacturing method thereof. Background technique [0002] With the development of railway transportation towards heavy load and high speed, higher requirements are put forward for the materials and inherent quality of railways. The high-manganese steel turnouts in active service have become more and more difficult to meet the needs of high-speed development of heavy-duty railway transportation, especially for turnout core rails with harsh service conditions, which must not only have sufficient wear resistance, but also require sufficient strength and toughness. Should have a stable inner quality. For this reason, both at home and abroad are trying to develop high-performance wear-resistant steel that can meet the requirements of heavy-duty and high-speed railway transportation. For example, the application number is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/18
Inventor 关铁
Owner ZHEJIANG DESHENG RAILWAY EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap