High strength anti-weather burial arc welding wire
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A submerged arc welding wire and weather-resistant technology, applied in arc welding equipment, welding medium, welding equipment, etc., can solve the problems of complex composition design, increased smelting difficulty, high cost, good atmospheric corrosion resistance, simple design, low temperature impact Good toughness
Active Publication Date: 2006-01-04
BAOSHAN IRON & STEEL CO LTD
View PDF1 Cites 21 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The composition design is relatively complicated and messy, which increases the difficulty of smelting; the cost is also high, and it is mainly suitable for pipeline manufacturing
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0025] Examples are shown in Table 1.
[0026] Numbering
C
Si
mn
Cu
Cr
Ni
Ti
1
0.04
0.15
1.80
0.30
0.40
0.50
0.100
2
0.07
0.20
1.50
0.20
0.60
0.35
0.080
3
0.15
0.33
1.45
0.10
0.85
0.26
0.035
4
0.11
0.08
1.35
0.15
0.95
0.68
0.060
5
0.08
0.05
1.23
0.16
1.13
0.80
0.050
[0027]
Numbering
σ 0.2
(MPa)
σ b
(MPa)
δ 5
(%)
A kv * (J)
room temperature
-40℃
1
475
560
24
146
102
2
475
565
30
126
96
3
525
620
25
138
118
4
480
570
26
150
106
5
530...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
yield strength
aaaaa
aaaaa
yield strength
aaaaa
aaaaa
tensile strength
aaaaa
aaaaa
Login to view more
Abstract
The high strength weather resisting submerged arc welding wire consists of: C 0.04-0.15 wt%, Mn 1.2-2.0 wt%, S not more than 0.030 wt%, P not more than 0.030 wt%, Cu 0.10-0.30 wt%, Cr 0.40-1.2 wt%, Ni 0.20-0.80 wt%, and Ti 0.03-0.10 wt%. The welding wire forms fused-on metal and welded joint with excellent atmospheric corrosion resistance and excellent comprehensive performance, including yield strength not lower than 450 MPa, tensile strength not lower than 550 MPa, elongation greater than 22 %, and especially low temperature impact toughness of Akv not lower than 60 J at the temperature of -40 deg c.
Description
technical field [0001] The invention belongs to the field of welding materials. Background technique [0002] Existing submerged arc welding wires such as the patent "High Toughness Welding Wire Suitable for Low Carbon Microalloyed Steel" proposed by Yanshan University disclosed in Chinese Patent Application No. 02119591.9. The chemical composition formula of welding wire is as follows: C: 0.01~0.12%, Si: 0.10~0.40%, Mn: 0.6~2.3%, Cr: 0.01~0.22%, Mo: 0.08~0.60%, V: 0.004~0.06%, Cu : 0.01-0.50%, Ni: 0.01-0.60%, Al: 0.01-0.06%, Nb: 0.02-0.08%, Ti: 0.01-0.20%, B: 0.0001-0.01%, Re: 0.001-0.5%. [0003] This welding wire has certain weather resistance characteristics and contains Cu, Cr, Ni alloy elements. At the same time, it uses a variety of alloying elements, such as Mo, Nb, V, Ti, B, Re elements. The composition design is relatively complicated and messy, which increases the difficulty of smelting; the cost is also high, and it is mainly suitable for pipeline manufacturin...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.